Polyurethane composition having polymeric plasticizer and a low content of monomeric diisocyanates

Patent metadata

Field	Value
Publication number	US-12129377-B2
Application number	US-201917263323-A
Country	US
Kind code	B2
Filing date	Aug 5, 2019
Priority date	Aug 8, 2018
Publication date	Oct 29, 2024
Grant date	Oct 29, 2024

Abstract

A moisture-curing polyurethane composition having a content of monomeric diisocyanates of at most 0.1 wt %, containing: at least one isocyanate-group-containing polyurethane polymer having a content of monomeric diisocyanates of at most 0.5 wt %, obtained from reaction of at least one monomeric diisocyanate with at least one polyether polyol at a NCO/OH ratio of at least 3/1 and subsequent removal of a large part of monomeric diisocyanates by way of a suitable separating method; and at least one polyether having blocked hydroxyl groups and free of isocyanate groups, as a plasticizer. Moisture-curing polyurethane composition is highly storage-stable when moisture is excluded, can be safely handled without special safety precautions, can be sold without hazard label, can be well processed, has long open time and has fast curing to form elastic material of high strength and extensibility, high cold flexibility, good adhesion properties and high stability with respect to heat and moisture.

First claim

The invention claimed is:

1. A moisture-curing polyurethane composition having a monomeric diisocyanate content of not more than 0.1% by weight, the moisture-curing polyurethane composition comprising
20% to 60% of at least one polyetherurethane polymer containing isocyanate groups and having a monomeric diisocyanate content of not more than 0.5% by weight, the at least one polyetherurethane polymer having been obtained from the reaction of at least one monomeric diisocyanate with at least one polyether polyol in an NCO/OH ratio of at least 3/1, and subsequent removal of a majority of the monomeric diisocyanates by means of a suitable separation method,
5% to 35% of at least one polyether having blocked hydroxyl groups, which is free of isocyanate groups, as plasticizer, wherein the blocked hydroxyl groups are acetate groups,
20% to 60% by weight of fillers, and
optionally further constituents.

2. The polyurethane composition as claimed in claim 1 , wherein the polyetherurethane polymer has an NCO content in the range from 0.5% to 6.0% by weight.

3. The polyurethane composition as claimed in claim 1 , wherein the polyetherurethane polymer has 80% to 100% by weight of 1,2-propyleneoxy groups and 0% to 20% by weight of 1,2-ethyleneoxy groups in the polyether segment.

4. The polyurethane composition as claimed in claim 1 , wherein the monomeric diisocyanate used for the reaction is diphenylmethane 4,4′-diisocyanate, tolylene 2,4-diisocyanate or mixtures thereof with tolylene 2,6-diisocyanate, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane or hexane 1,6-diisocyanate.

5. The polyurethane composition as claimed in claim 1 , wherein the NCO content of the polyetherurethane polymer is at least 80% of the theoretical NCO content which is calculated from the addition of one mole of monomeric diisocyanate per mole of OH groups of the polyether polyol.

6. The polyurethane composition as claimed in claim 1 , wherein the polyether having blocked hydroxyl groups is derived from a hydroxy-functional polyether having an average OH functionality in the range from 1 to 3.

7. The polyurethane composition as claimed in claim 1 , wherein the polyether having blocked hydroxyl groups has an average molecular weight M n in the range from 600 to 15,000 g/mol, determined by means of gel permeation chromatography (GPC) versus polystyrene standard with tetrahydrofuran as mobile phase, refractive index detector and evaluation from 200 g/mol.

8. The polyurethane composition as claimed in claim 1 , further comprising at least one further constituent selected from oligomeric isocyanates and catalysts.

9. A method of bonding or sealing, comprising the steps of
(i) applying the polyurethane composition as claimed in claim 1
to a first substrate and contacting the composition with a second substrate within the open time of the composition, or
to a first and to a second substrate and joining the two substrates within the open time of the composition, or
between two substrates,

(ii) curing the composition by contact with moisture.

10. A method of coating or sealing, comprising the steps of
(i) applying the polyurethane composition as claimed in claim 1 to a substrate,
(ii) curing the composition by contact with moisture.

11. An article obtained from the method as claimed in claim 9 .

Assignees

• Sika Tech Ag

Inventors

• Kramer Andreas
• Schlumpf Michael
• Burckhardt Urs

Classifications

• C08K3/36

  Silica · CPC title

• C08K3/04

  Carbon · CPC title

• C08G2170/00

  Compositions for adhesives · CPC title

• C08G2150/00

  Compositions for coatings · CPC title

• C08G18/7657

  containing two or more aromatic rings · CPC title