Fire resistant adhesive compositions and methods of preparing and using the same

Patent metadata

Field	Value
Publication number	US-12018180-B2
Application number	US-202318108592-A
Country	US
Kind code	B2
Filing date	Feb 11, 2023
Priority date	Feb 11, 2022
Publication date	Jun 25, 2024
Grant date	Jun 25, 2024

Abstract

Described herein is a fire-resistant adhesive coating composition which emits water vapor when exposed to fire. Such compositions comprise an ionic polyacrylate dispersant, aluminum hydroxide, silicate, and an alkoxylated alcohol. In certain embodiments, the composition comprises a solids content of at least about 44.2%, based on the wet weight of the composition. Also described herein are methods for making and using of such coating compositions.

First claim

What is claimed is:

1. A fire-resistant adhesive coating composition comprising:
an ionic polyacrylate dispersant;
aluminum hydroxide present from about 20.0% to about 35.0%, based on the total dry weight of the composition;
potassium silicate present from about 65.0% to about 85.0%, based on the total dry weight of the composition; and
alkoxylated alcohol.

2. The fire-resistant adhesive coating composition of claim 1 , wherein the composition has a solids content from about 44.0% to about 85% based on the wet weight of the composition.

3. The fire-resistant adhesive coating composition of claim 1 , wherein the ionic polyacrylate dispersant comprises an alkali metal.

4. The fire-resistant adhesive coating composition of claim 3 , wherein the alkali metal is selected from sodium or potassium.

5. The fire-resistant adhesive coating composition of claim 1 , wherein the ionic polyacrylate dispersant is present from about 0.02% to about 0.2%, based on the dry weight of the composition.

6. The fire-resistant adhesive coating composition of claim 1 , wherein the silicate is present from about 70.0% to about 80.0%, based on the dry weight of the composition.

7. The fire-resistant adhesive coating composition of claim 1 , wherein the silicate has a pH from about 11.0 to about 12.5.

8. The fire-resistant adhesive coating composition of claim 1 , wherein the aluminum hydroxide is present from about 20.0% to about 30.0%, based on the dry weight of the composition.

9. The fire-resistant adhesive coating composition of claim 1 , wherein the aluminum hydroxide has an oil absorption from about 25 to about 45 ml/100 g.

10. The fire-resistant adhesive coating of claim 1 , wherein the alkoxylated alcohol is non-ionic.

11. The fire-resistant adhesive coating composition of claim 1 , wherein the alkoxylated alcohol comprises C 8 to C 10 alcohols.

12. The fire-resistant adhesive coating composition of claim 1 , wherein the alkoxylated alcohol has a pH from about 6.0 to about 8.0 and has an initial boiling point of about 200° C.

13. The fire-resistant adhesive coating composition of claim 1 , wherein the alkoxylated alcohol is present from about 0.7% to about 2.0%, based on the dry weight of the composition.

14. A building panel comprising the composition of claim 1 , wherein the panel is made of wood.

15. The fire-resistant adhesive coating composition of claim 1 , further comprising a rheology modifier present in an amount of up to about 15.0 wt. %, based on the dry weight of the composition.

16. The fire-resistant adhesive coating composition of claim 15 , wherein the rheology modifier comprises bentonite clay.

17. A method for producing a building panel comprising a fire-resistant adhesive coating composition, the fire-resistant adhesive coating composition comprising:
an aqueous liquid solvent;
an ionic polyacrylate dispersant;
aluminum hydroxide present from about 20.0% to about 35.0% based on the total dry weight of the composition;
potassium silicate present from about 65.0% to about 85.0%, based on the total dry weight of the composition; and
alkoxylated alcohol,
the method comprising:
i) coating a building panel with the fire-resistant adhesive coating composition; and
ii) drying the fire-resistant adhesive coating composition to evaporate the aqueous liquid solvent;
wherein the coating composition has a solids content of at least about 44.0%, based on the wet weight of the composition.

18. The method of claim 17 , wherein the ionic polyacrylate dispersant comprises an alkali metal, and wherein the alkali metal is selected from sodium or potassium.

Assignees

• Armstrong World Ind Inc
• Awi Licensing Llc

Inventors

• Hughes John E
• Zhang Linzhu
• Wang Michelle X

Classifications

• C09J11/06

  organic · CPC title

• C09J11/08

  Macromolecular additives · CPC title

• C09J2400/306

  in the pretreated surface to be joined · CPC title

• C09J1/02 Primary

  containing water-soluble alkali silicates · CPC title