Method including additive manufacturing a part and post-processing with two ionizing bars and a rotary barrel

Patent metadata

Field	Value
Publication number	US-11945165-B2
Application number	US-201916962140-A
Country	US
Kind code	B2
Filing date	Jan 9, 2019
Priority date	Jan 15, 2018
Publication date	Apr 2, 2024
Grant date	Apr 2, 2024

Abstract

A method for post-processing part obtained by additive manufacturing through sintering of a plastic powder, in order to remove particles detached from the part or partially sintered, the method including, consecutively, stripping (S 1 ) and ionizing blowing (S 2 ). Such a method makes it possible to remove particles having a largest dimension greater than a given dimension. The invention also relates to a corresponding manufacturing method of a plastic material part, and to a corresponding production method.

First claim

The invention claimed is:

1. A method of post-treatment of a part obtained by additive manufacturing by sintering of a powder of a plastic material, for the elimination, an at least partially sintered part, of the particles detached from said part or that are partially sintered, the method comprising successively:
stripping (S 1 ), thereby obtaining a stripped part; and
ionizing blowing (S 2 ) of the stripped part, comprising blowing ionized air onto the part;
wherein the stripping is performed in a rotary barrel; and
the ionizing blowing is performed with two ionizing bars, one ionizing bar being positioned inside said rotary barrel and another ionizing bar being disposed outside said rotary barrel.

2. The method of post-treatment according to claim 1 , wherein:
the stripping comprises sand-blasting (S 1 ′) said part.

3. The method of post-treatment according to claim 2 , wherein:
the sand-blasting employs glass microspheres of a diameter comprised between 45 and 90 microns.

4. The method of post-treatment according to claim 1 , comprising:
pre-blowing prior to the stripping (S 1 ).

5. The method of post-treatment according to claim 1 , further comprising:
a final method part of washing (S 3 ).

6. The method of post-treatment according to claim 5 , wherein:
the washing (S 3 ) comprises washing of the part in a non-aqueous solvent.

7. The method of post-treatment according to claim 1 , wherein:
the stripping (S 1 ) and the ionizing blowing (S 2 ) are carried out in batches of 300 to 10 000 parts.

8. The method of manufacturing a part from plastic material, comprising:
additive manufacturing (E 1 ) by sintering a powder of the plastic material, followed by depowdering (E 2 ); and
a method of post-treatment (E 3 ) according to claim 1 .

9. The manufacturing method according to claim 8 , wherein:
the plastic material is a polyamide.

10. The manufacturing method according to claim 8 , wherein:
the plastic material is an aliphatic polyamide.

11. The manufacturing method according to claim 8 , wherein:
the plastic material is an aliphatic polyamide in the form of polyamide 11.

12. The manufacturing method according to claim 8 , further comprising, prior to the additive manufacturing (E 1 ):
processing of the polyamide powder (E 0 ) comprising:
providing new powder having only grains of which a greatest dimension is less than or equal to 150 microns;
providing so-called used powder having already served for an additive manufacturing method part, and a calibration of said used powder in order for it to have only grains of which a greatest dimension is less than or equal to 150 microns; and
mixing the new powder and the calibrated used powder in a new powder/used powder ratio comprised between 70/30 and 50/50.

13. The manufacturing method according to claim 8 , further comprising, prior to the additive manufacturing (E 1 ):
processing of the polyamide powder (E 0 ) comprising:
providing new powder having only grains of which a greatest dimension is less than or equal to 150 microns;

providing so-called used powder having already served for an additive manufacturing method part, and a calibration of said used powder in order for it to have only grains of which a greatest dimension is less than or equal to 150 microns; and
mixing the new powder and the calibrated used powder in a new powder/used powder ratio of about 60/40.

14. The method of producing parts comprising a manufacturing method according to claim 8 , further comprising:
at least one qualifying method part (S 4 ) comprising determining, in a batch of a predetermined number of parts, a number of residual particles that are detached or partially sintered of a largest dimension greater than a predefined dimension, and, if said number of particles is not zero, modifying at least one parameter of a post-treatment, then performing a succession of manufacturing methods and qualifying method parts until said number of particles of largest dimension greater than a predefined dimension is zero.

Assignees

• Chanel Parfums Beaute

Inventors

• Salciarini Christian
• Bertucchi Quentin

Classifications

• B29C64/35 Primary

  Cleaning · CPC title

• B29C64/153

  using layers of powder being selectively joined, e.g. by selective laser sintering or melting · CPC title

• B33Y10/00

  Processes of additive manufacturing · CPC title

• B33Y40/10

  Pre-treatment · CPC title

• B33Y40/20

  Post-treatment, e.g. curing, coating or polishing · CPC title