Fluoroelastomers with perfluorinated thermoplastic fillers

Patent metadata

Field	Value
Publication number	US-12134669-B2
Application number	US-202218568981-A
Country	US
Kind code	B2
Filing date	Jun 30, 2022
Priority date	Jul 12, 2021
Publication date	Nov 5, 2024
Grant date	Nov 5, 2024

Abstract

Fluoroelastomers containing at least 25 weight percent perfluorinated thermoplastic fillers are described. The perfluorinated thermoplastic fillers comprise a first perfluorinated thermoplastic filler having a first d50 particle size of 10 to 250 nanometers, and a second perfluorinated thermoplastic filler having a second d50 particle size of 5 to 500 micrometers. The first thermoplastic filler may be obtained from a latex while the second thermoplastic filler may be obtained as a dry powder. Methods of making such materials and cured articles prepared from them are also described.

First claim

What is claimed is:

1. An elastomer composition comprising a curable fluoroelastomer and at least 25% by weight of perfluorinated thermoplastic fillers based on the total weight of the fluoroelastomer and the perfluorinated thermoplastic fillers; wherein the perfluorinated thermoplastic fillers comprise a first perfluorinated thermoplastic filler having a first d50 particle size of 10 to 250 nanometers as measured according to the Latex Size Procedure, and a second perfluorinated thermoplastic filler having a second d50 particle size of 5 to 500 micrometers as measured according to the Powder Size Procedure.

2. The composition of claim 1 wherein the perfluorinated thermoplastic fillers comprise 30 to 70% by weight of the first perfluorinated thermoplastic filler and 30 to 70% by weight of the second perfluorinated thermoplastic filler, based on the total weight of the perfluorinated thermoplastic fillers.

3. The composition of claim 2 , wherein the perfluorinated thermoplastic fillers comprise 40 to 60% by weight of the first perfluorinated thermoplastic filler and 40 to 60% by weight of the second perfluorinated thermoplastic filler, based on the total weight of the perfluorinated thermoplastic fillers.

4. The composition of claim 1 , comprising 30 to 60% by weight of the perfluorinated thermoplastic fillers.

5. The composition of claim 1 , wherein the first d50 particle size is no greater than 150 nanometers.

6. The composition of claim 5 , wherein the first d50 particle size is at least 30 nanometers.

7. The composition of claim 1 , wherein the second d50 particle size is at least 10 micrometers.

8. The composition of claim 7 , wherein the second d50 particle size is between 20 and 150 micrometers.

9. The composition of claim 1 , wherein the first perfluorinated thermoplastic comprises at least 99 mole % of tetrafluoroethylene and at least 0.5 mole % of at least one perfluorinated alkyl ether.

10. The composition of claim 9 , wherein the at least one perfluorinated alkyl ether of the first perfluorinated thermoplastic comprises at least one perfluorinated alkyl vinyl ether, optionally selected from the group consisting of PMVE, PEVE, PPVE, and combinations thereof.

11. The composition of claim 9 , wherein the at least one perfluorinated alkyl ether of the first perfluorinated thermoplastic comprises at least one perfluorinated alkyl allyl ether, optionally wherein the perfluorinated alkyl allyl ether is perfluoromethyl allyl ether.

12. The composition of claim 1 , wherein the second perfluorinated thermoplastic comprises at least 99 mole % of tetrafluoroethylene and at least 0.5 mole % of at least one perfluorinated alkyl ether.

13. The composition of claim 12 , the at least one perfluorinated alkyl ether of the second perfluorinated thermoplastic comprises at least one perfluorinated alkyl vinyl ether, optionally selected from the group consisting of PMVE, PEVE, PPVE, and combinations thereof.

14. The composition of claim 12 , wherein the at least one perfluorinated alkyl ether of the second perfluorinated thermoplastic comprises at least one perfluorinated alkyl allyl ether, optionally wherein the perfluorinated alkyl allyl ether is perfluoromethyl allyl ether.

15. The composition of claim 1 , wherein the curable fluoroelastomer is a perfluoroelastomer.

16. The composition of claim 15 , wherein the perfluoroelastomer is a copolymer comprising 60 to 70 mole % tetrafluoroethylene, 30 to 40 mole % of at least one of a perfluoroalkyl vinyl ether and a perfluoroalkyl allyl ether, and 0.5 to 3 mole % of a cure site monomer.

17. The composition of claim 1 , wherein the curable fluoroelastomer is a partially-fluorinated elastomer.

18. The composition of claim 17 , wherein the partially-fluorinated elastomer is copolymer of tetrafluoroethylene, hexafluoropropylene, vinylidene fluoride, and a cure site monomer.

19. The composition of claim 17 , wherein the partially-fluorinated elastomer is copolymer of tetrafluoroethylene, vinylidene fluoride, at least one of an alkyl vinyl ether and an alkoxy vinyl ether, and a cure site monomer.

20. A method of preparing a composition comprising a curable fluoroelastomer and at least 25% by weight of perfluorinated thermoplastic fillers based on the total weight of the fluoroelastomer and the perfluorinated thermoplastic fillers; wherein the perfluorinated thermoplastic fillers comprise a first perfluorinated thermoplastic filler having a first d50 particle size of 10 to 250 nanometers as measured according to the Latex Size Procedure, and a second perfluorinated thermoplastic filler having a second d50 particle size of 5 to 500 micrometers as measured according to the Powder Size Procedure, the method comprising blending a first latex comprising the curable fluoroelastomer and a second latex comprising the first perfluorinated thermoplastic filler to form a latex blend; coagulating and drying the latex blend to form a first portion of the composition; and milling the second perfluorinated thermoplastic filler into the first portion to form the composition.

Assignees

• 3M Innovative Properties Company

Inventors

• Fukushi Tatsuo
• Baker Julie A
• Suzuki Yuta
• Vowinkel Steffen
• Mcbride Justin P
• Mitchell Michael H

Classifications

• C08L2205/025

  containing two or more polymers of the same hierarchy C08L, and differing only in parameters such as density, comonomer content, molecular weight, structure · CPC title

• C08L27/18 Primary

  Homopolymers or copolymers or tetrafluoroethene · CPC title

• C08F214/262 Primary

  with fluorinated vinyl ethers · CPC title

• C08L2205/03

  containing three or more polymers in a blend · CPC title