Preparation method of super absorbent polymer and super absorbent polymer prepared therefrom

Patent metadata

Field	Value
Publication number	US-12083497-B2
Application number	US-202017413793-A
Country	US
Kind code	B2
Filing date	May 4, 2020
Priority date	May 7, 2019
Publication date	Sep 10, 2024
Grant date	Sep 10, 2024

Abstract

The present disclosure relates to a method for preparing a super absorbent polymer that enables the preparation of a more improved super absorbent polymer even without excessive use of a surfactant and use of a foaming agent, and a super absorbent polymer prepared therefrom which exhibits a superior absorption rate.

First claim

The invention claimed is:

1. A method for preparing a super absorbent polymer comprising:
preparing a monomer mixture including a water-soluble ethylenically unsaturated monomer having an acidic group of which at least a part is neutralized;
preparing a solution containing an anionic surfactant;
passing the solution containing the anionic surfactant through a tubular flow channel having a plurality of projecting pins therein at a space velocity of 50 to 1500 (min −1 );
subsequently mixing the solution containing the anionic surfactant and the monomer mixture to form a mixed solution comprising the anionic surfactant, the monomer mixture, and an internal crosslinking agent;

performing crosslinking polymerization of the mixed solution to form a hydrogel polymer;
drying, pulverizing and classifying the hydrogel polymer to form a base polymer powder; and
further cross-linking the surface of the base polymer powder in the presence of a surface crosslinking agent to form a surface cross-linked layer,
wherein the anionic surfactant is used at a concentration of 50 to 200 ppmw of the water-soluble ethylenically unsaturated monomer.

2. The method for preparing a super absorbent polymer according to claim 1 , wherein the anionic surfactant comprises one or more of sodium dodecyl sulfate, ammonium lauryl sulfate, sodium laureth sulfate, dioctyl sodium sulfosuccinate, perfluorooctane sulfonate, perfluorobutane sulfonate, alkyl-aryl ether phosphate, alkyl ether phosphate, sodium myreth sulfate or carboxylate salt.

3. The method for preparing a super absorbent polymer according to claim 1 , wherein the monomer mixture further includes 0.1% by weight or less of a nonionic surfactant having an HLB value of 4 to 15.

4. The method for preparing a super absorbent polymer according to claim 3 , wherein the nonionic surfactant is one or more selected from the group consisting of fatty acid ester, sorbitan trioleate, polyethoxylated sorbitan monooleate, sorbitan monooleate and sugar ester.

5. The method for preparing a super absorbent polymer according to claim 3 , further comprising:
forming a primary mixture in a solution state containing the water-soluble ethylenically unsaturated monomer and the internal crosslinking agent;
mixing the primary mixture with a basic aqueous solution to form a secondary mixture in which at least a part of the acid groups of the unsaturated monomer is neutralized; and
mixing a solution containing the nonionic surfactant having an HLB value of 4 to 15, and a solution containing an initiator, other additives and the anionic surfactant with the secondary mixture while passing the above solutions through the tubular flow channel having the plurality of projecting pins therein at the space velocity of 50 to 1500 (min −1 ).

6. The method for preparing a super absorbent polymer according to claim 5 , wherein mixing the solution containing the anionic surfactant further comprises supplying and mixing an aqueous solution containing the anionic surfactant at a concentration of 0.1 to 0.3% by weight of the water soluble ethylenically unsaturated monomer.

7. The method for preparing a super absorbent polymer according to claim 1 , wherein the crosslinking polymerization of the hydrogel polymer is performed by solution polymerization with respect to the monomer mixture in an aqueous solution state.

Assignees

• Lg Chemical Ltd

Inventors

• Lee Sang Gi
• Kim Mookon
• Lee Yong Hun
• Nam Hyemi
• Jeong Jiyoon
• Lee Chang Hun

Classifications

• C08J2333/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C08J3/245 Primary

  Differential crosslinking of one polymer with one crosslinking type, e.g. surface crosslinking · CPC title

• C08J3/12

  Powdering or granulating · CPC title

• C08J3/075

  Macromolecular gels · CPC title

• C08F2810/20

  leading to a crosslinking, either explicitly or inherently · CPC title