Abstract

The invention relates to an additive-manufacture feedstock, comprising an ethylene-vinyl ester polymer having a melt flow rate of from 0.1 to 150 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238, and a vinyl ester content of from about 1.0 wt % to about 30 wt %, wherein the ethylene-vinyl ester polymer exhibits a Shore A hardness of at least about 60. The pellets and filaments produced from the additive-manufacture feedstock have a high degree of printability in material-extrusion-based 3D printing technology, and can be used to produce 3D printing articles with a high consistency to the targeted 3D model and substantially no warpage. The invention also relates to methods of making the additive-manufacture feedstock and methods of 3D printing using the additive-manufacture feedstock in various forms.

First claim

What is claimed is:

1. An additive-manufacture feedstock, comprising
an ethylene-vinyl ester polymer, the ethylene-vinyl ester polymer having:
a melt flow rate of from 0.1 to 150 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238, and
a vinyl ester content of from 1.0 to 30 wt %, relative to 100 wt % of the ethylene-vinyl ester polymer,
wherein the ethylene-vinyl ester polymer exhibits a Shore A hardness of at least 60, and
wherein the ethylene-vinyl ester polymer, in neat form, has an elastic modulus of from 10 to 1500 MPa, measured according to ASTM D 638, and/or a melt viscosity of from 100 to 1000 Pa·s, measured at a shear rate of 1000 s −1 .

2. The additive-manufacture feedstock according to claim 1 , wherein the ethylene-vinyl ester polymer comprises at least one member selected from the group consisting of a tubular-reactor-polymerized ethylene-vinyl acetate copolymer, an autoclave-reactor-polymerized ethylene-vinyl acetate copolymer, and an ethylene-vinyl acetate-vinyl versatate terpolymer.

3. The additive-manufacture feedstock according to claim 1 , wherein the vinyl ester of the ethylene-vinyl ester polymer is vinyl acetate.

4. The additive-manufacture feedstock according to claim 3 , wherein the vinyl acetate content is from 5.5 to 20 wt %, relative to 100 wt % of the ethylene-vinyl acetate polymer.

5. The additive-manufacture feedstock according to claim 1 , wherein the ethylene-vinyl ester polymer has a melt flow rate of from 0.1 to 50 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238.

6. The additive-manufacture feedstock according to claim 1 , wherein the ethylene-vinyl ester polymer has a melt flow rate of from 0.1 to 20 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238.

7. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer has a melt flow rate of from 2 to 6 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238.

8. The additive-manufacture feedstock according to claim 1 , wherein the ethylene-vinyl ester polymer exhibits a Shore A hardness of at least 80.

9. The additive-manufacture feedstock according to claim 1 , wherein the ethylene-vinyl ester polymer exhibits a Shore A hardness of at least 90.

10. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer exhibits a melting point of at least 80° C.

11. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer exhibits a melting point of at least 85° C.

12. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer has a melt flow rate of from 0.1 to 20 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238, and exhibits a Shore A hardness of at least 80.

13. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer is prepared by a tubular-reactor polymerization.

14. The additive-manufacture feedstock according to claim 3 , wherein the ethylene-vinyl acetate polymer has a linear backbone configuration.

15. The additive-manufacture feedstock according to claim 13 , wherein:
the ethylene-vinyl acetate polymer exhibits a Shore A hardness of at least 90; or
the ethylene-vinyl acetate polymer has a vinyl acetate content of from 5.5 to 20 wt %, relative to 100 wt % of the ethylene-vinyl acetate polymer, and a melt flow rate of from 0.1 to 20 g/10 min (190° C./2.16 kg), measured according to ASTM D 1238.

16. The additive-manufacture feedstock according to claim 1 , further comprising an additive selected from the group consisting of an antioxidant, a pigment, an inorganic filler, a reinforcement, an adhesion-promoting agent, a biocide, a whitening agent, a nucleating agent, an anti-static agent, an anti-blocking agent, a processing aid, a flame-retardant, a plasticizer, a heat stabilizer, a light stabilizer, a viscosity-modifier, a polyethylene, a polypropylene, an elastomer, a thermoplastic polyurethane, a sizing agent or compatibilizer, a rubber, a thermoplastic hydrocarbon resin, and any combination thereof.

17. The additive-manufacture feedstock according to claim 16 , wherein the additive is an inorganic filler comprising at least one member selected from the group consisting of talc, natural fiber, carbon fiber, glass fiber, metal fibers, ceramic fibers, marble dust, cement dust, rice husks, clay, carbon black, feldspar, silica, glass, fumed silica, silicate, calcium silicate, silicic acid powder, glass microspheres, mica, magnesium oxide, antimony oxide, zinc oxide, barium sulfate, wollastonite, alumina, aluminum silicate, titanium oxide, calcium carbonate, and polyhedral oligomeric silsesquioxane.

18. The additive-manufacture feedstock according to claim 16 , comprising:
at least 51% of the ethylene-vinyl ester polymer, and not more than 49% of the additive, relative to 100% of the additive manufacture feedstock.

19. A filament, comprising the additive-manufacture feedstock according to claim 1 .

20. The filament according to claim 19 , having a length of 0.1 to 50000 meters.

21. The filament according to claim 19 , having a diameter of from 1 to 5 mm, ±0.05 mm.

22. The filament according to claim 19 , having a diameter of 1.75 mm or 2.85 mm, ±0.05 mm.

23. A distribution of pellets, each pellet comprising the additive-manufacture feedstock according to claim 1 .

24. The distribution of pellets according to claim 23 , having a count of 5 to 60 pellets per gram of the additive-manufacture feedstock.

25. The distribution of pellets according to claim 23 , having a count of 5 to 20 pellets per gram of the additive-manufacture feedstock.

26. The distribution of pellets according to claim 23 , having a count of 30 to 60 pellets per gram of the additive-manufacture feedstock.

27. An additive-manufacture feedstock according to claim 1 , comprising a □ 2 /□ 1 value of from 0.5 to 1.

28. A method of three-dimensional printing, the method comprising:
(1) supplying the additive-manufacture feedstock according to claim 1 to a printing apparatus and forming a hot-melt of the additive-manufacture feedstock;
(2) depositing the hot-melt of the additive-manufacture feedstock from the printing apparatus on a substrate to form a first deposited printing layer;
(3) repeating (1) and (2) to deposit a second printing layer on the first printing layer; and
(4) optionally depositing at least one further printing layer on said second printing layer.

29. The method of three-dimensional printing according to claim 28 , wherein the printing apparatus employs a fused filament fabrication method.

30. The method of three-dimensional printing according to claim 28 , wherein the printing apparatus employs a pellet extrusion method.

Assignees

• Braskem America Inc

Inventors

• Soares Juliana Breda
• Fallon Jacob
• Bernardes Dillan Passos
• Oviedo Mauro Alfredo Soto
• Domingues Jr Nei Sebastião
• Cangussu Manoela Ellwanger
• Sing Michelle K
• Da Silva Jorge Manuel Jardim

Classifications

• C08F2800/20

  as weight or mass percentages · CPC title

• C08F210/02

  Ethene · CPC title

• B29K2105/16

  Fillers · CPC title

• B29K2023/083

  EVA, i.e. ethylene vinyl acetate copolymer · CPC title

• B33Y70/10

  Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials · CPC title