Fabric for airbag and method for manufacturing the same

Patent metadata

Field	Value
Publication number	US-12060028-B2
Application number	US-201917767879-A
Country	US
Kind code	B2
Filing date	Dec 27, 2019
Priority date	Dec 27, 2019
Publication date	Aug 13, 2024
Grant date	Aug 13, 2024

Abstract

This invention relates to fabric for airbag comprising a textile substrate; and a coating layer on at least one side of the textile substrate, wherein coating layer comprises polyurethane resin, a crosslinking agent, and a hydrophilic thickener, and the crosslinking agent is a compound having a blocked active group, and a method for preparing fabric for airbag, comprising steps of: preparing a textile substrate; and forming a coating layer on at least one side of the textile substrate, wherein the step of forming a coating layer comprise steps of: adding a crosslinking agent and a hydrophilic thickener to an aqueous polyurethane dispersion to prepare a coating solution; applying the coating solution on at least one side of the textile substrate; drying the textile substrate on which the coating solution is applied; and heat treating the dried textile substrate.

First claim

The invention claimed is:

1. A fabric for airbag comprising;
a textile substrate; and
a coating layer on at least one side of the textile substrate,
wherein the coating layer comprises polyurethane resin, a crosslinking agent, and a hydrophilic thickener,
wherein the hydrophilic thickener is a non-associative thickener, and
the crosslinking agent is a compound having a blocked active group,
wherein the crosslinking agent is a polyisocyanate compound or a polycarbodiimide compound to which one or more blocking components selected from the group consisting of 3,5-dimethyl pyrazole (DMP), ε-caprolactam, and methylethylketoxime are bonded.

2. The fabric for airbag according to claim 1 , wherein penetration level of the coating layer into the textile substrate defined by the following Formula 1, is 10 to 50%:
Penetration level (%)=( D/T )×100  Formula 1:

wherein, D is the maximum depth of penetration of the coating layer into the textile substrate, and T is the thickness of the textile substrate.

3. The fabric for airbag according to claim 1 , wherein the textile substrate is fabric comprising warp yarns and weft yarns, and flex abrasion of the airbag fabric, measured according to ISO 5981 standard after aging under temperature of 70+2° C. and relative humidity of 95+2% for 408 hours, is 1,000 strokes or more, in both warp direction and weft direction.

4. The fabric for airbag according to claim 1 , wherein the hydrophilic thickener is a non-Newtonian pseudoplastic acryl-based thickener.

5. The fabric for airbag according to claim 1 , wherein the textile substrate is one piece woven (OPW) type fabric comprising plural warp yarns and weft yarns, each of the warp yarns and weft yarns has fineness of 210 to 1500 denier, the density of warp yarns and the density of weft yarns are respectively 40 th/inch to 80 th/inch, based on one layer of the chamber region of the fabric, and each of the warp yarns and weft yarns comprises at least one of aliphatic polyamide, aromatic polyamide, polyester, and polyolefin.

6. A method for preparing fabric for airbag, comprising steps of:
preparing a textile substrate; and
forming a coating layer on at least one side of the textile substrate, wherein the step of forming a coating layer comprise steps of:
adding a crosslinking agent and a hydrophilic thickener to an aqueous polyurethane dispersion to prepare a coating solution;
applying the coating solution on at least one side of the textile substrate;
drying the textile substrate on which the coating solution is applied; and
heat treating the dried textile substrate, and the crosslinking agent is a compound having a blocked active group,
wherein the thickener is a non-associative thickener, and
wherein the crosslinking agent is a polyisocyanate compound or a polycarbodiimide compound to which one or more blocking components selected from the group consisting of 3,5-dimethyl pyrazole (DMP), ε-caprolactam, and methylethylketoxime are bonded.

7. The method for preparing fabric for airbag according to claim 6 , wherein the hydrophilic thickener is a non-Newtonian pseudoplastic acryl-based thickener.

8. The method for preparing fabric for airbag according to claim 6 , wherein the thickener has viscosity of 25,000 to 60,000 cps, and the coating solution has viscosity of 6,000 to 30,000 cps.

9. The method for preparing fabric for airbag according to claim 6 , wherein the amount of the coating solution applied on at least one side of the textile substrate is 15 to 50 gsm.

10. The method for preparing fabric for airbag according to claim 6 , wherein the drying step is conducted by raising a temperature between 80° C. and 150° C., and the heat treatment step is conducted at a temperature greater than 150° C.

Assignees

• Kolon Inc

Inventors

• Kim Ki Jeong
• Lee Sang-Mok
• Kim Gi-Woong
• Heo Jin Wook

Classifications

• D06N2211/268

  Airbags · CPC title

• D06N2205/20

  Cured materials, e.g. vulcanised, cross-linked · CPC title

• D06N2203/068

  Polyurethanes · CPC title

• D06N3/14

  with polyurethanes · CPC title

• B60R2021/23519

  Resin · CPC title