Isocyanate-functional polymer components and polyurethane articles formed from recycled polyurethane articles and associated methods for forming same

Patent metadata

Field	Value
Publication number	US-12054589-B2
Application number	US-201816636092-A
Country	US
Kind code	B2
Filing date	Aug 1, 2018
Priority date	Aug 7, 2017
Publication date	Aug 6, 2024
Grant date	Aug 6, 2024

Abstract

A method of forming an isocyanate-functional polymer component includes forming a first mixture by mixing a recycled polyurethane article and a first isocyanate component having isocyanate-functional groups. The first mixture is heated to a temperature sufficient to transform the recycled polyurethane article from a solid form to a liquid form and react the liquid recycled polyurethane component with the first isocyanate component to form an isocyanate-functional polymer component having an isocyanate-functional group content greater than zero and less than isocyanate-functional group content of the first isocyanate component. The formed isocyanate-functional polymer component may then be used for forming a polyurethane article or polyurethane foam article that is the reaction product of the formed isocyanate-functional polymer component, a second isocyanate component and an isocyanate-reactive component having hydroxyl-functional groups.

First claim

The invention claimed is:

1. A method of forming an isocyanate-functional polymer component, the method comprising:
forming a first mixture by mixing a recycled polyurethane article in solid form and a first isocyanate component having isocyanate-functional groups;
heating the first mixture to a temperature sufficient to transform the recycled polyurethane article in solid form to a recycled polyurethane article in liquid form; and
reacting the recycled polyurethane article in the liquid form with the first isocyanate component at the temperature for a time sufficient to form the isocyanate-functional polymer component,
wherein the isocyanate-functional group content (NCO content) of the isocyanate-functional polymer component is greater than zero and is less than an NCO content of the first isocyanate component, wherein the NCO content of the Isocyanate-functional polymer component and the NCO content of the first isocyanate component are each determined according to ASTM D2572.

2. The method according to claim 1 , wherein the NCO content of the isocyanate-functional polymer component is from 2 to 98 weight percent less than the NCO content of the first isocyanate component.

3. The method according to claim 2 , wherein the NCO content of the isocyanate-functional polymer component ranges from 1 to 47 weight percent based on the total weight of the isocyanate-functional polymer component.

4. The method according to claim 1 , wherein the provided recycled polyurethane article is in a non-comminuted solid form, and wherein the method further comprises the step of pulvering the recycled polyurethane article to form a comminuted recycled polyurethane article in solid form prior to the step of mixing the comminuted recycled polyurethane article and a first isocyanate component having isocyanate-functional groups.

5. The method according to claim 1 , wherein the temperature ranges from 50 to 300 degrees Celsius.

6. The method according to claim 1 , wherein the temperature ranges from 50 to 300 degrees Celsius and the time ranges from 1 to 48 hours.

7. The method according to claim 1 , wherein the isocyanate-functional polymer component has a viscosity ranging from 5 to 10,000 centipoise at 25 degrees Celsius as measured in accordance with ASTM D2196.

8. The method according to claim 1 , wherein the recycled polyurethane article comprises a recycled polyurethane foam article.

9. The method according to claim 1 , wherein the recycled polyurethane article comprises a recycled flexible polyurethane foam article.

10. The method according to claim 1 , wherein the recycled polyurethane article comprises a recycled rigid polyurethane foam article.

11. The method according to claim 1 , wherein the recycled polyurethane article comprises a recycled TPU article.

Assignees

• Basf Se

Inventors

• Kumar Rajesh
• Wujcik Steven
• Lebediniski Nikolay
• Milantoni Christopher

Classifications

• C08G2110/0025

  rigid · CPC title

• C08G2110/0008

  flexible · CPC title

• C08J2375/04

  Polyurethanes · CPC title

• C08G18/797

  containing carbodiimide and/or uretone-imine groups · CPC title

• C08G18/76

  aromatic · CPC title