Flexible wood structures and devices, and methods for fabricating and use thereof

Patent metadata

Field	Value
Publication number	US-12157249-B2
Application number	US-202217866767-A
Country	US
Kind code	B2
Filing date	Jul 18, 2022
Priority date	Apr 3, 2017
Publication date	Dec 3, 2024
Grant date	Dec 3, 2024

Abstract

A flexible structure is formed by subjecting cellulose-based natural wood material to a chemical treatment that partially removes hemicellulose and lignin therefrom. The treated wood has a unique 3-D porous structure with numerous channels, excellent biodegradability and biocompatibility, and improved flexibility as compared to the natural wood. By further modifying the treated wood, the structure can be adapted to particular applications. For example, nanoparticles, nanowires, carbon nanotubes, or any other coating or material can be added to the treated wood to form a hybrid structure. In some embodiments, open lumina within the structure can be at least partially filled with a non-wood substance, such as a flexible polymer, or with entangled cellulose nanofibers. The unique architecture and superior properties of the flexible wood allow for its use in various applications, such as, but not limited to, structural materials, solar thermal devices, flexible electronics, tissue engineering, thermal management, and energy storage.

First claim

The invention claimed is:

1. A method comprising:
treating a piece of natural wood with a chemical solution so as to partially remove hemicellulose and lignin therein, wherein after the treating, the piece of chemically-treated natural wood retains at least some lignin and cellulose-based lumina defined by wood cells formed of cellulose nanofibers;
after the treating, drying the piece of chemically-treated natural wood; and
using the dried piece of chemically-treated natural wood as a flexible structure that bends without fracturing,
wherein a flexibility of the piece of chemically-treated natural wood after the treating and the drying is greater than a flexibility of the piece of natural wood before the treating and drying, and
during the using, inner volumes of at least some of the retained cellulose-based lumina remain open or unobstructed.

2. The method of claim 1 , wherein the drying is performed in air, such that the cellulose-based lumina crumple in a cross-sectional view.

3. The method of claim 1 , wherein the drying comprises freeze drying or critical point drying, such that the cellulose-based lumina remain open in a cross-sectional view.

4. The method of claim 1 , wherein the chemical solution comprises at least one of NaOH, Na 2 SO 3 , (NH 4 ) 2 SO 3 , p-TsOH, NH 3 ·H 2 O, NaOH+Na 2 S, Na 2 CO 3 , NaOH+Na 2 SO 3 , NaOH+(NH 4 ) 2 SO 3 , NH 4 OH+(NH 4 ) 2 SO 3 , NH 4 OH+Na 2 SO 3 , NaOH+Na 2 CO 3 , NaOH+AQ, NaOH/Na 2 S+AQ, NaOH+Na 2 SO 3 +AQ, Na 2 SO 3 +AQ, NaOH+Na 2 S+Na 2 S n , Na 2 SO 3 +NaOH+CH 3 OH+AQ, C 2 H 5 OH+NaOH, C 2 H 8 N 2 , C 2 H 7 NO+NH 3 −H 2 O, N 2 H 4 −H 2 O, and NaHCO 3 , where n in an integer and AQ is Anthraquinone.

5. The method of claim 1 , wherein between 5% and 95% of the lignin has been removed from said piece of natural wood by the treating.

6. The method of claim 1 , wherein the using as a flexible structure comprises:
(a) at least one of:
bending or folding the piece of chemically-treated natural wood onto itself;
twisting the piece of chemically-treated natural wood more than 45°; and
wrapping the piece of chemically-treated natural wood around an appendage of a user; and

(b) after (a), releasing the piece of chemically-treated natural wood such that it returns to its original shape.

7. The method of claim 1 , further comprising, after the drying, forming a coating on the piece of chemically-treated natural wood.

8. The method of claim 7 , wherein the coating comprises at least one of nanoparticles, nanowires, graphene, graphite, single-walled carbon nanotubes, double-walled carbon nanotubes, multi-walled carbon nanotubes, carbon black, graphite, hard carbon, reduced graphene oxide, graphene, plasmonic metallic nanoparticles, and semiconductor nanoparticles.

