Preparation method and application of tailings-based zeolite@CDs-TiO2 composite photocatalyst

Patent metadata

Field	Value
Publication number	US-11951460-B1
Application number	US-202318466851-A
Country	US
Kind code	B1
Filing date	Sep 14, 2023
Priority date	Apr 24, 2023
Publication date	Apr 9, 2024
Grant date	Apr 9, 2024

Abstract

A preparation method and an application of a tailings-based zeolite@carbon dots-titanium dioxide (CDs-TiO 2 ) composite photocatalyst are provided, which relates to the field of solid waste utilization technologies. The preparation method includes performing an acidification treatment on tailings powder and then roasting to obtain modified tailings powder; adding the modified tailings powder and titanium dioxide into lye to obtain mixed suspension; stirring and aging the mixed suspension under ultraviolet irradiation to obtain an aged suspension, performing a hydrothermal reaction on the aged suspension to obtain a product, filtering, washing and drying the product to obtain the tailings-based zeolite@CDs-TiO 2 composite photocatalyst. The tailings-based zeolite@CDs-TiO 2 composite photocatalyst is used to degrade methylene blue, and the photocatalyst is used to treat an organic pollutant in water, which has advantages including a shift in response wavelength and a high photocatalyst activity, and the composite photocatalyst can be applied in an environmental protection field.

First claim

What is claimed is:

1. A preparation method of a tailings-based zeolite@carbon dots-titanium dioxide (CDs-TiO 2 ) composite photocatalyst, comprising:
step 1: tailings pretreatment, comprising: performing an acidification treatment on tailings powder by immersing the tailings powder into acid liquor and stirring evenly to obtain acidified tailings powder; roasting the acidified tailings powder at a temperature of 700-900 Celsius degrees (° C.) under a nitrogen (N 2 ) preservation and then keeping the temperature unchanged to obtain modified tailings powder; wherein the acidification treatment comprises: adding the tailings powder into diluted hydrochloric acid with a molar concentration of 1 molar per liter (M) and performing an ultrasonic treatment on the diluted hydrochloric acid added with the tailings powder for 1.5-2.5 hours (h);
step 2: adding titanium dioxide (TiO 2 ) and the modified tailings powder into lye sequentially and stirring to obtain a mixed suspension, wherein a weight ratio of the TiO 2 and the modified tailings powder is in a range of 0.5-1; and stirring and aging the mixed suspension for 8-16 h under a condition of ultraviolet irradiation to obtain an aged suspension; wherein a light intensity of the ultraviolet irradiation is in a range of 10-20 milliwatts per square centimeter (mW/cm 2 ); and the lye is sodium hydroxide (NaOH) solution with a molar concentration of 1-3 M; and
step 3: performing a hydrothermal reaction on the aged suspension to obtain a product, filtering the product to obtain a filtered product, and washing and drying the filtered product to obtain the tailings-based zeolite@CDs-TiO 2 composite photocatalyst; wherein a temperature of the hydrothermal reaction is in a range of 115-125° C., and a period of the hydrothermal reaction is in a range of 20-30 h.

2. The preparation method of the tailings-based zeolite@CDs-TiO 2 composite photocatalyst as claimed in claim 1 , wherein a particle size of the tailings powder is smaller than 125 microns (μm).

3. The preparation method of the tailings-based zeolite@CDs-TiO 2 composite photocatalyst as claimed in claim 1 , wherein the roasting comprises: introducing the N 2 into a tube furnace, heating the acidified tailings powder at a heating rate of 5 Celsius degrees per minute (° C./min) to the temperature of 700-900° C., and then roasting the acidified tailings powder at the temperature of 700-900° C.

4. The preparation method of the tailings-based zeolite@CDs-TiO 2 composite photocatalyst as claimed in claim 3 , wherein a flow speed of the N 2 is 100 milliliters per minute (mL/min).

5. The preparation method of the tailings-based zeolite@CDs-TiO 2 composite photocatalyst as claimed in claim 3 , wherein a period for keeping the temperature unchanged is 1 h.

6. The preparation method of the tailings-based zeolite@CDs-TiO 2 composite photocatalyst as claimed in claim 3 , wherein the washing and drying in step 3 comprises: washing, by using deionized water, the filtered product to neutrality to obtain a washed product, and freezing and drying the washed product for 48 h to obtain the tailings-based zeolite@CDs-TiO 2 composite photocatalyst.

Assignees

• Univ Taiyuan Technology

Inventors

• Dong Xianshu
• Fan Yuping
• Ma Xiaomin
• Guo Jiaqi
• Fu Yuanpeng
• Guo Ruifeng

Classifications

• B01J21/20

  Regeneration or reactivation · CPC title

• B01J35/77

  Compounds characterised by their crystallite size · CPC title

• B01J35/397

  Egg shell like · CPC title

• B01J29/06

  Crystalline aluminosilicate zeolites; Isomorphous compounds thereof · CPC title

• B01J37/345

  of ultraviolet wave energy · CPC title