Master batch, polycarbonate resin composition, injection foam molded body and method for producing same

Patent metadata

Field	Value
Publication number	US-11898016-B2
Application number	US-202017079388-A
Country	US
Kind code	B2
Filing date	Oct 23, 2020
Priority date	Apr 27, 2018
Publication date	Feb 13, 2024
Grant date	Feb 13, 2024

Abstract

A masterbatch (C) containing thermally expandable microcapsules (A) and a carrier resin composition (B) is provided. The carrier resin composition (B) contains a carrier resin (B1) and a plasticizer (B2), the carrier resin (B1) being an acrylic resin having a weight average molecular weight of 8,000 or more and 350,000 or less, and the plasticizer (B2) being an acrylic plasticizer having a weight average molecular weight of 1,000 or more and 20,000 or less. The carrier resin composition (B) is substantially compatible with a polycarbonate resin and has a shear viscosity of 1.0 Pa·s or more and 1.5×106 Pa·s or less at 80° C. The occurrence of whitening is suppressed and a good appearance can be obtained in an injection molded foam made with the masterbatch. A polycarbonate resin composition, an injection molded foam, and a method for producing an injection molded foam are provided.

First claim

The invention claimed is:

1. A masterbatch (C) comprising:
thermally expandable microcapsules (A); and
a carrier resin composition (B), wherein the carrier resin composition (B) contains a carrier resin (B1) and a plasticizer (B2), the carrier resin (B1) being an acrylic resin having a weight average molecular weight of 8,000 or more and 350,000 or less and being a solid at 20° C., and
the plasticizer (B2) being a liquid at 20° C. and having a weight average molecular weight of 1,000 or more and 20,000 or less, and
wherein the carrier resin composition (B) is substantially compatible with a polycarbonate resin and has a shear viscosity of 1.0 Pas or more and 1.5×10 6 Pa·s or less at 80° C.

2. The masterbatch according to claim 1 , wherein the masterbatch (C) is used for the polycarbonate resin.

3. The masterbatch according to claim 1 , wherein the polycarbonate resin further comprises at least one other thermoplastic resin selected from the group consisting of a polyester resin, a polyester-polyether copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylonitrile-ethylene-propylene-diene-styrene copolymer, an acrylate-styrene-acrylonitrile copolymer, an acrylonitrile-styrene copolymer, a polyarylate resin, a polystyrene resin, and a polyamide resin.

4. The masterbatch according to claim 1 , wherein the plasticizer (B2) is an acrylic plasticizer.

5. The masterbatch according to claim 1 , wherein the carrier resin (B1) has a glass transition temperature (Tg) of −30° C. or more and 150° C. or less.

6. The masterbatch according to claim 1 ,
wherein the thermally expandable microcapsules (A) have a core-shell structure and are constituted by a core comprising at least one compound having a boiling point of 10° C. or more and 330° C. or less, and a shell that encloses the core, and
wherein the shell comprises a resin having a constitutional unit derived from at least one monomer selected from the group consisting of a nitrile monomer, a (meth)acrylate monomer, an aromatic vinyl monomer, a diene monomer, a vinyl monomer having a carboxyl group, and a monomer having at least one reactive functional group selected from the group consisting of a methylol group, a hydroxyl group, an amino group, an epoxy group, and an isocyanate group.

7. The masterbatch according to claim 1 , wherein the thermally expandable microcapsules (A) have a maximum expansion temperature of 180° C. or more and 300° C. or less.

8. The masterbatch according to claim 6 , wherein, in the resin forming the shell, a constitutional unit derived from at least one monomer selected from the group consisting of a monomer containing a carboxyl group and a monomer containing an amino group is contained in a concentration of 12 mmol/g or less.

9. The masterbatch according to claim 1 , wherein the thermally expandable microcapsules (A) have an average particle size of 0.5 μm or more and 50 μm or less.

