Electrode for electrochemical device comprising dry electrode film and method for manufacturing the same

Patent metadata

Field	Value
Publication number	US-12002962-B2
Application number	US-202217881879-A
Country	US
Kind code	B2
Filing date	Aug 5, 2022
Priority date	Aug 6, 2021
Publication date	Jun 4, 2024
Grant date	Jun 4, 2024

Abstract

Disclosed is a method for manufacturing a dry electrode. The method allows determination of the micro-fibrilization degree of a binder resin from the crystallinity of the binder resin. Based on this, the processing conditions of mixed powder for electrode or an electrode film may be controlled. In this manner, it is possible to check and control the processing conditions easily and efficiently. In addition, the method for manufacturing a dry electrode includes a kneading step using a kneader under a low speed and high temperature and pulverization step. Therefore, there is no problem of blocking of a flow path caused by aggregation of the ingredients, which is favorable to mass production.

First claim

What is claimed is:

1. An electrode for an electrochemical device, comprising:
a dry free-standing electrode film obtained by a dry manufacturing process using no solvent, wherein the dry electrode film comprises an electrode active material, a conductive material, and a binder resin,
wherein the binder resin contained in the dry electrode film has a crystallinity of 10% or less,
wherein the dry electrode film has a tensile strength of 0.5 MPa or more and 10 MPa or less in the machine direction (MD).

2. The electrode for an electrochemical device according to claim 1 , wherein the dry electrode film has a tensile elongation of 2% or more and 30% or less.

3. The electrode for an electrochemical device according to claim 1 , wherein the dry electrode film has a porosity of 20-50 vol %.

4. A method for manufacturing an electrode for an electrochemical device, the method comprising:
(a) preparing a powdery blend comprising an electrode active material, a conductive material and a binder resin;
(b) kneading the powdery mixture at 70-200° C. to prepare mixture lumps;
(c) pulverizing the mixture lumps to obtain mixed powder for electrode; and
(d) calendering the mixed powder for electrode to obtain a free-standing-type dry electrode film, wherein the binder resin contained in the dry electrode film obtained from the calendering (d) has a crystallinity (d) of 10% or less,
wherein the method is a dry manufacturing process using no solvent.

5. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the binder resin contained in the mixed powder for electrode obtained from the pulverizing (c) has a crystallinity (c) of 20% or less.

6. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the binder resin contained in the mixture obtained from preparing the powdery blend (a) has a crystallinity (a) of 50% or less.

7. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the preparing the powdery blend (a) is carried out at 500-30,000 rpm.

8. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the kneading (b) is carried out under a rotation speed of 100 rpm or less.

9. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the kneading (b) is carried out under a pressure of 0.5 kgf/cm 2 to 10 kgf/cm 2 .

10. The method for manufacturing the electrode for an electrochemical device according to claim 4 , wherein the kneading (b) is carried out under a pressure of an atmospheric pressure or more.

11. The electrode for an electrochemical device according to claim 1 , wherein the binder resin comprises polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polyolefin, or a mixture of two or more of them.

12. The electrode for an electrochemical device according to claim 1 , which further comprises a current collector, wherein the dry electrode film is disposed on at least one surface or both surfaces of the current collector.

13. The method for manufacturing the electrode for an electrochemical device according to claim 4 , which further comprises preparing a current collector, disposing the dry electrode film on at least one surface of the current collector and carrying out lamination.

14. A secondary battery comprising the dry electrode as defined in claim 1 , wherein the dry electrode is a positive electrode, and an electrode assembly comprising the positive electrode, a negative electrode and a separator is received in a battery casing together with a lithium-containing non-aqueous electrolyte.

Assignees

• Lg Energy Solution Ltd

Inventors

• Kang Seong-Wook
• Han Jae-Sung
• Shin Dong-Mok
• Shin Dong-Oh
• Yoon Kyung-Hwan
• Yoo Kwang-Ho

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M2004/028

  Positive electrodes · CPC title

• H01G11/86

  specially adapted for electrodes (carbonisation or activation of carbon for the manufacture of electrodes H01G11/34) · CPC title

• H01M10/052

  Li-accumulators · CPC title