Sealing material sheet for solar-cell module, solar-cell module using the same, and method for manufacturing solar-cell module

Patent metadata

Field	Value
Publication number	US-11973155-B2
Application number	US-202217866692-A
Country	US
Kind code	B2
Filing date	Jul 18, 2022
Priority date	Apr 11, 2019
Publication date	Apr 30, 2024
Grant date	Apr 30, 2024

Abstract

To provide a sealing material sheet for a solar-cell module that has high productivity, and can also suppress unevenness in thickness at the time of integration as a solar-cell module. There is provided a sealing material sheet 1 in which there are two inflection point temperatures that are temperatures only around which a change rate of the linear expansion coefficient locally increases, a first inflection point temperature at a low temperature side of two inflection point temperatures is within a range of 55° C. to 70° C., and a second inflection point at a high temperature side of the inflection point temperatures is within a range of 80° C. to 95° C.

First claim

What is claimed is:

1. A sealing material sheet for a solar-cell module, the sealing material sheet comprising:
a core layer containing a polyethylene-based resin; and
a skin layer formed as a top-most surface of the sealing material sheet, and containing a polyethylene-based resin and a silage-modified polyethylene-based resin,
wherein:
a density of the core layer is greater than a density of the skin layer,
a graph representing a linear expansion coefficient of the sealing material sheet as a function of a resin temperature as measured according to JIS K 7197 includes two inflection point temperatures at which a change rate of the linear expansion coefficient increases:
a first inflection point temperature within a range of 55° C. to 70° C., and
a second inflection point temperature within a range of 80° C. to 95° C.,

the change rate of the linear expansion coefficient from the first inflection point temperature to a temperature +3° C. the first inflection point temperature is larger than the change rate of the linear expansion coefficient from a temperature −3° C. the first inflection point temperature to the first inflection point temperature,
the change rate of the linear expansion coefficient from the second inflection point temperature to a temperature +3° C. the second inflection point temperature is larger than the change rate of the linear expansion coefficient from a temperature −3° C. the second inflection point temperature to the second inflection point temperature.

2. The sealing material sheet according to claim 1 , wherein:
the change rate of the linear expansion coefficient from the first inflection point temperature to the temperature +3° C. the first inflection point temperature is at least 1.2 times the change rate of the linear expansion coefficient from the temperature −3° C. the first inflection point temperature to the first inflection point temperature, and
the change rate of the linear expansion coefficient from the second inflection point temperature to the temperature +3° C. the second inflection point temperature is at least 1.2 times the change rate of the linear expansion coefficient from the temperature −3° C. the second inflection point temperature to the second inflection point temperature.

3. The sealing material sheet according to claim 1 , wherein:
the change rate of the linear expansion coefficient from the first inflection point temperature to the temperature +3° C. the first inflection point temperature is at least 1.35 times the change rate of the linear expansion coefficient from the temperature −3° C. the first inflection point temperature to the first inflection point temperature, and
the change rate of the linear expansion coefficient from the second inflection point temperature to the temperature +3° C. the second inflection point temperature is at least 1.35 times the change rate of the linear expansion coefficient from the temperature −3° C. the second inflection point temperature to the second inflection point temperature.

4. The sealing material sheet according to claim 1 , wherein:
a thickness of the core layer is at least 200 μm and no more than 400 μm, and
a thickness of the skin layer is at least 30 μm and no more than 100 μm.

5. A solar-cell module comprising, in order:
a transparent front substrate;
a solar cell element;
the sealing material sheet according to claim 1 ; and
a rear-surface protecting substrate.

6. The solar-cell module according to claim 5 , further comprising:
a lead wire disposed between the solar cell element and the sealing material sheet,
wherein a thickness of the lead wire is no more than 90% relative to a thickness of the sealing material sheet.

7. A method for manufacturing a solar-cell module by a vacuum heating lamination method, the method comprising:
laminating module constituent members including the sealing material sheet according to claim 1 by vacuum aspiration;
after the vacuum aspiration, setting a resin temperature of the sealing material sheet to equal to or higher than the first inflection point temperature, and then subjecting the laminated module constituent members to thermocompression at the second inflection point temperature or higher.

8. A sealing material sheet for a solar-cell module, the sealing material sheet comprising:
a core layer containing a polyethylene-based resin; and
a skin layer containing a polyethylene-based resin and a silane-modified polyethylene-based resin,
wherein a whole resin component of the sealing material sheet contains:
a low melting point resin component having a melting point of at least 60° C. and less than 70° C., in an amount of at least 25% by mass and no more than 70% by mass of the whole resin component,
a high melting point resin component having a melting point of at least 95° C. and no higher than 110′C in an amount of at least 25% by mass and no more than 70% by mass of the whole resin component, and
an intermediate melting point resin component having a melting point that is at least 20° C. higher than the melting point of the low melting point resin component and at least 10° C. lower than the melting point of the high melting point resin component, in an amount of at least 5% by mass and no more than 15% by mass of the whole resin component.

9. The sealing material sheet according to claim 8 , wherein:
a thickness of the core layer is at least 200 μm and no more than 400 μm, and
a thickness of the skin layer is at least 30 μm and no more than 100 μm.

10. A solar-cell module comprising, in order:
a transparent front substrate;
a solar cell element;
the sealing material sheet according to claim 8 ; and
a rear-surface protecting substrate.

11. The solar-cell module according to claim 10 , further comprising:
a lead wire disposed between the solar cell element and the sealing material sheet,
wherein a thickness of the lead wire is no more than 90% relative to a thickness of the sealing material sheet.

12. A method for manufacturing a solar-cell module by a vacuum heating lamination method, the method comprising:
laminating module constituent members including the sealing material sheet according to claim 8 by vacuum aspiration;
after the vacuum aspiration, setting a resin temperature of the sealing material sheet to equal to or higher than the first inflection point temperature, and then subjecting the laminated module constituent members to thermocompression at the second inflection point temperature or higher.

Assignees

• Dainippon Printing Co Ltd

Inventors

• Saeki Kosuke
• Yoneda Shinya
• Tanaka Jun
• Tamaki Hiroaki
• Nagino Shinsuke
• Obonai Naohiro

Classifications

• H10F71/00

  Manufacture or treatment of devices covered by this subclass (patterning processes to connect thin photovoltaic cells in integrated devices, or assemblies of multiple devices, having photovoltaic cells H10F19/33; manufacture or treatment of encapsulations or containers for integrated devices, or assemblies of multiple devices, having photovoltaic cells H10F19/80; manufacture or treatment of integrated devices, or assemblies of multiple devices, comprising at least one element in which radiation controls the flow of current H10F39/00) · CPC title

• H10F19/804 Primary

  Materials of encapsulations · CPC title

• H10F19/85

  Protective back sheets · CPC title

• H01L31/0481 Primary

  Electricity · mapped topic

• B32B7/022

  Mechanical properties · CPC title