Method for producing grain oriented electrical steel sheet

Patent metadata

Field	Value
Publication number	US-12110567-B2
Application number	US-202017421820-A
Country	US
Kind code	B2
Filing date	Jan 16, 2020
Priority date	Jan 16, 2019
Publication date	Oct 8, 2024
Grant date	Oct 8, 2024

Abstract

A method for producing a grain oriented electrical steel sheet includes a decarburization annealing process where an oxidation degree PH 2 O/PH 2 is controlled, an annealing separator applying process where a mass ratio of MgO and MCl in an annealing separator is controlled, a final annealing process where an oxidation degree is controlled when atmosphere includes hydrogen or a dew point is controlled when atmosphere consists of inert gas, and an insulation coating forming process where a mass ratio of phosphoric acid and metal compound in insulation coating forming solution is controlled.

First claim

What is claimed is:

1. A method for producing a grain oriented electrical steel sheet,
the method comprising:
a hot rolling process of hot-rolling a steel piece to obtain a hot rolled steel sheet, the steel piece including, as a chemical composition, by mass %,
0.030 to 0.100% of C,
0.80 to 7.00% of Si,
0.01 to 1.00% of Mn,
0 to 0.060% in total of S and Se,
0.010 to 0.065% of acid soluble Al,
0.004 to 0.012% of N,
0 to 0.30% of Cr,
0 to 0.40% of Cu,
0 to 0.50% of P,
0 to 0.30% of Sn,
0 to 0.30% of Sb,
0 to 1.00% of Ni,
0 to 0.008% of B,
0 to 0.15% of V,
0 to 0.20% of Nb,
0 to 0.10% of Mo,
0 to 0.015% of Ti,
0 to 0.010% of Bi, and
a balance consisting of Fe and impurities;
a cold rolling process of cold-rolling the hot rolled steel sheet to obtain a cold rolled steel sheet;
a decarburization annealing process of decarburization-annealing the cold rolled steel sheet to obtain a decarburization annealed sheet;
an annealing separator applying process of applying and drying an annealing separator including MgO to the decarburization annealed sheet;
a final annealing process of final-annealing the decarburization annealed sheet after applying the annealing separator to obtain a final annealed sheet;
an annealing separator removing process of removing a redundant annealing separator from a surface of the final annealed sheet; and
an insulation coating forming process of forming an insulation coating on the surface of the final annealed sheet,
wherein, in the decarburization annealing process,
PH 2 O/PH 2 which is an oxidation degree of an atmosphere is 0.01 to 0.15, an annealing temperature is 750 to 900° C., and a holding is 10 to 600 seconds,
wherein, in the annealing separator applying process,
the annealing separator further includes MCl which is at least one selected from chlorides of an alkali metal, an alkaline earth metal, and Bi, and MCl/MgO which is a mass ratio of MgO and MCl is 2 to 40%,
wherein, in the final annealing process,
an oxidation degree is 0.00010 to 0.2 when an atmosphere includes hydrogen, or a dew point is 0° C. or less when an atmosphere consists of an inert gas without hydrogen, and
wherein, in the insulation coating forming process,
an insulation coating forming solution in which a phosphoric acid and a metal compound are included and in which a mass ratio of the phosphoric acid to the metal compound is 2:1 to 1:2 is applied and is baked at 600 to 1150° C., and after decreasing a temperature, an insulation coating forming solution in which a phosphate and a colloidal silica are included and in which a metal compound is not included is applied and is baked at 600 to 1150° C., in order to form the insulation coating.

2. The method for producing the grain oriented electrical steel sheet according to claim 1 ,
the method including, between the hot rolling process and the cold rolling process,
at least one of a hot band annealing process of annealing the hot rolled steel sheet and a hot band pickling process of pickling the hot rolled steel sheet.

3. The method for producing the grain oriented electrical steel sheet according to claim 1 ,
wherein, in the decarburization annealing process, a nitriding treatment is conducted by annealing the cold rolled steel sheet in an atmosphere including ammonia.

