Electric steel strip or sheet for higher frequency electric motor applications, with improved polarization and low magnetic losses

Patent metadata

Field	Value
Publication number	US-11970757-B2
Application number	US-201917292114-A
Country	US
Kind code	B2
Filing date	Nov 7, 2019
Priority date	Nov 8, 2018
Publication date	Apr 30, 2024
Grant date	Apr 30, 2024

Abstract

A non-oriented electrical steel strip or sheet having the following composition, in percent by weight: 3.2 to 3.4 of Si, 0.85 to 1.1 of Al, 0.07 to 0.18 of Mn, 0.01 to 0.04 of P, 0.0003 to 0.0030 of S, 0.0005 to 0.0020 of N, 0.0010 to 0.0050 of C, 0.0015 to 0.0040 of Ti, 0.01 to 0.008 of Cr, up to 0.05 in total of Nb+Mo+V, balance Fe and unavoidable impurities up to a total amount of 1.0% and having a specific electrical resistance at 50° C. of 0.62 to 0.65μΩm. Also, a process for the production thereof and the use thereof in iron cores of rotating electric machines, in particular in electric motors, for example in electric vehicles or hybrid vehicles, and generators.

First claim

The invention claimed is:

1. A non-oriented electrical steel strip or sheet comprising, in % by weight:
3.20 to 3.40 of Si,
0.85 to 1.10 of Al,
0.07 to 0.18 of Mn,
0.01 to 0.04 of P,
0.0003 to 0.0030 of S,
0.0005 to 0.0025 of N,
0.0010 to 0.0050 of C,
0.0015 to 0.0040 of Ti,
0.01 to 0.08 of Cr, up to 0.05 in total of Nb+Mo+V,
balance Fe and unavoidable impurities below 1% by weight,
wherein the steel strip or sheet in a cold rolled and annealed condition with a thickness of 0.255-0.310 mm has a specific electrical resistance at 50° C. of 0.62 to 0.65 μΩm and loss values of not more than 14.2 W/kg at a polarization of 1.0 T and 400 Hz at a sheet thickness of 0.280 to 0.31 mm and not more than 13.6 W/kg at a polarization of 1.0 T and 400 Hz at a sheet thickness of 0.255 to 0.280 mm.

2. The non-oriented electrical steel strip or sheet according to claim 1 , wherein a ratio multiplied by 100 of the polarization at 50 Hz and 100 A/m and the magnetic loss at 1 T and 400 Hz is at least 6.8.

3. The non-oriented electrical steel strip or sheet according to claim 1 , wherein a ratio multiplied by 100 of the polarization at 400 Hz and 100 A/m and the magnetic loss at 1 T and 400 Hz is at least 6.0.

4. The non-oriented electrical steel strip or sheet according to claim 1 , wherein a sum of C, S, N and Ti is not more than 0.0090% by weight.

5. The non-oriented electrical steel strip or sheet according to claim 1 , wherein a heat treatment step at a maximum temperature of 1050 to 1070° C. is carried out during the production of the steel strip or sheet.

6. The non-oriented electrical steel strip or sheet according to claim 1 , wherein a polarization at a modulation of 2500 A/m is at least 1.53 T, at 5000 A/m is at least 1.63 and/or at 10 000 A/m is at least 1.75 T, in each case, at a sheet thickness of 0.280 to 0.31 mm, and a polarization at a modulation of 2500 A/m of at least 1.52 T, at 5000 A/m of at least 1.62 and/or at 10 000 A/m of at least 1.75, in each case, at a sheet thickness of 0.255 to 0.280 mm.

7. A process for producing a non-oriented electrical steel strip or sheet according to claim 1 , comprising at least the following process steps:
(A) providing a hot-rolled, hot strip annealed non-oriented electrical steel strip or sheet in a thickness of 1.5 to 2.5 mm,
(B) cold rolling the electrical steel strip or sheet from step (A) to a thickness of 0.255 to 0.31 mm in order to obtain a cold-rolled strip,
(C) final heat treating the cold-rolled strip from step (B) in order to obtain the non-oriented electrical steel strip or sheet, and
(D)cooling the finally heat-treated cold-rolled strip from step (C) at a usual average cooling rate of from 1 K/s to 10 K/s in a nonoxidizing atmosphere to a lower limiting temperature of 500° C.,
wherein the cold-rolled strip from step (B) is, in step (C), firstly heated at a heating rate of at least 40 K/s to a temperature of 860 to 940° C. and subsequently heated at a heating rate of from 3 to 20 K/s to a temperature of 1050 to 1070° C.

