Positive electrode material, electrochemical device containing same, electronic device, and method for preparing the positive electrode material

Patent metadata

Field	Value
Publication number	US-12126016-B2
Application number	US-202017281046-A
Country	US
Kind code	B2
Filing date	Mar 31, 2020
Priority date	Mar 31, 2020
Publication date	Oct 22, 2024
Grant date	Oct 22, 2024

Abstract

A positive electrode material includes a lithium composite oxide, and the positive electrode material comprises stress relief particles. There are cavities inside the stress relief particles, and the cavities are closed structures. The positive electrode material that includes the stress relief particles can be used to effectively tackle a stress and relieve the stress in advance, relieve a strain of the positive electrode material used at a high voltage, avoid ruptures of particles of the positive electrode material, and enhance structural stability of the positive electrode material. The positive electrode material and the electrochemical device having the positive electrode material achieve good high-voltage cycle performance and cycle stability.

First claim

What is claimed is:

1. A positive electrode material, comprising:
a lithium composite oxide represented by a general formula Li x Co a M b O 2-c , wherein M element comprises at least one of nickel (Ni), manganese (Mn), magnesium (Mg), aluminum (Al), Titanium (Ti), vanadium (V), chromium (Cr), iron (Fe), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), calcium (Ca), strontium (Sr), tungsten (W), yttrium (Y), lanthanum (La), zirconium (Zr), or silicon (Si), and 0.8≤x≤1.2, 0.8≤a≤1, 0≤b≤0.2, −0.1≤c≤0.2; and
the positive electrode material comprises stress relief particles, wherein cavities are formed inside the stress relief particles;
wherein a shape of a cross section of each cavity on a scanning electron microscope image satisfies the following relational expression:
(a longest diameter of the cavity−a shortest diameter of the cavity)/the longest diameter of the cavity≤30%,
wherein the longest diameter and the shortest diameter are a longest diameter and a shortest diameter that respectively pass through an area centroid of the cross section of the cavity, and the longest diameter of the cavity is larger than at least 100 nm.

2. The positive electrode material according to claim 1 , wherein a quantity of the cavities in each stress relief particle is less than 500.

3. The positive electrode material according to claim 1 , wherein a particle size Dv50 of the positive electrode material is 3 μm to 25 μm.

4. The positive electrode material according to claim 1 , wherein the stress relief particles form 2% to 30% of the positive electrode material.

5. An electrochemical device, comprising:
a positive electrode, comprising a positive active material layer, wherein the positive active material layer comprises a positive electrode material;
a negative electrode; and
a separator, wherein the separator is disposed between the positive electrode and the negative electrode;
wherein the positive electrode material comprises a lithium composite oxide represented by a general formula Li x Co a M b O 2-c , wherein M element comprises at least one of nickel (Ni), manganese (Mn), magnesium (Mg), aluminum (Al), Titanium (Ti), vanadium (V), chromium (Cr), iron (Fe), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), calcium (Ca), strontium (Sr), tungsten (W), yttrium (Y), lanthanum (La), zirconium (Zr), or silicon (Si), and 0.8≤x≤1.2, 0.8≤a≤1, 0≤b≤0.2,−0.1≤c≤0.2; and
the positive electrode material comprises stress relief particles, wherein cavities are formed inside the stress relief particles;
wherein a shape of a cross section of each cavity on a scanning electron microscope image satisfies the following relational expression:
(a longest diameter of the cavity−a shortest diameter of the cavity)/the longest diameter of the cavity≤30%,
wherein the longest diameter and the shortest diameter are a longest diameter and a shortest diameter that respectively pass through an area centroid of the cross section of the cavity, and the longest diameter of the cavity is larger than at least 100 nm.

6. The electrochemical device according to claim 5 , wherein a quantity of the cavities in each stress relief particle is less than 500.

7. The electrochemical device according to claim 5 , wherein a particle size Dv50 of the positive electrode material is 3 μm to 25 μm.

8. The electrochemical device according to claim 5 , wherein the stress relief particles form 2% to 30% of the positive electrode material.

9. The electrochemical device according to claim 5 , wherein in a cross section of the positive active material layer in a thickness direction, with the cross section being obtained by using an ion beam cross section polisher, a total quantity of the cavities in 100 particles of the positive electrode material is 20 to 1,000.

10. The electrochemical device according to claim 9 , wherein in the cross section of the positive active material layer in the thickness direction, with the cross section being obtained by using the ion beam cross section polisher, a total cross-sectional area of the 100 particles of the positive electrode material is S1, a total cross-sectional area of the cavities in the 100 particles of the positive electrode material is S0, and S0/S1 is 0.00001% to 0.3%.

11. An electronic device, comprising an electrochemical device, the electrochemical device comprising:
a positive electrode, comprising a positive active material layer, wherein the positive active material layer comprising a positive electrode material;
a negative electrode; and
a separator, wherein the separator is disposed between the positive electrode and the negative electrode;
wherein the positive electrode material comprises a lithium composite oxide represented by a general formula Li x Co a M b O 2-c , wherein M element comprises at least one of nickel (Ni), manganese (Mn), magnesium (Mg), aluminum (Al), Titanium (Ti), vanadium (V), chromium (Cr), iron (Fe), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), calcium (Ca), strontium (Sr), tungsten (W), yttrium (Y), lanthanum (La), zirconium (Zr), or silicon (Si), and 0.8≤x≤1.2, 0.8≤a≤1, 0≤b≤0.2,−0.1≤c≤0.2; and
the positive electrode material comprises stress relief particles, wherein cavities are formed inside the stress relief particles;
wherein a shape of a cross section of each cavity on a scanning electron microscope image satisfies the following relational expression:
(a longest diameter of the cavity−a shortest diameter of the cavity)/the longest diameter of the cavity≤30%,
wherein the longest diameter and the shortest diameter are a longest diameter and a shortest diameter that respectively pass through an area centroid of the cross section of the cavity, and the longest diameter of the cavity is larger than at least 100 nm.

12. The electronic device according to claim 11 , wherein a quantity of the cavities in each stress relief particle is less than 500.

13. The electronic device according to of claim 11 , wherein a particle size Dv50 of the positive electrode material is 3 μm to 25 μm.

14. The electronic device according to claim 11 , wherein the stress relief particles form 2% to 30% of the positive electrode material.

15. The electronic device according to claim 11 , wherein in a cross section of the positive active material layer in a thickness direction, with the cross section being obtained by using an ion beam cross section polisher, a total quantity of the cavities in 100 particles of the positive electrode material is 20 to 1,000.

16. The electronic device according to claim 15 , wherein in the cross section of the positive active material layer in the thickness direction, with the cross section being obtained by using the ion beam cross section polisher, a total cross-sectional area of the 100 particles of the positive electrode material is S1, a total cross-sectional area of the cavities in the 100 particles of the positive electrode material is S0, and S0/S1 is 0.00001% to 0.3%.

Assignees

• Ningde Amperex Technology Ltd

Inventors

• Wang Kai
• Zhang Fei
• Wang Meng
• Xu Leimin

Classifications

• H01M2004/028

  Positive electrodes · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M10/0525

  Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries · CPC title

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• Y02E60/10

  Energy storage using batteries · CPC title