Build material composition with metal powder and freeze-dried heteropolymer

Patent metadata

Field	Value
Publication number	US-11998977-B2
Application number	US-201816499484-A
Country	US
Kind code	B2
Filing date	Mar 15, 2018
Priority date	Mar 15, 2018
Publication date	Jun 4, 2024
Grant date	Jun 4, 2024

Abstract

An example of a composition includes a host metal present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition. A flow additive is also present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition. The flow additive consists of an organic material that is pyrolyzable at a pyrolysis temperature that is less than a sintering temperature of the host metal. The composition is spreadable, having a Hausner Ratio less than 1.25.

First claim

What is claimed is:

1. A build material composition, comprising:
a host metal powder present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the composition, the host metal powder including host metal particles having an average particle size of less than 20 micrometers and the host metal powder having a sintering temperature of from about 500° C. to about 1800° C.; and
a flow additive present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the composition, wherein the flow additive consists of particles of a freeze-dried organic material that is pyrolyzable at a pyrolysis temperature that is less than the sintering temperature of the host metal powder,
wherein the particles of the freeze-dried organic material include a heteropolymer having a hydrophobic component that makes up from about 65% by weight to about 99.9% by weight of the heteropolymer and a hydrophilic component that makes up from about 0.1% by weight to about 35% by weight of the heteropolymer with the hydrophobic component having a lower glass transition temperature compared to the hydrophilic component, wherein:
the hydrophobic component is formed from a monomer selected from the group consisting of ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, hydroxyethyl acrylate, octadecyl methacrylate, tetrahydrofurfuryl acrylate, alkoxylated tetrahydrofurfuryl acrylate, 2-phenoxyethyl methacrylate, benzyl acrylate, ethoxylated nonyl phenol methacrylate, cyclohexyl methacrylate, trimethyl cyclohexyl methacrylate, t-butyl methacrylate, n-octyl methacrylate, tridecyl methacrylate, isodecyl acrylate, dimethyl maleate, dioctyl maleate, acetoacetoxyethyl methacrylate, diacetone acrylamide, vinyl chloride, vinylidene chloride, N-vinyl imidazole, N-vinylcarbazole, N-vinyl-caprolactam, and combinations thereof; and
the hydrophilic component is formed from an acidic monomer selected from the group consisting of ethacrylic acid, dimethylacrylic acid, maleic anhydride, maleic acid, vinylsulfonate, cyanoacrylic acid, vinylacetic acid, allylacetic acid, ethylidineacetic acid, propylidineacetic acid, crotonoic acid, fumaric acid, itaconic acid, sorbic acid, angelic acid, cinnamic acid, styrylacrylic acid, citraconic acid, glutaconic acid, aconitic acid, phenylacrylic acid, acryloxypropionic acid, aconitic acid, phenylacrylic acid, acryloxypropionic acid, vinylbenzoic acid, N-vinylsuccinamidic acid, mesaconic acid, methacroylalanine, acryloylhydroxyglycine, sulfoethyl methacrylic acid, sulfopropyl acrylic acid, styrene sulfonic acid, sulfoethylacrylic acid, 2-methacryloyloxymethane-1-sulfonic acid, 3-methacryoyloxypropane-1-sulfonic acid, 3-(vinyloxy)propane-1-sulfonic acid, ethylenesulfonic acid, vinyl sulfuric acid, 4-vinylphenyl sulfuric acid, ethylene phosphonic acid, vinyl phosphoric acid, vinyl benzoic acid, 2 acrylamido-2-methyl-1-propanesulfonic acid, and combinations thereof, and wherein the composition is spreadable, having a Hausner Ratio less than 1.25.

2. The build material composition as defined in claim 1 wherein the particles of the flow additive include primary particles having an average flow additive primary particle size ranging from about 1 to about 3 orders of magnitude smaller than the average particle size of the host metal particles.

3. The build material composition as defined in claim 2 wherein the average flow additive primary particle size ranges from about 5 nanometers to about 200 nanometers.

4. The build material composition as defined in claim 1 wherein the flow additive is a polymer having a glass transition temperature greater than about 5 degrees above a spread temperature of the composition, and wherein the spread temperature of the composition is from about 25° C. to about 200° C.