8. The process according to claim 7 , wherein step (C) is carried out at strip tensions of not more than 10 N/mm 2 .

9. The process according to claim 7 , wherein step (C) is carried out in a heat treatment atmosphere containing at least 70% by volume of hydrogen.

10. The process according to claim 7 , wherein step (C) is carried out at a dew point of not more than −10° C.

11. The process according to claim 7 , wherein a hot-rolled, hot strip annealed, non-oriented electrical steel strip or sheet is provided for step (B) in a thickness of from 1.5 to 2.5 mm.

12. The process according to claim 7 , wherein the hot-rolled, hot strip annealed non-oriented electrical steel strip or sheet is produced via continuous casting or thin-slab casting.

13. The process according to claim 7 , wherein the cold-rolled strip from step (B) is, in step (C), firstly heated at a heating rate of at least 40 K/s to a temperature of 880 to 920° C.

14. A component for electrical applications comprising a non-oriented electrical steel strip or sheet according to claim 1 .

15. The component of claim 14 , wherein the component is an iron core of a rotating electrical machine.

16. The component of claim 15 , wherein the electrical machine is an electric motor or a generator.

17. An iron core of a rotating electric machine comprising a non-oriented electrical steel strip or sheet according to claim 1 .

18. The iron core of claim 17 , wherein the rotating electric machine is an electric motor or a generator.

19. A non-oriented electrical steel strip or sheet comprising, in % by weight:
3.20 to 3.40 of Si,
0.85 to 1.10 of Al,
0.07 to 0.18 of Mn,
0.01 to 0.04 of P,
0.0003 to 0.0030 of S,
0.0005 to 0.0025 of N,
0.0010 to 0.0050 of C,
0.0015 to 0.0040 of Ti,
0.01 to 0.08 of Cr, up to 0.05 in total of Nb+Mo+V,
balance Fe and unavoidable impurities below 1% by weight,
wherein the steel strip or sheet in a cold rolled and annealed condition with a thickness of 0.255-0.310 mm has a specific electrical resistance at 50° C. of 0.62 to 0.65 μΩm and has loss values of not more than 2.3 W/kg at a polarization of 1.5 T and 50 Hz, not more than 14.2 W/kg at a polarization of 1.0 T and 400 Hz, not more than 33 W/kg at a polarization of 1.0 T and 700 Hz, not more than 58 W/kg at a polarization of 1.0 T and 1000 Hz, in each case, at a sheet thickness of 0.280 to 0.31 mm, and the steel strip or sheet has loss values of not more than 2.2 W/kg at a polarization of 1.5 T and 50 Hz, not more than 13.6 W/kg at a polarization of 1.0 T and 400 Hz, not more than 32 W/kg at a polarization of 1.0 T and 700 Hz, not more than 55 W/kg at a polarization of 1.0 T and 1000 Hz, in each case, at a sheet thickness of 0.255 to 0.280 mm.

20. A non-oriented electrical steel strip or sheet comprising, in % by weight:
3.20 to 3.40 of Si,
0.85 to 1.10 of Al,
0.07 to 0.18 of Mn,
0.01 to 0.04 of P,
0.0003 to 0.0030 of S,
0.0005 to 0.0025 of N,
0.0010 to 0.0050 of C,
0.0015 to 0.0040 of Ti,
0.01 to 0.08 of Cr, up to 0.05 in total of Nb+Mo+V,
balance Fe and unavoidable impurities below 1% by weight,
wherein the steel strip or sheet in a cold rolled and annealed condition with a thickness of 0.255-0.310 mm has a specific electrical resistance at 50° C. of 0.62 to 0.65 μΩm, and
wherein a polarization at a modulation of 2500 A/m is at least 1.53 T, at 5000 A/m is at least 1.63 and/or at 10 000 A/m is at least 1.75 T, in each case, at a sheet thickness of 0.280 to 0.31 mm, and a polarization at a modulation of 2500 A/m of at least 1.52 T, at 5000 A/m of at least 1.62 and/or at 10 000 A/m of at least 1.75, in each case, at a sheet thickness of 0.255 to 0.280 mm.

Assignees

• Thyssenkrupp Steel Europe Ag
• Thyssenkrupp Ag

Inventors

• Vidovic Anton
• Telger Karl
• Fischer Olaf
• Winkler Nina Maria

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C22C38/26 Primary

  with niobium or tantalum · CPC title

• C21D8/0205

  Chemistry & Metallurgy · mapped topic

• C21D8/0226

  Hot rolling · CPC title

• C21D8/0236

  Cold rolling · CPC title