Multi-stage polymeric latexes, coating compositions containing such latexes, and articles coated therewith

Patent metadata

Field	Value
Publication number	US-12006380-B2
Application number	US-202217882330-A
Country	US
Kind code	B2
Filing date	Aug 5, 2022
Priority date	Sep 1, 2017
Publication date	Jun 11, 2024
Grant date	Jun 11, 2024

Abstract

An aqueous coating composition useful in coating a variety of substrates, including interior or exterior portions of food or beverage cans. The coating composition includes a multi-stage polymeric latex having two or more emulsion polymerized stages in an aqueous carrier liquid, wherein the latex has one or both of:
(i) a lower glass transition temperature (Tg) emulsion polymerized stage having a calculated Tg that is at least 20° C. lower than a calculated Tg of a higher Tg emulsion polymerized stage, or (ii) a gradient Tg with at least a 20° C. differential in the calculated Tg of monomers fed at the start of polymerization compared to monomers fed at the end of polymerization.

When spray-applied on the interior of a food or beverage can, the composition exhibits a global extraction result of less than 50 ppm and a metal exposure value of less than 3 mA.

First claim

The invention claimed is:

1. An aqueous interior spray beverage container coating composition comprising:
an aqueous carrier liquid; and
a multi-stage polymeric latex having two or more emulsion polymerized ethylenically unsaturated monomer stages, wherein:
the latex has a lower Tg emulsion polymerized stage having a calculated Tg that is at least 20° C. lower than a calculated Tg of a higher Tg emulsion polymerized stage, and
more than 50 weight percent of the emulsion polymerized stages have a calculated Tg of greater than 40° C. and the lower Tg emulsion polymerized stage has a calculated Tg of less than 40° C.;

wherein the aqueous coating composition has a viscosity of from 20 to 80 seconds (Ford Cup #2, 25° C.); and
wherein the coating composition, when spray applied onto an interior of a 355 mL no. 211 two-piece drawn and ironed aluminum beverage can at 115 milligrams per can coating weight and cured at 188° C. to 199° C. (measured at the can dome) for 55 seconds, has a dry film thickness less than about 0.53 mils and exhibits:
(i) a global extraction result of less than 50 ppm,
(ii) a metal exposure of less than 3 mA on average when the can is filled with 1% NaCl in deionized water and tested pursuant to the Initial Metal Exposure test method disclosed herein, and
(iii) a metal exposure of less than 3.5 mA when tested pursuant to the Metal Exposure after Drop Damage test disclosed herein.

2. The coating composition of claim 1 , wherein the latex has a lower Tg emulsion polymerized stage having a calculated Tg of less than 30° C. and a higher Tg emulsion polymerized stage having a calculated Tg of greater than 50° C.

3. The coating composition of claim 1 , wherein the latex has a lower Tg emulsion polymerized stage having a calculated Tg of less than 20° C. and a higher Tg emulsion polymerized stage having a calculated Tg of greater than 60° C.

4. The coating composition of claim 1 , wherein the latex has a lower Tg emulsion polymerized stage having a calculated Tg that is at least 40° C. lower than a calculated Tg of the higher Tg emulsion polymerized stage.

5. The coating composition of claim 1 , wherein the latex has a lower Tg emulsion polymerized stage having a calculated Tg that is at least 60° C. lower than a calculated Tg of the higher Tg emulsion polymerized stage.

6. The coating composition of claim 1 , wherein more than 50 weight percent of the emulsion polymerized stages have a calculated Tg of at least 60° C.

7. The coating composition of claim 1 , wherein two or more of the emulsion polymerized stages are formed from monomers having in the aggregate a calculated Tg of at least 30° C.

8. The coating composition of claim 1 , wherein the aqueous coating composition includes, based on total resin solids, at least 50 wt. % of the two or more emulsion polymerized stages.

9. The coating composition of claim 1 , wherein the aqueous coating composition contains more than 70 wt. % resin solids from polymerized ethylenically unsaturated monomers based on total resin solids in the coating composition.

10. The coating composition of claim 1 , wherein at least 50 wt. % of the monomers used to form one or more of the emulsion polymerized stages are (meth)acrylates.

11. The coating composition of claim 1 , wherein at least 50 wt. % of the monomers used to form one or more of the emulsion polymerized stages are alkyl methacrylates.

