Three-dimensionally ordered macroporous oxygen-deficient cerium dioxide catalyst, and preparation method and application thereof

Patent metadata

Field	Value
Publication number	US-12023650-B2
Application number	US-202017311352-A
Country	US
Kind code	B2
Filing date	Dec 4, 2020
Priority date	Oct 23, 2019
Publication date	Jul 2, 2024
Grant date	Jul 2, 2024

Abstract

The present application is related to a three-dimensionally ordered macroporous oxygen-deficient cerium dioxide catalyst, and a preparation method and an application thereof. The catalyst is prepared by using a polymethyl methacrylate (PMMA) colloidal crystal template method, calcining in a reducing/oxidizing atmosphere, and treating with water vapor, and the prepared catalyst shows an excellent activity and stability in photothermocatalytic purification of typical amospheric pollutants such as styrene, n-hexane, and cyclohexane. The method has the characteristics of cheap and easily available raw materials, simple preparation process, controllable oxygen vacancy, surface acid amount, and acid strength of the obtained material, and excellent photothermocatalytic performance.

First claim

What is claimed is:

1. A preparation method of a three-dimensionally ordered macroporous oxygen-deficient cerium dioxide catalyst, comprising following steps of:
S1: adding cerium nitrate hexahydrate and citric acid monohydrate powder into an alcohol solution to obtain an even transparent solution A after ultrasonic treatment;
S2: immersing polymethyl methacrylate microsphere powder in the solution A, carrying out ultrasonic homogenization, then removing excess liquid by suction filtration to obtain a solid B, and sequentially carrying out vacuum drying, calcination I, and calcination II on the solid B to obtain a solid C; and
S3: transferring the solid C obtained in the step S2 into a fixed bed reactor, and then carrying out calcination III, water vapor treatment, and calcination IV to obtain the three-dimensionally ordered macroporous oxygen-deficient cerium dioxide catalyst;
wherein the calcination III and the water vapor treatment in the step S3 are carried out at the same time, and comprise processes of: controlling a humidity in the reactor to be 10% to 90% by using a nitrogen bubbling device, and calcinating at 200° C. to 600° C. for 1 hour to 24 hours in a mixed gas atmosphere of hydrogen and nitrogen with a volume ratio of 1:0.1 to 1:10; and the calcination IV comprises a process of: introducing nitrogen for blowing for 1 hour at a temperature of the calcination III, and calcining at 200° C. to 600° C. for 1 hour to 24 hours in a mixed gas atmosphere of air and nitrogen with a volume ratio of 1:0.1 to 1:10.

2. The preparation method according to claim 1 , wherein the alcohol solution in the step S1 is a mixed solution of ethylene glycol and methyl alcohol, or ethyl alcohol, and a volume ratio of the ethylene glycol to the methyl alcohol in the mixed solution of ethylene glycol and methyl alcohol is 1:0.1 to 1:10; and a molar ratio of the cerium nitrate hexahydrate to citric acid monohydrate powder is 1:0.1 to 1:10.

3. The preparation method according to claim 1 , wherein a ratio of a total mass of the cerium nitrate hexahydrate and citric acid monohydrate to a volume of the alcohol solution in the step S1 is 0.9 g·mL −1 to 1.1 g·mL −1 .

4. The preparation method according to claim 1 , wherein a diameter of the polymethyl methacrylate microsphere in the step S2 is 50 nm to 500 nm; a mass volume ratio of the polymethyl methacrylate microsphere to the solution A is 0.25 g·mL −1 to 0.3 g·mL −1 ; the vacuum drying is carried out at 30° C. to 80° C. for 1 hour to 100 hours; the calcination I and the calcination II are carried out in a tubular furnace, wherein the calcination I comprises a process of: calcinating at 100° C. to 1,000° C. for 1 hour to 36 hours in an argon atmosphere, and the calcination II comprises a process of: calcinating at 300° C. to 1,000° C. for 1 hour to 36 hours in an air atmosphere.

Assignees

• Univ Guangdong Technology

Inventors

• An Taicheng
• Kong Jiejing
• Li Guiying

Classifications

• B01J35/657

  larger than 1000 nm · CPC title

• B01J35/39

  Photocatalytic properties · CPC title

• B01J37/343 Primary

  of ultrasonic wave energy · CPC title

• B01J37/0201

  Impregnation · CPC title

• B01J8/0285

  Heating or cooling the reactor (for tubular reactors in furnaces B01J8/062) · CPC title