Electroconductive paste

Patent metadata

Field	Value
Publication number	US-12043722-B2
Application number	US-202017762832-A
Country	US
Kind code	B2
Filing date	Sep 25, 2020
Priority date	Sep 27, 2019
Publication date	Jul 23, 2024
Grant date	Jul 23, 2024

Abstract

The present invention provides a conductive paste which leaves less fine undissolved matter when dissolved in an organic solvent and thus can be easily filtrated, which has excellent printability, and which can exhibit excellent surface smoothness after printing. Provided is a conductive paste used for forming an electrode of a multilayer ceramic capacitor, the conductive paste containing: a polyvinyl acetal resin; an organic solvent; and a conductive powder, the polyvinyl acetal resin having a wave number A (cm −1 ) of a peak within a range of 3,100 to 3,700 cm −1 in an IR absorption spectrum measured using an infrared spectrophotometer; and a hydroxy group content (mol %), the wavenumber A of the peak and the hydroxy group content satisfying relations of the following formulas (1) and (2):

[(3,470− A )/Hydroxy group content]≤5.0  (1)

(3,470− A )≤150  (2)

wherein A is a wavenumber which is lower than 3,470 cm −1 and at which a transmittance a (%) satisfying [100−(100−X)/2] is exhibited, where X (%) is s minimum transmittance of the peak within the wavenumber range of 3,100 to 3,700 cm −1 .

First claim

The invention claimed is:

1. A conductive paste used for forming an electrode of a multilayer ceramic capacitor, the conductive paste comprising:
a polyvinyl acetal resin;
an organic solvent; and
a conductive powder,
the polyvinyl acetal resin having:
a wavenumber A (cm −1 ) of a peak within a range of 3,100 cm −1 or higher and lower than 3,470 cm −1 in an IR absorption spectrum measured using an infrared spectrophotometer; and
a hydroxy group content (mol %),
the wavenumber A of the peak and the hydroxy group content satisfying relations of the following formulas (1) and (2):
[(3,470− A )/Hydroxy group content]≤5.0  (1)

(3,470− A )≤150  (2)

wherein A is a wavenumber which is lower than 3,470 cm −1 and at which a transmittance a (%) satisfying [100−(100−X)/2] is exhibited, where X (%) is a minimum transmittance of the peak within the wavenumber range of 3,100 to 3,700 cm −1 .

2. The conductive paste according to claim 1 ,
wherein the polyvinyl acetal resin has a wavenumber B (cm −1 ) of the peak within the wavenumber of higher than 3,470 cm −1 and 3,700 cm −1 or lower in the IR absorption spectrum measured using the infrared spectrophotometer; and
the wavenumber A of the peak and the wavenumber B of the peak satisfy a relation of the following formula (3):
(3,470 −A )/( B− 3,470)≤1.4  (3)

wherein B is a wavenumber which is higher than 3,470 cm −1 and at which the transmittance a (%) satisfying [100−(100−X)/2] is exhibited, where X (%) is the minimum transmittance of the peak within the wavenumber range of 3,100 to 3,700 cm −1 .

3. The conductive paste according claim 2 ,
wherein the polyvinyl acetal resin has a hydroxy group content of 16 to 25 mol %, an acetyl group content of 0.1 to 12 mol %, and an acetoacetal group content of 27 mol % or less.

4. The conductive paste according to claim 3 ,
wherein the polyvinyl acetal resin contains a carboxy group-containing constitutional unit in an amount of 0.01 to 1.0 mol %.

5. The conductive paste according to claim 2 ,
wherein the polyvinyl acetal resin contains a carboxy group-containing constitutional unit in an amount of 0.01 to 1.0 mol %.

6. The conductive paste according claim 1 ,
wherein the polyvinyl acetal resin has a hydroxy group content of 16 to 25 mol %, an acetyl group content of 0.1 to 12 mol %, and an acetoacetal group content of 27 mol % or less.

7. The conductive paste according to claim 6 ,
wherein the polyvinyl acetal resin contains a carboxy group-containing constitutional unit in an amount of 0.01 to 1.0 mol %.

8. The conductive paste according to claim 1 ,
wherein the polyvinyl acetal resin contains a carboxy group-containing constitutional unit in an amount of 0.01 to 1.0 mol %.

Assignees

• Sekisui Chemical Co Ltd

Inventors

• Kobayashi Hiroko
• Nakamura Kazuto

Classifications

• H01G4/0085

  Fried electrodes · CPC title

• C09D5/24

  Electrically-conducting paints {(conductive materials H01B1/00)} · CPC title

• C09D11/52

  Electrically conductive inks · CPC title

• C08K3/22

  of metals · CPC title

• C08F8/28

  Condensation with aldehydes or ketones · CPC title