Non-oriented electrical steel sheet and method for manufacturing slab used as material for the same

Patent metadata

Field	Value
Publication number	US-12146209-B2
Application number	US-201917281075-A
Country	US
Kind code	B2
Filing date	Sep 5, 2019
Priority date	Oct 2, 2018
Publication date	Nov 19, 2024
Grant date	Nov 19, 2024

Abstract

Provided is a non-oriented electrical steel sheet having such a low Al concentration so that it is excellent in terms of the recycling efficiency of scrap iron and having a high magnetic flux density and low iron loss.
The non-oriented electrical steel sheet according to the present invention has a chemical composition containing C; 0.0050 mass % or less, Si; 1.5 mass % to 5.0 mass %, Mn; 0.2 mass % to 3.0 mass %, sol.Al; 0.0030 mass % or less, P; 0.2 mass % or less, S; 0.0050 mass % or less, N; 0.0040 mass % or less, T.Ca; 0.0010 mass % to 0.0080 mass %, T.O; 0.0100 mass % or less, REM; 0.0001 mass % to 0.0050 mass %, and a balance of Fe and inevitable impurities, in which a value of a mass-related fractional expression ((T.Ca+REM)/(T.O+S)), which is a relational expression for the masses of the four constituents described above, that is, T.Ca, REM, T.O, and S, is 0.4 or more.

First claim

The invention claimed is:

1. A non-oriented electrical steel sheet having
a chemical composition containing C; 0.0050 mass % or less, Si; 1.5 mass % to 5.0 mass %, Mn; 0.2 mass % to 3.0 mass %, sol.Al; 0.0030 mass % or less, P; 0.2 mass % or less, S; 0.0050 mass % or less, N; 0.0040 mass % or less, T.Ca; 0.0010 mass % to 0.0080 mass %, T.O; 0.0100 mass % or less, REM; 0.0001 mass % to 0.0050 mass %, and a balance of Fe and inevitable impurities,
wherein a value of a mass-related fractional expression ((T.Ca+REM)/(T.O+S)), which is a relational expression for masses of four constituents including T.Ca, REM, T.O, and S, is 0.4 or more.

2. The non-oriented electrical steel sheet according to claim 1 , wherein a value of a mass-related fractional expression (T.Ca/REM), which is a relational expression for masses of two constituents including T.Ca and REM, is 1.0 or more.

3. The non-oriented electrical steel sheet according to claim 1 , wherein an average crystal grain diameter of a metallographic structure is 40 μm or more.

4. The non-oriented electrical steel sheet according to claim 2 , wherein an average crystal grain diameter of a metallographic structure is 40 μm or more.

5. A non-oriented electrical steel sheet having
a chemical composition containing C; 0.0050 mass % or less, Si; 1.5 mass % to 5.0 mass %, Mn; 0.2 mass % to 3.0 mass %, sol.Al; 0.0030 mass % or less, P; 0.2 mass % or less, S; 0.0050 mass % or less, N; 0.0040 mass % or less, T.Ca; 0.0010 mass % to 0.0080 mass %, T.O; 0.0100 mass % or less, REM; 0.0001 mass % to 0.0050 mass %, at least one of element group A through element group C below, and a balance of Fe and inevitable impurities,
wherein a value of a mass-related fractional expression ((T.Ca+REM)/(T.O+S)), which is a relational expression for masses of four constituents including T.Ca, REM, T.O, and S, is 0.4 or more, where
group A consists of one or both selected from Sn and Sb each in an amount of 0.01 mass % to 0.1 mass %,
group B consists of Mg in an amount of 0.0001 mass % to 0.0050 mass %, and
group C consists of one, two, or all selected from Cu, Ni, and Cr each in an amount of 0.01 mass % to 0.5 mass %.

6. The non-oriented electrical steel sheet according to claim 5 , wherein a value of a mass-related fractional expression (T.Ca/REM), which is a relational expression for masses of two constituents including T.Ca and REM, is 1.0 or more.

7. The non-oriented electrical steel sheet according to claim 5 , wherein an average crystal grain diameter of a metallographic structure is 40 μm or more.

8. The non-oriented electrical steel sheet according to claim 6 , wherein an average crystal grain diameter of a metallographic structure is 40 μm or more.

Assignees

• Jfe Steel Corp

Inventors

• HARADA Akifumi
• Matsui Akitoshi
• Oda Yoshihiko
• Okubo Tomoyuki
• Uesaka Masanori

Classifications

• C22C38/04

  containing manganese · CPC title

• C22C38/02

  containing silicon · CPC title

• C22C38/005

  containing rare earths, i.e. Sc, Y, Lanthanides · CPC title

• C22C38/002 Primary

  containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60 · CPC title

• C22C38/001

  containing N · CPC title