Acrylic emulsion pressure sensitive adhesive composition

Patent metadata

Field	Value
Publication number	US-11912909-B2
Application number	US-202017290914-A
Country	US
Kind code	B2
Filing date	Jul 29, 2020
Priority date	Sep 3, 2019
Publication date	Feb 27, 2024
Grant date	Feb 27, 2024

Abstract

An acrylic emulsion pressure sensitive adhesive composition is provided. The acrylic emulsion pressure sensitive adhesive composition, due to pH-dependent properties, exhibits stable adhesion when attached to an adherend, but when it needs to be removed, it can be easily removed without residue using an alkaline solution. Thus, if the acrylic emulsion pressure sensitive adhesive composition is used as a pressure sensitive adhesive for a label of a plastic packaging article, the label can be easily removed during a recycling process, thus improving recycling efficiency.

First claim

The invention claimed is:

1. An acrylic emulsion pressure sensitive adhesive composition comprising:
a first acrylic polymer, wherein the first acrylic polymer is negatively charged;
a second acrylic polymer, wherein the second acrylic polymer is positively charged;
a first external cross-linking agent; and
a second external cross-linking agent,
wherein the first external cross-linking agent is bonded to at least one of the first acrylic polymer or the second acrylic polymer,
wherein the first external cross-linking agent is a keto group-containing monomer, and the second external cross-linking agent is a dihydrazide,
wherein the second acrylic polymer comprises repeating units derived from alkyl (meth)acrylate; repeating units derived from comonomers selected from the group consisting of a vinyl-based monomer and a hydroxyl group-containing (meth)acrylate; and repeating units derived from an amino group-containing (meth)acrylate,
wherein the vinyl-based monomer is one or more selected from the group consisting of styrene, methylstyrene, ethylstyrene, butylstyrene, chlorostyrene, vinylnaphthalene, chloromethylstyrene, hydroxymethylstyrene, divinylbenzene and vinyl acetate, and
wherein the second acrylic polymer is positively charged through the repeating units derived from the amino group-containing (meth)acrylate, and the repeating units derived from the amino group-containing (meth)acrylate are included in a content of 5 to 12 mol %, based on total repeating units of the second acrylic polymer.

2. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first acrylic polymer is negatively charged through repeating units derived from unsaturated carboxylic acid, and the repeating units derived from the unsaturated carboxylic acid are included in an amount of 1 to 10 mol %, based on total repeating units of the first acrylic polymer.

3. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first acrylic polymer comprises repeating units derived from alkyl (meth)acrylate; repeating units derived from comonomers selected from the group consisting of vinyl monomers and hydroxyl group-containing (meth)acrylate; and repeating units derived from unsaturated carboxylic acid.

4. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first acrylic polymer comprises repeating units derived from methyl (meth)acrylate and 2-ethylhexyl (meth)acrylate; repeating units derived from styrene and vinyl acetate; and repeating units derived from (meth)acrylic acid.

5. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the second acrylic polymer comprises repeating units derived from methyl (meth)acrylate and 2-ethylhexyl (meth)acrylate; repeating units derived from styrene; and
repeating units derived from dimethyl aminoethyl (meth)acrylate.

6. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first acrylic polymer and the second acrylic polymer are included at a weight ratio of 9.9:0.1 to 0.1:9.9.

7. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first acrylic polymer comprises repeating units derived from unsaturated carboxylic acid in an amount of 1 to 7 mol % based on total repeating units of the first acrylic polymer, the second acrylic polymer comprises the repeating units derived from the amino group-containing (meth)acrylate in an amount of 8 to 12 mol % based on total repeating units of the second acrylic polymer, and the first acrylic polymer and the second acrylic polymer are included at a weight ratio of 9:1 to 8:2.

8. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first external cross-linking agent is one or more keto group-containing monomers selected from the group consisting of diacetone (meth)acrylamide, diacetone (meth)acrylate, and acetoacetoxyalkyl (meth)acrylate.

9. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the second external cross-linking agent is one or more dihydrazide selected from the group consisting of oxalic acid dihydrazide, malonic acid dihydrazide, succinic acid dihydrazide, glutaric acid dihydrazide, adipic acid dihydrazide, pimelic acid dihydrazide, suberic acid dihydrazide, azelaic acid dihydrazide, sebacic acid dihydrazide, dodecanedioic acid dihydrazide, phthalic acid dihydrazide, isophthalic acid dihydrazide, terephthalic acid dihydrazide, 2,6-naphthalene dicarboxylic acid dihydrazide, naphthalic acid dihydrazide, acetonedicarboxylic acid dihydrazide, fumaric acid dihydrazide, maleic acid dihydrazide, itaconic acid dihydrazide, trimellitic acid dihydrazide, 1,3,5-benzenetricarboxylic acid dihydrazide, pyromellitic acid dihydrazide and aconitic acid dihydrazide.

10. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the first external cross-linking agent is bonded in an amount of 0.1 to 1 mole, based on 100 moles of total repeating units of the first acrylic polymer or the second acrylic polymer.

11. The acrylic emulsion pressure sensitive adhesive composition according to claim 1 , wherein the second external cross-linking agent is included at 0.2 to 1 equivalent, based on 1 equivalent of the first external cross-linking agent.

12. A pressure sensitive adhesive comprising a substrate; a pressure sensitive adhesive layer, wherein the pressure sensitive layer is formed by coating the acrylic emulsion pressure sensitive adhesive composition according to claim 1 on at least one side of the substrate.

Assignees

• Lg Chemical Ltd

Inventors

• Lee Yong Man
• Ryu Jin Young

Classifications

• C09J7/385 Primary

  Acrylic polymers · CPC title

• C08K5/0025

  Crosslinking or vulcanising agents; including accelerators · CPC title

• C08K5/07

  Aldehydes; Ketones · CPC title

• C08K5/132

  Phenols containing keto groups {, e.g. benzophenones} · CPC title

• C08K5/25

  Carboxylic acid hydrazides · CPC title