12. The coating composition of claim 1 , wherein at least one of the emulsion polymerized stages is formed from monomers including at least 80 wt. % of one or more of methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, and butyl methacrylate.

13. The coating composition of claim 12 , wherein the coating composition is substantially free of styrene and substituted styrene compounds.

14. The coating composition of claim 12 , wherein the coating composition does not contain any structural units derived from a bisphenol.

15. The coating composition of claim 1 , wherein at least one of the emulsion polymerized stages is formed from monomers including a multi-ethylenically unsaturated monomer.

16. The coating composition of claim 1 , wherein the coating composition is substantially free of each of bisphenol A, bisphenol F, and bisphenol S, the coating composition is not prepared using halogenated monomers, and the coating composition includes or is derived from no more than 0.5 wt. % of acrylamide-type monomers, if any, based on the aggregate weight of polymerizable monomers employed to make the latex.

17. The coating composition of claim 1 , wherein the coating composition includes or is derived from no more than 5 wt. % polyether compounds or polymers based on the total coating composition solids.

18. The coating composition of claim 1 , wherein one or more polymerizable surfactants are used in forming the multi-stage polymeric latex.

19. The coating composition of claim 1 , wherein the aqueous coating composition further comprises a phenoplast crosslinker.

20. The coating composition of claim 1 , wherein the coating composition, when spray applied onto an interior of a 355 mL no. 211 two-piece drawn and ironed aluminum beverage can at 115 milligrams per can coating weight and cured at 188° C. to 199° C. (measured at the can dome) for 55 seconds, exhibits a lower sidewall adhesion rating value of 9 or 10 after retort in 2% citric acid under pressure at 121° C. and tested according to ASTM D 3359—Test Method B.

21. The coating composition of claim 1 , wherein the coating composition, when spray applied onto an interior of a 355 mL no. 211 two-piece drawn and ironed aluminum beverage can at 115 milligrams per can coating weight and cured at 188° C. to 199° C. (measured at the can dome) for 55 seconds, is capable of passing a necking and flanging test as indicated by a change of metal exposure after necking of less than 1.0 mA.

22. The coating composition of claim 1 , wherein the lower Tg emulsion polymerized stage was emulsion polymerized before the higher Tg emulsion polymerized stage.

23. The coating composition of claim 1 , wherein the weight ratio of the lower Tg emulsion polymerized stage relative to the higher Tg emulsion polymerized stage ranges from 25:75 to 48:52.

24. The coating composition of claim 1 , wherein the aqueous carrier liquid contains greater than about 5% organic solvent based on the total weight of the aqueous carrier liquid.

25. An aqueous interior spray beverage can coating composition comprising:
an aqueous carrier liquid; and
a multi-stage polymeric latex having two or more emulsion polymerized ethylenically unsaturated monomer stages, wherein:
the latex has a lower Tg emulsion polymerized stage having a calculated Tg that is at least 20° C. lower than a calculated Tg of a higher Tg emulsion polymerized stage, and
more than 50 weight percent of the emulsion polymerized stages have a calculated Tg of greater than 40° C. and the lower Tg emulsion polymerized stage has a calculated Tg of less than 40° C.;

wherein the aqueous coating composition comprises a beta-hydroxyalkyl-amide crosslinker; has a viscosity of from 20 to 80 seconds (Ford Cup #2, 25° C.); and
wherein the coating composition, when spray applied onto an interior of a 355 mL no. 211 two-piece drawn and ironed aluminum beverage can at 115 milligrams per can coating weight and cured at 188° C. to 199° C. (measured at the can dome) for 55 seconds, exhibits:
(i) a global extract

Assignees

• Swimc Llc

Inventors

• O'Brien Robert M
• Stuetelberg Mark
• Desousa Joseph D
• Scandolari Mary Jo
• Koch Nikolaus
• Pollin Stephen
• Hussain Nusrah

Classifications

• C09D133/26

  Homopolymers or copolymers of acrylamide or methacrylamide · CPC title

• C09D133/12

  Homopolymers or copolymers of methyl methacrylate · CPC title

• C09D5/024

  characterised by the additives · CPC title

• B65D25/14

  Linings or internal coatings (of containers made by folding or erecting blanks made of paper B65D5/56 {; linings for domestic water storage heaters F24H1/183}) · CPC title

• C09D7/40

  Additives · CPC title