4. The method for producing the grain oriented electrical steel sheet according to claim 1 ,
the method including, between the cold rolling process and the decarburization annealing process, between the decarburization annealing process and the annealing separator applying process, between the annealing separator removing process and the insulation coating forming process, or after the insulation coating forming process,
a magnetic domain refining process of conducting a magnetic domain refining treatment.

5. The method for producing the grain oriented electrical steel sheet according to claim 1 ,
wherein, in the annealing separator removing process, a pickling is conducted after water-washing using an acidic solution whose volume concentration is less than 20%.

6. The method for producing the grain oriented electrical steel sheet according to claim 1 ,
wherein, the steel piece includes, as the chemical composition, by mass %, at least one of
0.02 to 0.30% of Cr,
0.05 to 0.40% of Cu,
0.005 to 0.50% of P,
0.02 to 0.30% of Sn,
0.01 to 0.30% of Sb,
0.01 to 1.00% of Ni,
0.0005 to 0.008% of B,
0.002 to 0.15% of V,
0.005 to 0.20% of Nb,
0.005 to 0.10% of Mo,
0.002 to 0.015% of Ti, and
0.001 to 0.010% of Bi.

7. A method for producing a grain oriented electrical steel sheet,
the method comprising:
a hot rolling process of hot-rolling a steel piece to obtain a hot rolled steel sheet, the steel piece including, as a chemical composition, by mass %,
0.030 to 0.100% of C,
0.80 to 7.00% of Si,
0.01 to 1.00% of Mn,
0 to 0.060% in total of S and Se,
0.010 to 0.065% of acid soluble Al,
0.004 to 0.012% of N,
0 to 0.30% of Cr,
0 to 0.40% of Cu,
0 to 0.50% of P,
0 to 0.30% of Sn,
0 to 0.30% of Sb,
0 to 1.00% of Ni,
0 to 0.008% of B,
0 to 0.15% of V,
0 to 0.20% of Nb,
0 to 0.10% of Mo,
0 to 0.015% of Ti,
0 to 0.010% of Bi, and
a balance comprising Fe and impurities,
a cold rolling process of cold-rolling the hot rolled steel sheet to obtain a cold rolled steel sheet;
a decarburization annealing process of decarburization-annealing the cold rolled steel sheet to obtain a decarburization annealed sheet;
an annealing separator applying process of applying and drying an annealing separator including MgO to the decarburization annealed sheet;
a final annealing process of final-annealing the decarburization annealed sheet after applying the annealing separator to obtain a final annealed sheet;
an annealing separator removing process of removing a redundant annealing separator from a surface of the final annealed sheet; and
an insulation coating forming process of forming an insulation coating on the surface of the final annealed sheet,
wherein, in the decarburization annealing process,
PH 2 O/PH 2 which is an oxidation degree of an atmosphere is 0.01 to 0.15, an annealing temperature is 750 to 900° C., and a holding is 10 to 600 seconds,
wherein, in the annealing separator applying process,
the annealing separator further includes MCl which is at least one selected from chlorides of an alkali metal, an alkaline earth metal, and Bi, and MCl/MgO which is a mass ratio of MgO and MCl is 2 to 40%,
wherein, in the final annealing process,
an oxidation degree is 0.00010 to 0.2 when an atmosphere includes hydrogen, or a dew point is 0° C. or less when an atmosphere comprises an inert gas without hydrogen, and
wherein, in the insulation coating forming process,
an insulation coating forming solution in which a phosphoric acid and a metal compound are included and in which a mass ratio of the phosphoric acid to the metal compound is 2:1 to 1:2 is applied and is baked at 600 to 1150° C., and after decreasing a temperature, an insulation coating forming solution in which a phosphate and a colloidal silica are included and in which a metal compound is not included is applied and is baked at 600 to 1150° C., in order to form the insulation coating.

Assignees

• Nippon Steel Corp

Inventors

• TAKATANI Shinsuke
• Ushigami Yoshiyuki

Classifications

• H01F1/147

  Alloys characterised by their composition {(treatment thereof for enhancing their electromagnetic properties C21D8/12)} · CPC title

• C22C2202/02

  Magnetic · CPC title

• C22C38/60

  containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur · CPC title

• C22C38/54

  with boron · CPC title

• C22C38/50

  with titanium or zirconium · CPC title