Abstract

A polar plate is fabricated. The polar plate is flexible and made of a plastic graphite composite. No matter a supporting member is used for calendering or not, a thin polar plate with controllable thickness is fabricated. The polar plate is excellent in blocking the through-transmission of vanadium ions and the limit of blending ratio of conductive carbon is broken through. The longitudinal through-transmission volume resistivity (proportional resistance to thickness) is greatly improved by adjusting the blending ratio of conductive carbon for meeting the demand of conductivity. In the mean time, the present invention strengthens the rigidity required for the thin polar plate while providing large-area polar plate fabrication for industrial use and convenience and provides a cooling and pressing method for patterning a composite polar plate. An integrated mold is thus obtained to replace the conventional polar plate which needs to be processed and prepared with runner.

First claim

What is claimed is:

1. A method for fabricating a polar plate of a plastic graphite composite comprising steps of:
(a) ball-milling a conductive powder composition with high carbon (>98%), less than 5 weight percent (wt %) of a flame retardant, and low ash (<1%) for at least 0.5 hours (hr) at a speed of at least 200 rounds per minute (rpm) to form a conductive powder;
(b) mixing the conductive powder, a thermoplastic/thermosetting resin adhesive composition, and a solvent by stirring at least 1 hr to form a mixture;
(c) directly and repeatedly calendering said mixture into a rigid plastic sheet by rolling/squeezing and obtaining a requested thickness of said plastic sheet;
(d) depositing said plastic sheet to process volatilization under a low-temperature vacuum to remove said solvent;
(e) obtaining a composite plastic plate through repeatedly calendering said plastic sheet to a requested thickness with at least one conductive woven iron fabric supporting member stacked into layers consisting of an upper layer of the plastic sheet together with a lower layer of the plastic sheet and a plurality of overlapping layers of the plastic sheet alternating with the conductive woven iron fabric support members to obtain at least one layer of a plastic composite plate having the plastic sheets and the at least one woven iron fabric supporting member; and
(f) graphic-shaping said plastic composite plate with required heat and pressure according to a requested graph to obtain a finished shaped plate.

2. The method according to claim 1 , wherein said thermoplastic/thermosetting resin adhesive composition is selected from a group consisting of a thermoplastic resin, a thermosetting resin, and a combination of said thermoplastic resin and said thermosetting resin.

3. The method according to claim 2 , wherein said thermoplastic/thermosetting resin adhesive composition is selected from a group consisting of a halogen crystalline resin, a halogen non-crystalline resin, a non-halogen crystalline resin, and a non-halogen non-crystalline resin.

4. The method according to claim 1 , wherein said graph is at least one line continuously extending and said line is selected from a group consisting of a straight line, a wavy curve, a regular line, and an irregular line.

5. The method according to claim 1 , wherein, in step (f), said pressure is a gauge pressure greater than 20 kilograms-force per square centimeter (kgf/cm 2 ).

6. The method according to claim 1 , wherein said finished plate has a volume resistivity at Z-axis not greater than 10 −1 ohm-meters.

Assignees

• Iner Aec Executive Yuan

Inventors

• Ku Hung-Hsien
• Hsu Ning-Yih
• Lin Han-Jou
• Hung Tai-Feng
• Chen Qiao-Ya

Classifications

• B29C43/006 Primary

  Pressing and sintering powders, granules or fibres · CPC title

• B29B9/02

  by dividing preformed material · CPC title

• B29C43/003

  characterised by the choice of material · CPC title

• B29C43/24

  Calendering · CPC title

• B29C43/46

  Rollers · CPC title