Super-hydrophobic anti-pollution flashover coating with hydrophobicity migration, and preparation method thereof

Patent metadata

Field	Value
Publication number	US-12024643-B2
Application number	US-202117601708-A
Country	US
Kind code	B2
Filing date	Aug 6, 2021
Priority date	Jun 8, 2020
Publication date	Jul 2, 2024
Grant date	Jul 2, 2024

Abstract

The present invention provides a super-hydrophobic anti-pollution flashover coating with hydrophobicity transference, which is prepared from the following raw materials: a silicone resin, an organic solvent, silicon oxide, a flame retardant, a cross-linking agent, a coupling agent, a dispersing agent, a defoaming agent, a leveling agent, and a silicone resin curing agent. The present invention also provides a preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference. The anti-pollution flashover coating provided by the present invention has both super-hydrophobicity and hydrophobicity transference, which improves the hydrophobicity of a surface of an anti-pollution flashover coating layer, ensures the long-term effectiveness of an anti-pollution flashover coating layer, and prolongs a service life of an anti-pollution flashover coating layer, thereby solving the problem that existing anti-pollution flashover coatings have low hydrophobicity and are prone to contaminant accumulation on the surface and reducing the occurrence probability of pollution flashover accidents.

First claim

The invention claimed is:

1. A super-hydrophobic anti-pollution flashover coating with hydrophobicity transference, wherein the super-hydrophobic anti-pollution flashover coating is prepared by mixing a component A and a component B, and a mass ratio of the component A to the component B is (90-110):1;
wherein the component A is made of the following raw materials in parts by mass: 8 to 12 parts of a silicone resin, 70 to 80 parts of an organic solvent, 1 to 5 parts of silicon oxide, 5 to 10 parts of a flame retardant, 1 to 3 parts of a cross-linking agent, 1 to 5 parts of a coupling agent, 0.5 to 1.5 parts of a dispersing agent, 0.1 to 1 part of a defoaming agent, and 0.1 to 2 parts of a leveling agent; and
the component B is a silicone resin curing agent.

2. The super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , wherein the silicone resin is a polyorganosiloxane resin.

3. The super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , wherein the organic solvent is one or more selected from the group consisting of xylene, toluene, ethyl acetate, and butyl acetate.

4. The super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , wherein the flame retardant is one or more selected from the group consisting of aluminum hydroxide, magnesium hydroxide, attapulgite, an organic nitrogen-phosphorous based flame retardant, decabromodiphenyl ether, and diantimony trioxide.

5. The super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , wherein the cross-linking agent is a ketoxime cross-linking agent, and the ketoxime cross-linking agent is one or two selected from the group consisting of methyltris(methylethylketoximino)silane and methyltris(dimethylketoxime)silane.

6. The super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , wherein the coupling agent is a silane coupling agent.

7. A preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 1 , comprising the following steps:
1) preparation of an organic solvent A and an organic solvent B: weighing the organic solvent according to a formula, thoroughly stirring, and dividing a resulting solvent into two parts: an organic solvent A and an organic solvent B;
2) preparation of a particle dispersion: adding the silicon oxide and the flame retardant to the organic solvent A prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion by ultrasonic treatment, shearing, or stirring;
3) preparation of a film-forming material dispersion: adding the silicone resin to the organic solvent B prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion through shearing or stirring;
4) adding the particle dispersion prepared in step 2) to the film-forming material dispersion prepared in step 3), adding the cross-linking agent, the coupling agent, the dispersing agent, the defoaming agent, and the leveling agent, and thoroughly stirring a resulting mixture to obtain the component A; and
5) mixing the component A prepared in step 4) and the component B according to the formula and thoroughly stirring to obtain the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference.

8. A preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 2 , comprising the following steps:
1) preparation of an organic solvent A and an organic solvent B: weighing the organic solvent according to a formula, thoroughly stirring, and dividing a resulting solvent into two parts: an organic solvent A and an organic solvent B;
2) preparation of a particle dispersion: adding the silicon oxide and the flame retardant to the organic solvent A prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion by ultrasonic treatment, shearing, or stirring;
3) preparation of a film-forming material dispersion: adding the silicone resin to the organic solvent B prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion through shearing or stirring;
4) adding the particle dispersion prepared in step 2) to the film-forming material dispersion prepared in step 3), adding the cross-linking agent, the coupling agent, the dispersing agent, the defoaming agent, and the leveling agent, and thoroughly stirring a resulting mixture to obtain the component A; and
5) mixing the component A prepared in step 4) and the component B according to the formula and thoroughly stirring to obtain the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference.

9. A preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 3 , comprising the following steps:
1) preparation of an organic solvent A and an organic solvent B: weighing the organic solvent according to a formula, thoroughly stirring, and dividing a resulting solvent into two parts: an organic solvent A and an organic solvent B;
2) preparation of a particle dispersion: adding the silicon oxide and the flame retardant to the organic solvent A prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion by ultrasonic treatment, shearing, or stirring;
3) preparation of a film-forming material dispersion: adding the silicone resin to the organic solvent B prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion through shearing or stirring;
4) adding the particle dispersion prepared in step 2) to the film-forming material dispersion prepared in step 3), adding the cross-linking agent, the coupling agent, the dispersing agent, the defoaming agent, and the leveling agent, and thoroughly stirring a resulting mixture to obtain the component A; and
5) mixing the component A prepared in step 4) and the component B according to the formula and thoroughly stirring to obtain the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference.

10. A preparation method of the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference according to claim 4 , comprising the following steps:
1) preparation of an organic solvent A and an organic solvent B: weighing the organic solvent according to a formula, thoroughly stirring, and dividing a resulting solvent into two parts: an organic solvent A and an organic solvent B;
2) preparation of a particle dispersion: adding the silicon oxide and the flame retardant to the organic solvent A prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion by ultrasonic treatment, shearing, or stirring;
3) preparation of a film-forming material dispersion: adding the silicone resin to the organic solvent B prepared in step 1) according to the formula, and subjecting a resulting mixture to dispersion through shearing or stirring;
4) adding the particle dispersion prepared in step 2) to the film-forming material dispersion prepared in step 3), adding the cross-linking agent, the coupling agent, the dispersing agent, the defoaming agent, and the leveling agent, and thoroughly stirring a resulting mixture to obtain the component A; and
5) mixing the component A prepared in step 4) and the component B according to the formula and thoroughly stirring to obtain the super-hydrophobic anti-pollution flashover coating with hydrophobicity transference.

11.

Assignees

• State Grid Shandong Electric Power Res Institute
• State Grid Corp China

Inventors

• Li Wenjing
• Wang Xiaoming
• Li Xingeng
• Jiang Bo
• Yao Shuo
• Zhu Gengzeng
• Wu Yaping
• Zong Lijun
• Tian Shuang
• Yan Fengjie
• Fan Zhibin
• Zhang Zhenyue
• Wang Die
• Gao Zhiyue
• Mi Chunxu
• Wang Qian

Classifications

• C09D5/18

  Fireproof paints {including high temperature resistant paints} · CPC title

• C09D5/1687

  Use of special additives · CPC title

• C09D7/61

  inorganic · CPC title

• C08K5/5465

  containing at least one C=N bond · CPC title

• C08K3/22

  of metals · CPC title