Process for the facile electrosynthesis of graphene from CO2

Patent metadata

Field	Value
Publication number	US-12024782-B2
Application number	US-202318354435-A
Country	US
Kind code	B2
Filing date	Jul 18, 2023
Priority date	May 28, 2019
Publication date	Jul 2, 2024
Grant date	Jul 2, 2024

Abstract

The present invention relates to the production of graphene from CO 2 through electrolysis and exfoliation processes. One embodiment is a method for producing graphene comprising (i) performing electrolysis between an electrolysis anode and an electrolysis cathode in a molten carbonate electrolyte to generate carbon nanomaterial on the cathode, and (ii) electrochemically exfoliating the carbon nanomaterial from a second anode to produce graphene. The exfoliating step produces graphene in high yield than thicker, conventional graphite exfoliation reactions. CO 2 can be the sole reactant used to produce the valuable product as graphene. This can incentivize utilization of CO 2 , and unlike alternative products made from CO 2 such as carbon monoxide or other fuels such as methane, use of the graphene product does not release this greenhouse gas back into the atmosphere.

First claim

What is claimed is:

1. A method for producing carbon nano-platelets comprising:
(a) heating a carbonate electrolyte to obtain a molten carbonate electrolyte;
(b) disposing the molten carbonate electrolyte between an electrolysis anode and an electrolysis cathode in a cell; and
(c) applying an electrical current to the electrolysis cathode and the electrolysis anode in the cell to electrolyze the carbonate and generate carbon nano-platelets on the electrolysis cathode without the formation of transition metal nucleation sites on the cathode,
wherein the molten carbonate electrolyte comprises one or more transition metal nucleating agents and the conditions for electrolysis reduce the solubility of one or more of the transition metal nucleating agents.

2. The method of claim 1 , wherein the carbonate electrolyte comprises an oxide additive.

3. The method of claim 2 , wherein the oxide additive comprises lithium oxide.

4. The method of claim 1 , wherein the one or more transition metal nucleating agents for which solubility has been reduced are selected from nickel, chromium, iron, and any combination of any of the foregoing.

5. The method of claim 1 , wherein the conditions for reducing the solubility of one or more transition metal nucleating agents during electrolysis include (a) an electrolyte comprising (i) a lithium carbonate and (ii) one or both of sodium carbonate and potassium carbonate, (b) decreasing the electrolysis temperature, (c) decreasing the concentration of lithium in the electrolyte, (d) increasing the electrolysis current density, or (e) any combination of any of the foregoing.

6. The method of claim 1 , wherein the electrolyzed carbonate in step (c) is replenished by addition of carbon dioxide.

7. The method of claim 6 , wherein the source of the added carbon dioxide is one of air, pressurized CO 2 , concentrated CO 2 , a power generating industrial process, an iron generating industrial process, a steel generating industrial process, a cement formation process, an ammonia formation industrial process, an aluminum formation industrial process, a manufacturing process, an oven, a smokestack, or an internal combustion engine.

8. The method of claim 1 , wherein the electrolysis cathode comprises stainless steel, cast iron, a nickel alloy, a material that resists corrosion in the presence of the molten carbonate electrolyte, or any combination of the foregoing.

9. The method of claim 1 , wherein the electrolysis cathode is coated with zinc.

10. The method of claim 1 , wherein in step (c), electrical current is applied with stepwise increases.

11. The method of claim 1 , wherein the molten carbonate electrolyte comprises an alkali metal carbonate, an alkali earth metal carbonate, or any combination thereof.

12. The method of claim 11 , wherein the alkali metal carbonate or alkali earth metal carbonate is lithium carbonate, sodium carbonate, potassium carbonate, rubidium carbonate, cesium carbonate, francium carbonate, beryllium carbonate, magnesium carbonate, calcium carbonate, strontium carbonate, barium carbonate, radium carbonate, or any mixture thereof.

13. The method of claim 1 , wherein the molten carbonate electrolyte comprises lithium carbonate.

14. The method of claim 1 , wherein the molten carbonate electrolyte further comprises one or more additional oxygen, sulfur, halide, nitrogen or phosphorous containing inorganic salts.

15. The method of claim 1 , wherein the coulombic efficiency in step (c) is greater than about 80%.

16. The method of claim 1 , wherein the method results in a coulombic efficiency in step (c) is about 100%.

17. The method of claim 1 , wherein the electrolysis reaction is performed at a current density of between about 5 and about 1000 mA cm 2 .

18. The method of claim 1 , wherein step (c) also produces molecular oxygen (O 2 ).

19. The method of claim 1 , wherein the method further comprises electrochemically exfoliating the carbon nanoplatelets from a second anode to produce graphene having 1 to 5 layers.

Assignees

• C2Cnt Llc

Inventors

• Licht Stuart

Classifications

• C25B1/135 Primary

  Carbon · CPC title

• C25B11/075

  consisting of a single catalytic element or catalytic compound · CPC title

• C25B11/057

  consisting of a single element or compound · CPC title

• C25B11/051

  Electrodes formed of electrocatalysts on a substrate or carrier · CPC title

• C25B9/17

  Cells comprising dimensionally-stable non-movable electrodes; Assemblies of constructional parts thereof · CPC title