Duplex stainless clad steel plate and method of producing same

Patent metadata

Field	Value
Publication number	US-11891675-B2
Application number	US-201917042185-A
Country	US
Kind code	B2
Filing date	Mar 28, 2019
Priority date	Mar 30, 2018
Publication date	Feb 6, 2024
Grant date	Feb 6, 2024

Abstract

Disclosed is a duplex stainless clad steel plate in which a duplex stainless steel plate as a cladding metal is bonded or joined to one or both surfaces of a base steel plate, in which the base steel plate comprises a predetermined chemical composition such that Nb/N is 3.0 or more and Ceq is 0.35 to 0.45, and the duplex stainless steel plate comprises: a predetermined chemical composition such that PI is 34.0 to 43.0; and a microstructure containing a ferrite phase in an area fraction of 35% to 65%, and in the microstructure, an amount of precipitated Cr is 2.00% or less and an amount of precipitated Mo is 0.50% or less.

First claim

The invention claimed is:

1. A duplex stainless clad steel plate in which a duplex stainless steel plate as a cladding metal is bonded or joined to one or both surfaces of a base steel plate, wherein
the base steel plate comprises a first chemical composition containing, in mass %, C: 0.06% to 0.25%, Si: 0.05% to 0.50%, Mn: 0.70% to 1.60%, P: 0.030% or less, S: 0.010% or less, Al: 0.005% to 0.100%, Mo: 0.01% to 0.15%, Nb: 0.010% to 0.040%, Ti: less than 0.005%, and N: 0.0010% to 0.0100%, optionally at least one selected from the group consisting of Cu: 0.50% or less, Ni: 0.50% or less, Cr: 0.40% or less, and V: 0.050% or less, with the balance being Fe and inevitable impurities, in a range such that Nb/N is 3.0 or more and Ceq represented by the following Expression (1) is 0.35 to 0.45:
Ceq=C+Mn/6+(Cu+Ni)/15+(Cr+Mo+V)/5  (1)

where the symbol of each element indicates the content in mass % of the element, and any element not contained is calculated as 0,
the duplex stainless steel plate comprises:
a second chemical composition containing, in mass %, C: 0.030% or less, Si: 1.00% or less, Mn: 2.00% or less, P: 0.050% or less, S: 0.0100% or less, Ni: 5.00% to 8.00%, Cr: more than 24.0% and not more than 28.0%, Mo: 2.5% to 4.0%, and N: 0.08% to 0.30%, optionally at least one selected from the group consisting of Cu: 1.50% or less, W: 1.50% or less, Co: 1.50% or less, Ti: 0.25% or less, and Nb: 0.25% or less, with the balance being Fe and inevitable impurities, in a range such that PI defined by the following Expression (2) is 34.0 to 43.0:
PI=Cr+3.3Mo+16N  (2)

where the symbol of each element indicates the content in mass % of the element; and
a microstructure containing a ferrite phase in an area fraction of 35% to 65%, and
in the microstructure, an amount of precipitated Cr is 2.00 mass % or less and an amount of precipitated Mo is 0.50 mass % or less.

2. A method of producing a duplex stainless clad steel plate in which a duplex stainless steel plate as a cladding metal is bonded or joined to one or both surfaces of a base steel plate, the method comprising:
preparing a clad slab by stacking a first blank plate to be the base steel plate and a second blank plate to be the duplex stainless steel plate as the cladding metal in a layered manner, the first blank plate comprising the first chemical composition as recited in claim 1 , and the second blank plate comprising the second chemical composition as recited in claim 1 and a microstructure containing a ferrite phase in an area fraction of 35% to 65%;
heating the clad slab to 1050° C. to 1250° C.;
then hot rolling the clad slab with a rolling reduction ratio of 2.0 or more to obtain a rolled clad body in which the base steel plate and the duplex stainless steel plate are bonded or joined together;
allowing the rolled clad body to naturally cool;
then reheating the rolled clad body to 1000° C. to 1100° C.;
then cooling the rolled clad body such that the duplex stainless steel plate is cooled at a cooling rate of 0.8° C./s or higher and the base steel plate is cooled at a cooling rate of 1.0° C./s or higher; and
then tempering the rolled clad body at 700° C. or lower to produce the duplex stainless clad steel plate of claim 1 .

Assignees

• Jfe Steel Corp

Inventors

• Kuronuma Yota
• Ohtsubo Hirofumi
• Yokota Tomoyuki

Classifications

• C21D9/46 Primary

  for sheet metals · CPC title

• B21B1/38

  for rolling sheets of limited length, e.g. folded sheets, superimposed sheets, {pack rolling}(B21B1/40 takes precedence; folding sheets before, or separating layers after, rolling B21B47/00) · CPC title

• B21B3/02

  Rolling special iron alloys {, e.g. stainless steel} · CPC title

• B23K20/04

  by means of a rolling mill · CPC title

• C21D8/0226

  Hot rolling · CPC title