Flame retardant masterbatch composition for foams containing a pH moderator

Patent metadata

Field	Value
Publication number	US-11939445-B2
Application number	US-202117516016-A
Country	US
Kind code	B2
Filing date	Nov 1, 2021
Priority date	Dec 1, 2020
Publication date	Mar 26, 2024
Grant date	Mar 26, 2024

Abstract

A masterbatch composition suitable for use as a flame retardant in extruded polymer foams, and process for manufacturing the same, and extruded foams containing same; the composition comprising: (a) 20 to 40 parts by weight base resin comprising styrene homopolymer or copolymer; (b) 1 to 16 parts by weight acid scavenger comprising an epoxy-based compound; (c) 2 to 6 parts by weight antioxidant comprising an alkyl or aryl phosphite; and (d) 45 to 60 parts by weight flame retardant comprising a non-hexabromocyclododecane (HBCD) brominated polymer or copolymer, wherein the amounts of (a), (b), (c), and (d) total 100 parts by weight; and (e) 0.6 to 10 parts by weight of pH moderator, based on 100 parts of (a) base resin plus (e) water soluble pH moderator.

First claim

What is claimed is:

1. A masterbatch composition suitable for use as a flame retardant in extruded polymer foams, comprising:
(a) 20 to 40 parts by weight base resin comprising styrene homopolymer or copolymer;
(b) 1 to 16 parts by weight acid scavenger comprising an epoxy-based compound;
(c) 2 to 6 parts by weight antioxidant comprising an alkyl or aryl phosphite; and
(d) 45 to 60 parts by weight flame retardant comprising a non-hexabromocyclododecane (HBCD) brominated polymer or copolymer;
wherein the amounts of (a), (b), (c), and (d) total 100 parts by weight;
the masterbatch composition further comprising
(e) 0.6 to 10 parts by weight of water soluble pH moderator, based on 100 parts of base resin plus the at least one water soluble pH moderator.

2. The masterbatch composition of claim 1 wherein the base resin contains 5 to 10 parts by weight of water soluble pH moderator, based on 100 parts of (a) base resin plus (e) water soluble pH moderator.

3. The masterbatch composition of claim 1 wherein the alkyl phosphite is bis(2,4-dicumylphenyl)pentaerythritol diphosphite, distearylpentaerythritol diphosphite, or di(2,4-di-(t-butyl)phenyl) pentaerythritol diphosphite.

4. The masterbatch composition of claim 1 wherein the aryl phosphite is tris(2,4-di-tert-butylphenyl)phosphite.

5. The masterbatch composition of claim 1 wherein the acid scavenger comprises a brominated epoxy compound.

6. The masterbatch composition of claim 1 wherein acid scavenger comprises epoxy cresol novolac resin.

7. The masterbatch composition of claim 1 wherein acid scavenger comprises epoxidized oil.

8. The masterbatch composition of claim 7 wherein a majority by weight of the acid scavenger is epoxidized oil.

9. An extruded polymer foam comprising a masterbatch composition, the masterbatch composition comprising:
(a) 20 to 40 parts by weight base resin comprising styrene homopolymer or copolymer;
(b) 1 to 16 parts by weight acid scavenger comprising an epoxy-based compound;
(c) 2 to 6 parts by weight antioxidant comprising an alkyl or aryl phosphite; and
(d) 45 to 60 parts by weight flame retardant comprising a non-hexabromocyclododecane (HBCD) brominated polymer or copolymer;
wherein the amounts of (a), (b), (c), and (d) total 100 parts by weight;
the masterbatch composition further comprising
(e) 0.6 to 10 parts by weight of a water soluble pH moderator, based on 100 parts of (a) base resin plus (e) water soluble pH moderator.

10. The extruded polymer foam of claim 9 wherein (e) contains 5 to 10 parts by weight of a water soluble pH moderator, based on 100 parts of (a) base resin plus (e) water soluble pH moderator.

11. The extruded polymer foam of claim 9 wherein the alkyl phosphite is bis(2,4-dicumylphenyl)pentaerythritol diphosphite, distearylpentaerythritol diphosphite, or di(2,4-di-(t-butyl)phenyl) pentaerythritol diphosphite.

12. The extruded polymer foam of claim 9 wherein the aryl phosphite is tris(2,4-di-tert-butylphenyl)phosphite.

13. The extruded polymer foam of claim 9 wherein the acid scavenger comprises a brominated epoxy compound.

14. The extruded polymer foam of claim 9 wherein the acid scavenger comprises epoxy cresol novolac resin.

15. The extruded polymer foam of claim 9 wherein acid scavenger comprises epoxidized oil.

16. The extruded polymer foam of claim 15 wherein a majority by weight of the acid scavenger is epoxidized oil.

Assignees

• Ddp Specialty Electronic Materials Us Llc

Inventors

• Huang Wenyi
• Kram Shari
• Rickard Mark
• Shankar Ravi B

Classifications

• C08J9/0061 Primary

  characterized by the use of several polymeric components · CPC title

• C08J3/201

  Pre-melted polymers · CPC title

• C08J3/226 Primary

  using a polymer as a carrier · CPC title

• C08J9/0095

  Mixtures of at least two compounding ingredients belonging to different one-dot groups · CPC title

• C08J9/122

  Hydrogen, oxygen, CO2, nitrogen or noble gases · CPC title