Lithium-ion rechargeable battery negative electrode active material and preparation method thereof, lithium-ion rechargeable battery negative electrode plate, and lithium-ion rechargeable battery

Patent metadata

Field	Value
Publication number	US-12170365-B2
Application number	US-202218147618-A
Country	US
Kind code	B2
Filing date	Dec 28, 2022
Priority date	Dec 18, 2015
Publication date	Dec 17, 2024
Grant date	Dec 17, 2024

Abstract

A lithium-ion rechargeable battery negative electrode active material and a preparation method thereof, a lithium-ion rechargeable battery negative electrode plate, and a lithium-ion rechargeable battery are disclosed. The negative electrode active material includes a carbon core and a coating layer formed on a surface of the carbon core, a material of the coating layer includes amorphous carbon and a doping element, and the doping element includes element nitrogen. The lithium-ion rechargeable battery negative electrode active material has the carbon core, and the coating layer that includes the doping element and the amorphous carbon is provided on the surface of the carbon core.

First claim

What is claimed is:

1. A preparation method of a lithium-ion rechargeable battery negative electrode active material, the method comprising the following:
mixing a carbon material and an amorphous carbon material with an ionic liquid to obtain a mixture;
putting the mixture into a reaction kettle;
introducing a mixed gas of an inert carrier gas and a small organic molecule containing a doping element; and
keeping the mixture at 500° C. to 1200° C. for 1 hour to 12 hours to obtain a lithium-ion rechargeable battery negative electrode active material,
wherein the lithium-ion rechargeable battery negative electrode active material comprises a carbon core and a coating layer formed on a surface of the carbon core,
wherein a material of the coating layer comprises amorphous carbon and a doping element,
wherein the doping element comprises element nitrogen,
wherein the coating layer is of a single-layer structure,
wherein the doping element is dispersed in the amorphous carbon, and
wherein the doping element has a mass content in the coating layer of 0.1% to 20%.

2. A preparation method of a lithium-ion rechargeable battery negative electrode active material, the method comprising the following:
(1) mixing a carbon material with an amorphous carbon material, and performing coating and charring processing at 400° C. to 1200° C. to obtain a carbon negative electrode material coated by amorphous carbon;
(2) putting the obtained carbon negative electrode material into a reaction kettle ultrasonically dispersing the carbon negative electrode material in a first mixed solution, and adding an oxidant to the first mixed solution to obtain a suspension; adding a pyrrole monomer to the suspension to obtain a second mixed solution; keeping the second mixed solution at 0° C. to 5° C. for 1 hour to 24 hours to obtain a black precipitate; and washing the black precipitate to neutral and drying the black precipitate, wherein the first mixed solution is obtained by dissolving a surfactant in an acid solution; and
(3) putting the dried black precipitate into a reaction kettle, introducing a mixed gas of an inert carrier gas and a hydride containing a doping element, and keeping the black precipitate at 500° C. to 1200° C. for 1 hour to 12 hours to obtain a lithium-ion rechargeable battery negative electrode active material,
wherein the lithium-ion rechargeable battery negative electrode active material comprises a carbon core and a coating layer formed on a surface of the carbon core,
wherein a material of the coating layer comprises amorphous carbon and a doping element,
wherein the doping element comprises element nitrogen,
wherein the coating layer is of a double-layer structure,
wherein the coating layer comprises an amorphous carbon layer and a doped layer sequentially formed on the surface of the carbon core, and
wherein the doped layer comprises element carbon and the doping element.

3. A preparation method of a lithium-ion rechargeable battery negative electrode active material, the method comprising the following:
(1) putting a carbon material into a reaction kettle ultrasonically dispersing the carbon material in a first mixed solution, and adding an oxidant to the first mixed solution to obtain a suspension; adding a pyrrole monomer to the suspension to obtain a second mixed solution; keeping the second mixed solution at 0° C. to 5° C. for 1 hour to 24 hours to obtain a black precipitate; and washing the black precipitate to neutral and drying the black precipitate, wherein the first mixed solution is obtained by dissolving a surfactant in an acid solution, wherein a molar ratio of the surfactant to the acid solution is 1:2 to 1:10, and wherein a molar ratio of the added oxidant to the pyrrole monomer is 1:0.5 to 1:5;
(2) putting the dried black precipitate into a reaction kettle, introducing a mixed gas of an inert carrier gas and a hydride containing a doping element, and keeping the black precipitate at 500° C. to 1200° C. for 1 hour to 12 hours to obtain a negative electrode material coated by a doped layer; and
(3) mixing an amorphous carbon material with the obtained negative electrode material that is coated by the doped layer, and performing coating and charring processing at 400° C. to 1200° C., to obtain a lithium-ion rechargeable battery negative electrode active material,
wherein the lithium-ion rechargeable battery negative electrode active material comprises a carbon core and a coating layer formed on a surface of the carbon core,
wherein a material of the coating layer comprises amorphous carbon and a doping element,
wherein the doping element comprises element nitrogen,
wherein the coating layer is of a double-layer structure,
wherein the coating layer comprises a doped layer and an amorphous carbon layer sequentially formed on the surface of the carbon core, and
wherein the doped layer comprises element carbon and the doping element.

4. The preparation method of claim 1 , wherein the mass content of the doping element in the coating layer is 0.1% to 10%.

5. The preparation method of claim 1 , wherein the thickness of the coating layer is 0.1 μm to 10 μm.

6. The preparation method of claim 1 , wherein the coating layer has a mass content of 0.1% to 30%.

7. The preparation method of claim 1 , wherein the coating layer has a mass content of 0.5% to 15%.

8. The preparation method of claim 4 , wherein the thickness of the coating layer is 0.1 μm to 10 μm.

9. The preparation method of claim 6 , wherein the thickness of the coating layer is 0.1 μm to 10 μm.

10. The preparation method of claim 4 , wherein the coating layer has a mass content of 0.1% to 30%.

11. The preparation method of claim 4 , wherein the coating layer has a mass content of 0.5% to 15%.

12. The preparation method of claim 5 , wherein the coating layer has a mass content of 0.5% to 15%.

13. The preparation method of claim 8 , wherein the coating layer has a mass content of 0.1% to 30%.

14. The preparation method of claim 8 , wherein the coating layer has a mass content of 0.5% to 15%.

Assignees

• Huawei Tech Co Ltd

Inventors

• Liang Jiahua
• Xia Shengan
• Xie Fengchao

Classifications

• H01M2004/027

  Negative electrodes · CPC title

• C01P2006/40

  Electric properties · CPC title

• C01P2004/84

  one phase coated with the other · CPC title

• C01P2002/54

  one element only · CPC title

• C01P2002/02

  Amorphous compounds · CPC title