9. The method of claim 7 , wherein the coating is comprised of carbon nanotubes (CNT) and the forming comprises:
(a) immersing the piece of chemically-treated natural wood in a CNT solution; and
(b) after (a), drying the piece of chemically-treated natural wood.

10. The method of claim 9 , further comprising:
prior to the forming a coating, forming at a first surface of said piece a plurality of micro-sheet protrusions extending therefrom,
wherein the forming a coating is such that the coating is formed on the micro-sheet protrusions.

11. The method of claim 10 , further comprising, after the forming a coating:
placing a second surface of the piece of chemically-treated natural wood, opposite to the first surface, in contact with a fluid source; and
exposing the coated first surface to a source of light, such that fluid pumped to the first surface from the second surface via capillary action and/or nano-cavitation effects is heated to generate steam or vapor.

12. The method of claim 9 , wherein:
the piece of chemically-treated natural wood has a first surface;
the forming is such that the coating is formed on at least the first surface and inner surfaces of the lumina; and
the method further comprises:
after the forming the coating, depositing a plurality of catalytic nanoparticles and/or electroactive particles on a surface of the coating;
after the depositing, disposing a separator membrane between an anode and a second surface of the piece of chemically-treated natural wood, the second surface being opposite to the first surface; and
filling at least the piece of chemically-treated natural wood with an electrolyte solution.

13. The method of claim 12 , further comprising:
applying a voltage between the piece of chemically-treated natural wood and the anode so as to store charge therein.

14. The method of claim 1 , further comprising:
coupling non-wood particles to one or more surfaces of said piece of chemically-treated natural wood,
wherein the particles comprise metallic nanoparticles, metal alloy nanoparticles, sulfides, phosphides, borides, or oxides.

15. A method comprising:
treating a piece of natural wood with a chemical solution so as to partially remove hemicellulose and lignin therein, wherein after the treating, the piece of chemically-treated natural wood retains at least some lignin and cellulose-based lumina defined by wood cells formed of cellulose nanofibers; and
freeze-drying the piece of chemically-treated natural wood such that the retained cellulose-based lumina remain open in a cross-sectional view,
wherein a flexibility of the piece of chemically-treated natural wood after the treating and the freeze-drying is greater than a flexibility of the piece of natural wood before the treating and the freeze-drying, and
the freeze-drying is performed after the treating and without any rinsing in between, such that cellulose nanofibers, which were released from the wood cells during the treating and disposed within inner volumes of the cellulose-based lumina, are entangled with each other to form entangled fiber networks within the inner volumes of the cellulose-based lumina.

16. A method comprising:
treating a piece of natural wood with a chemical solution so as to partially remove hemicellulose and lignin therein, wherein after the treating, the piece of chemically-treated natural wood retains at least some lignin and cellulose-based lumina defined by wood cells formed of cellulose nanofibers;
after the treating, drying the piece of chemically-treated natural wood; and
after the drying, filling the lumina of the chemically-treated natural wood with a flexible polymer comprising hydrogel or a silicone polymer,
wherein a flexibility of the piece of chemically-treated natural wood after the filling with the flexible polymer is greater than a flexibility of the piece of natural wood before the treating.

17. The method of claim 16 , further comprising:
prior to the filling with a flexible polymer, forming a coating on the piece of chemically-treated natural wood.

Assignees

• Univ Maryland

Inventors

• Hu Liangbing
• Song Jianwei
• Chen Chaoji
• Gong Amy

Classifications

• H01M50/4295

  Natural cotton, cellulose or wood · CPC title

• H01M50/44

  Fibrous material · CPC title

• H01M10/052

  Li-accumulators · CPC title

• B82Y30/00

  Nanotechnology for materials or surface science, e.g. nanocomposites · CPC title

• B27M1/003

  Mechanical surface treatment · CPC title