5. The build material composition as defined in claim 1 wherein the flow additive is hydrophobic.

6. The build material composition as defined in claim 1 wherein when the flow additive undergoes pyrolysis, the pyrolysis yields volatile decomposition products and non-volatile carbon-rich residue with the volatile decomposition products being at least about 90 percent of a pre-pyrolyzed weight of the flow additive.

7. The build material composition as defined in claim 1 wherein the particles of the freeze-dried organic material are a nano-powder produced by freeze drying an aqueous dispersion of polymer nano-particles.

8. The build material composition as defined in claim 7 wherein the aqueous dispersion of polymer nano-particles is produced by emulsion polymerization or co-polymerization of the monomer of the hydrophobic component and the acidic monomer of the hydrophilic component.

9. The build material composition as defined in claim 1 wherein the average particle size of the host metal particles is from about 11 micrometers to about 20 micrometers.

10. The build material composition as defined in claim 1 wherein the host metal particles are stainless steel particles and the average particle size is about 11 micrometers.

11. The build material composition as defined in claim 1 wherein the flow additive is not an adhesive.

12. The build material composition as defined in claim 1 wherein the hydrophobic component makes up about 65% by weight and the hydrophilic component makes up about 35% by weight of the heteropolymer of the freeze-dried organic material.

13. The build material composition as defined in claim 1 wherein the monomer of the hydrophobic component is selected from the group consisting of ethyl acrylate, propyl acrylate, propyl methacrylate, hydroxyethyl acrylate, tetrahydrofurfuryl acrylate, alkoxylated tetrahydrofurfuryl acrylate, 2-phenoxyethyl methacrylate, benzyl acrylate, ethoxylated nonyl phenol methacrylate, trimethyl cyclohexyl methacrylate, n-octyl methacrylate, tridecyl methacrylate, isodecyl acrylate, dimethyl maleate, dioctylvinyl imidazole, maleate, acetoacetoxyethyl methacrylate, diacetone acrylamide, vinylidene chloride, N-N-vinylcarbazole, N-vinyl-caprolactam, and combinations thereof.

14. A three-dimensional (3D) printing kit, comprising:
a build material composition, including:
a host metal powder present in an amount ranging from about 95.00 weight percent to about 99.99 weight percent, based on a total weight of the build material composition, the host metal powder including host metal particles having an average particle size of less than 20 micrometers and the host metal powder having a sintering temperature of from about 500° C. to about 1800° C.; and
a flow additive present in an amount ranging from about 0.01 weight percent to about 5.00 weight percent, based on the total weight of the build material composition, wherein the flow additive consists of particles of a freeze-dried organic material that is pyrolyzable at a pyrolysis temperature less than the sintering temperature of the host metal powder, and wherein the particles of the freeze-dried organic material include a heteropolymer having a hydrophobic component that makes up from about 65% by weight to about 99.9% by weight of the heteropolymer and a hydrophilic component that makes up from about 0.1 by weight to about 35% by weight of the heteropolymer with the hydrophobic component having a lower glass transition temperature compared to the hydrophilic component, wherein:
the hydrophobic component is formed from a monomer selected from the group consisting of ethyl acrylate, ethyl methacrylate, propyl acrylate, propyl methacrylate, hydroxyethyl acrylate, octadecyl methacrylate, tetrahydrofurfuryl acrylate, alkoxylated tetrahydrofurfuryl

Assignees

• Hewlett Packard Development Co

Inventors

• Kasperchik Vladek
• Mckinnell James
• Shaarawi Mohammed S
• Monroe Michael G
• Hower Jason

Classifications

• B22F10/10

  Formation of a green body · CPC title

• B22F1/10 Primary

  Metallic powder containing lubricating or binding agents; Metallic powder containing organic material · CPC title

• B22F1/05

  Metallic powder characterised by the size or surface area of the particles · CPC title

• B22F1/102

  Metallic powder coated with organic material · CPC title

• B22F1/16

  Metallic particles coated with a non-metal (coated with lubricating or binding agents or with organic material B22F1/10) · CPC title