Additive manufacturing with nanofunctionalized precursors

Patent metadata

Field	Value
Publication number	US-11919085-B2
Application number	US-202117332229-A
Country	US
Kind code	B2
Filing date	May 27, 2021
Priority date	Feb 1, 2017
Publication date	Mar 5, 2024
Grant date	Mar 5, 2024

Abstract

Some variations provide a process for additive manufacturing of a nanofunctionalized metal alloy, comprising: providing a nanofunctionalized metal precursor containing metals and grain-refining nanoparticles; exposing a first amount of the nanofunctionalized metal precursor to an energy source for melting the precursor, thereby generating a first melt layer; solidifying the first melt layer, thereby generating a first solid layer; and repeating many times to generate a plurality of solid layers in an additive-manufacturing build direction. The additively manufactured, nanofunctionalized metal alloy has a microstructure with equiaxed grains. Other variations provide an additively manufactured, nanofunctionalized metal alloy comprising metals selected from aluminum, iron, nickel, copper, titanium, magnesium, zinc, silicon, lithium, silver, chromium, manganese, vanadium, bismuth, gallium, or lead; and grain-refining nanoparticles selected from zirconium, tantalum, niobium, titanium, or oxides, nitrides, hydrides, carbides, or borides thereof, wherein the additively manufactured, nanofunctionalized metal alloy has a microstructure with equiaxed grains.

First claim

What is claimed is:

1. An additively manufactured, nanofunctionalized metal alloy comprising one or more metals and grain-refining nanoparticles containing one or more nanoparticle elements, wherein said one or more metals are selected from the group consisting of aluminum, iron, nickel, copper, titanium, magnesium, zinc, silicon, lithium, silver, chromium, manganese, vanadium, bismuth, gallium, lead, and combinations thereof, wherein said one or more nanoparticle elements are selected from the group consisting of zirconium, zirconium oxides, zirconium nitrides, zirconium carbides, zirconium borides, tantalum, tantalum oxides, tantalum nitrides, tantalum carbides, tantalum borides, niobium, niobium oxides, niobium nitrides, niobium carbides, niobium borides, titanium, titanium oxides, titanium nitrides, titanium carbides, titanium borides, and combinations of the foregoing, wherein said additively manufactured, nanofunctionalized metal alloy has a microstructure with equiaxed grains, wherein said microstructure is substantially crack-free, and wherein at least 90 vol % of said microstructure contains grains that are characterized in that there is less than 25% standard deviation in each of average grain length, average grain width, and average grain height.

2. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said grain-refining nanoparticles are present in a nanoparticle concentration of at least 0.01 vol %.

3. The additively manufactured, nanofunctionalized metal alloy of claim 2 , wherein said grain-refining nanoparticles are present in a nanoparticle concentration of at least 0.1 vol %.

4. The additively manufactured, nanofunctionalized metal alloy of claim 3 , wherein said grain-refining nanoparticles are present in a nanoparticle concentration of at least 1 vol %.

5. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said grain-refining nanoparticles have an average largest dimension from about 50 nanometers to about 5000 nanometers.

6. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said grain-refining nanoparticles are selected from the group consisting of Al 3 Zr, Al 3 Ta, Al 3 Nb, Al 3 Ti, TiB, TiB 2 , WC, AlB, and combinations thereof.

7. The nanofunctionalized metal alloy of claim 1 , wherein said additively manufactured, nanofunctionalized metal alloy comprises inclusions that contain both (i) at least one of said one or more metals and (ii) at least one of said one or more nanoparticle elements.

8. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said grain-refining nanoparticles are lattice-matched to within ±5% compared to a metal alloy containing said one or more metals but not said grain-refining nanoparticles.

9. The additively manufactured, nanofunctionalized metal alloy of claim 8 , wherein said grain-refining nanoparticles are lattice-matched to within ±0.5% compared to a metal alloy containing said one or more metals but not said grain-refining nanoparticles.

10. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said grain-refining nanoparticles are atomic density-matched to within ±25% compared to a metal alloy containing said one or more metals but not said grain-refining nanoparticles.

11. The additively manufactured, nanofunctionalized metal alloy of claim 10 , wherein said grain-refining nanoparticles are atomic density-matched to within ±5% compared to a metal alloy containing said one or more metals but not said grain-refining nanoparticles.

12. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said additively manufactured, nanofunctionalized metal alloy is characterized by an average grain size of less than 1 millimeter.

13. The additively manufactured, nanofunctionalized metal alloy of claim 12 , wherein said additively manufactured, nanofunctionalized metal alloy is characterized by an average grain size of less than 10 microns.

14. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said microstructure has a crystallographic texture that is not solely oriented in an additive-manufacturing build direction.

15. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said microstructure contains a plurality of dendrite layers having differing primary growth-direction angles with respect to each other.

16. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said microstructure contains a plurality of dendrite layers having an average layer thickness of at least 10 microns.

17. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said additively manufactured, nanofunctionalized metal alloy is selected from the group consisting of an aluminum alloy, a steel alloy, a nickel alloy, a titanium alloy, a copper alloy, and combinations thereof.

18. A nanofunctionalized metal alloy comprising:
(a) one or more metals selected from the group consisting of aluminum, iron, nickel, copper, titanium, magnesium, zinc, silicon, lithium, silver, chromium, manganese, vanadium, bismuth, gallium, lead, and combinations thereof; and
(b) grain-refining nanoparticles comprising a nanoparticle element selected from the group consisting of zirconium, zirconium oxides, zirconium nitrides, zirconium carbides, zirconium borides, tantalum, tantalum oxides, tantalum nitrides, tantalum carbides, tantalum borides, niobium, niobium oxides, niobium nitrides, niobium carbides, niobium borides, titanium, titanium oxides, titanium nitrides, titanium carbides, titanium borides, and combinations of the foregoing,
wherein said nanofunctionalized metal alloy has a microstructure with equiaxed grains, wherein at least 90 vol % of said microstructure contains grains that are characterized in that there is less than 25% standard deviation in each of average grain length, average grain width, and average grain height, and
wherein said microstructure is substantially crack-free.

19. The nanofunctionalized metal alloy of claim 18 , wherein said grain-refining nanoparticles are present in a concentration of at least 0.1 vol %.

20. The nanofunctionalized metal alloy of claim 19 , wherein said grain-refining nanoparticles are present in a concentration of at least 1 vol %.

21. The nanofunctionalized metal alloy of claim 18 , wherein said nanofunctionalized metal alloy comprises inclusions that contain both (i) at least one of said one or more metals and (ii) said nanoparticle element.

22. The nanofunctionalized metal alloy of claim 18 , wherein said grain-refining nanoparticles have an average largest dimension from about 50 nanometers to about 5000 nanometers.

23. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein at least 99 vol % of said microstructure contains grains that are characterized in that there is less than 25% standard deviation in each of average grain length, average grain width, and average grain height.

24. The nanofunctionalized metal alloy of claim 18 , wherein at least 99 vol % of said microstructure contains grains that are characterized in that there is less than 25% standard deviation in each of average grain length, average grain width, and average grain height.

25. The additively manufactured, nanofunctionalized metal alloy of claim 1 , wherein said one or more nanoparticle elements are selected from the

Assignees

• Hrl Lab Llc

Inventors

• Martin John H
• Yahata Brennan
• Schaedler Tobias A
• Hundley Jacob M

Classifications

• B22F5/02 Primary

  of piston rings · CPC title

• B22F1/054

  Nanosized particles · CPC title

• B22F1/056

  Submicron particles having a size above 100 nm up to 300 nm · CPC title

• B22F1/08

  Metallic powder characterised by particles having an amorphous microstructure · CPC title

• B33Y10/00 Primary

  Processes of additive manufacturing · CPC title