10. The masterbatch according to claim 1 , wherein the carrier resin (B1) is an acrylic resin comprising acrylic resin particles (a) having an average particle size of 50 μm or more and 500 μm or less and acrylic resin particles (b) having an average particle size of 0.05 μm or more and 0.5 μm or less, and
wherein the acrylic resin particles (a) are coated with the acrylic resin particles (b).

11. The masterbatch according to claim 10 , wherein the acrylic resin particles (a) comprise a (meth)acrylic acid ester in an amount of 30 to 100 wt % and a vinyl monomer copolymerizable with the (meth)acrylic acid ester in an amount of 0 to 70 wt %.

12. The masterbatch according to claim 10 , wherein the acrylic resin particles (b) comprise a (meth)acrylic acid ester in an amount of 30 to 100 wt % and a vinyl monomer copolymerizable with the (meth)acrylic acid ester in an amount of 0 to 70 wt %.

13. The masterbatch according to claim 10 , wherein the acrylic resin particles (b) are polymer particles obtained by polymerization of 50 to 90 parts by weight of latex particles (b1) comprising a (meth)acrylic acid ester in an amount of 50 to 100 wt %, an aromatic vinyl monomer in an amount of 0 to 40 wt %, a vinyl monomer copolymerizable with the (meth)acrylic acid ester and the aromatic vinyl monomer in an amount of 0 to 10 wt %, and a multifunctional monomer in an amount of 0 to 5 wt % with 10 to 50 parts by weight of a monomer mixture (b2) comprising a (meth)acrylic acid ester in an amount of 10 to 100 wt %, an aromatic vinyl monomer in an amount of 0 to 90 wt %, a vinyl cyanate monomer in an amount of 0 to 25 wt %, and a vinyl monomer copolymerizable with the (meth)acrylic acid ester, the aromatic vinyl monomer, and the vinyl cyanate monomer in an amount of 0 to 20 wt %, and a total amount of the latex particles (b1) and the monomer mixture (b2) is 100 parts by weight.

14. The masterbatch according to claim 1 , wherein the masterbatch (C) comprises the thermally expandable microcapsules (A) in an amount of 30 wt % or more and 80 wt % or less, the carrier resin (B1) in an amount of 15 wt % or more and 65 wt % or less, and the plasticizer (B2) in an amount of 5 wt/o or more and 30 wt/o or less, and the amount of the carrier resin (B1) is larger than the amount of the plasticizer (B2).

15. A polycarbonate resin composition comprising:
the masterbatch according to claim 1 in an amount of 1 to 15 wt %, a polycarbonate resin in an amount of 30 to 99 wt %, and at least one other thermoplastic resin selected from the group consisting of a polyester resin, a polyester-polyether copolymer, an acrylonitrile-butadiene-styrene copolymer, an acrylonitrile-ethylene-propylene-diene-styrene copolymer an acrylate-styrene-acrylonitrile copolymer, an acrylonitrile-styrene copolymer, a polyarylate resin, a polystyrene resin, and a polyamide resin in an amount of 0 to 55 wt %.

16. The polycarbonate resin composition according to claim 15 , further comprising an inorganic compound.

17. An injection molded foam that is obtained through foam injection molding of the polycarbonate resin composition according to claim 15 .

18. A method for producing an injection molded foam, the method comprising:
supplying the polycarbonate resin composition according to claim 15 to an injection molding machine; and
moving a core of a mold backward after filling to an initial fill thickness has been completed.

Assignees

• Kaneka Corp

Inventors

• Uchida Soichi
• Saegusa Kazunori
• Sato Mitsutaka

Classifications

• C08J3/22 Primary

  using masterbatch techniques · CPC title

• B29C45/0001

  characterised by the choice of material · CPC title

• B29C45/14795

  Porous or permeable material, e.g. foam · CPC title

• C08J9/0061

  characterized by the use of several polymeric components · CPC title

• C08J9/228

  Forming foamed products · CPC title