Smooth high solids film coating composition comprising water soluble cellulose ether, process for preparing the same and method of use thereof

Patent metadata

Field	Value
Publication number	US-12098291-B2
Application number	US-201917282972-A
Country	US
Kind code	B2
Filing date	Oct 7, 2019
Priority date	Oct 5, 2018
Publication date	Sep 24, 2024
Grant date	Sep 24, 2024

Abstract

The present application provides high solids film coating compositions comprising a water-soluble cellulose ether, hydroxy propyl cellulose (HPC), a poly (N-vinyl pyrrolidone-co-vinyl acetate) copolymer, a film-forming agent based on D-glucose, plasticizer, medium chain triglycerides (MCT) and an anti-tack agent. The invention further provides a process for preparing the above described film coating compositions and method of coating solid substrate with such coating compositions.

First claim

What is claimed is:

1. A colorant film coating composition having total solids content of from about 20 wt. % to about 35 wt. %, the composition comprising:
(i) from 0.1 wt. % to 15 wt. % of hydroxypropyl cellulose (HPC), a water soluble cellulose ether;
(ii) from 0.1 wt. % to 40 wt. % of N-vinyl-2-pyrrolidone-co-vinyl acetate (PVP/VA) copolymer;
(iii) from 0.1 wt. % to 20 wt. % of polydextrose, a film forming agent;
(iv) from 0.0 wt. % to 15 wt. % of polyethylene glycol, a plasticizer; and
(v) from 1 wt. % to 10 wt. % of medium chain triglycerides (MCT).

2. The colorant coating composition according to claim 1 , wherein the composition further comprises a pigment content of up to 30 wt. % selected from the group consisting of FD&C Blue #1, FD&C Blue #2, FD&C Red #40, FD&C Yellow #5, FD&C Yellow #6, carmine, saffron, riboflavin, caramel, red cabbage extract, titanium dioxide, and iron oxides (red, yellow & black).

3. A non-colorant film coating composition having total solids content of from about 20 wt. % to about 32 wt. %, the composition comprising:
(i) from 0.1 wt. % to 20 wt. % of hydroxypropyl cellulose (HPC), a water soluble cellulose ether;
(ii) from 0.1 wt. % to 40 wt. % of N-vinyl-2-pyrrolidone-co-vinyl acetate (PVP/VA) copolymer;
(iii) from 0.1 wt. % to 20 wt. % of polydextrose, a film forming agent;

(iv) from 0.0 wt. % to 15 wt. % of polyethylene glycol, a plasticizer; and
(v) from 1 wt. % to 10 wt. % of medium chain triglycerides (MCT).

4. The coating composition according to claim 1 , wherein the composition further comprises from about 5 wt. % to about 20 wt. % of an anti-tack agent selected from talc or glyceryl monostearate.

5. A method of coating solid substrates comprising the steps of:
(a) creating a coating suspension comprising the colorant coating composition of claim 1 or the non-colorant coating composition of claim 3 ,
(b) applying the coating suspension of step (a) to the surface of the solid substrate to form a coating layer,
(c) drying said coating layer to form a dry coating on the surface of the solid substrate, and
(d) obtaining the final coated solid product.

6. The method according to claim 5 , wherein said solid substrate is an agricultural, a nutritional or a pharmaceutical product.

7. The method according to claim 5 , wherein process time for coating is reduced by up to 65% when compared to a traditional HPMC based film coating system.

8. A coated solid product produced by a method comprising the steps of:
(a) creating a coating suspension comprising the colorant coating composition of claim 1 or the non-colorant coating composition of claim 3 ,
(b) applying the coating suspension of step (a) to the surface of the solid substrate to form a coating layer,
(c) concurrently drying said coating layer to form a dry coating on the surface of the solid substrate, and
(d) obtaining the final coated solid product.

9. The coated solid substrate according to claim 8 , wherein the coated product is a coated agricultural product, a coated nutritional product or a coated pharmaceutical product.

10. The coated solid substrate according to claim 9 , wherein the coated pharmaceutical product is formulated into a pharmaceutical oral solid dosage form.

Assignees

• Isp Investments Llc

Inventors

• Karan Kapish
• Hach Ronald
• Porter Stuart C

Classifications

• C09D139/06

  Homopolymers or copolymers of N-vinyl-pyrrolidones · CPC title

• C09D131/04

  Homopolymers or copolymers of vinyl acetate · CPC title

• C09D105/02

  Dextran; Derivatives thereof · CPC title

• C08K2003/2241

  Titanium dioxide · CPC title

• C08K5/11

  of acyclic polycarboxylic acids · CPC title