Use of composite materials in the manufacture of electrical heating panels, process of production and electrical heating panels thereof

Patent metadata

Field	Value
Publication number	US-11856662-B2
Application number	US-202117908867-A
Country	US
Kind code	B2
Filing date	Feb 24, 2021
Priority date	Mar 2, 2020
Publication date	Dec 26, 2023
Grant date	Dec 26, 2023

Abstract

The disclosure relates to the use of a composite material as electro-thermal material in a process for the production of an electrical heating panel, wherein the electrical heating panel comprises at least one device selected from a plate, a sheet or a film, wherein said device has one or more layers wherein at least one layer is a heating layer made of a composite material comprising a first polymer which is one or more amorphous polymers or one or more semi-crystalline polymers selected from polyethylene and/or polypropylene; and from 2.0 to 20.0 wt. % of carbon particles and wherein the heating layer or at least one heating layer has a thickness ranging from 100 μm to 4.0 mm. The disclosure also relates to the use of such electrical heating panel in a motor vehicle.

First claim

The invention claimed is:

1. Electrical heating panel, wherein the electrical heating panel comprises at least one device selected from a plate, a sheet or a film, wherein said device has one or more layers wherein at least one layer is a heating layer, characterized in that the one or more heating layers are made of a composite material comprising:
from 5 to 95 wt. % based on the total weight of the composite material of a first polymer is or comprises a first polypropylene resin wherein resin wherein the first polypropylene resin is selected from a propylene homopolymer, a copolymer of propylene with one or more comonomers selected from ethylene and C4-C20 alpha-olefins, an heterophasic polypropylene and any mixture thereof;
from 5.0 to 16.0 wt. % of carbon particles based on the total weight of the composite material as determined according to ISO 11358:2014; wherein the carbon particles are selected from carbon nanotubes, carbon fibers, carbon black and any combination thereof; wherein at least 85 wt. % of the carbon particles based on the total weight of the carbon particles have an average aspect ratio L/D that is ranging from 120 to 800;
wherein each of the one or more heating layers has a thickness ranging from 100 μm to 4.0 mm.

2. The electrical heating panel according to claim 1 , characterized in that the device comprises only one heating layer.

3. The electrical heating panel according to claim 2 , characterized in that the device is monolayered and comprises only the heating layer.

4. The electrical heating panel according to claim 1 , characterized in that the device is multi-layered and comprises one or more heating layers and one or more insulating layers wherein the insulating layer is made of a third polymer that is the same as the first polymer or that is different from the first polymer provided it is of the same nature.

5. The electrical heating panel according to any claim 1 , characterised in that the device is multi-layered and comprises one or more heating layers and one or more insulating layers, wherein the insulating layer is devoid of conductive particles.

6. The electrical heating panel according to claim 1 , characterized in that the electrical heating panel comprises two electrodes in contact with the electrical heating layer, and in that the content of carbon particles in the composite material is selected to comply with the formula:

wt
.

%

⁢

carbon
⁢

particles

≥

-

1
a

*

ln

[

U
2

*
h

b
*

HP
min

*

l
2

]

wherein:
U is the voltage intended to be applied to the electrical heating panel; preferably U is ranging from 12 to 48 V;
HP min is the minimal heating power desired; preferably HP min is ranging from 200 W/m 2 to 4000 W/m 2 ;
h is the thickness of the heating layer and is ranging from 100 μm to 4.0 mm; preferably h is ranging from 100 μm to 1.0 mm or from 0.5 mm to 2.5 mm;
1 is the distance between the two electrodes; preferably 1 is ranging from 5 to 50 cm;
a is at least 0.5,
b is at least 2;
and wherein at least 85 wt. % of the carbon particles based on the total weight of the carbon particles have an average aspect ratio L/D ranging from 140 to 290.

7. The electrical heating panel according to claim 1 , characterized in that the first polymer:
is selected from a virgin polymer resin, a post-consumer polymer resin and a blend of a virgin polymer resin and a post-consumer polymer resin; and/or
comprises from 5 to 100 wt. % of post-consumer polymer resin based on the total weight of the first polymer.

8. The electrical heating panel according to claim 1 , characterized in that the carbon particles are directly blended with the first polymer; or in that the carbon particles are provided in a form of a masterbatch comprising the blend of carbon particles in a content ranging from 4.0 wt. % to 30.0 wt. % as determined according to ISO 11358:2014 and based on the total weight of said masterbatch; and a second polymer which is one or more semi-crystalline polymers selected from polypropylene; provided that the second polymer is of the same nature as the first polymer.

9. The electrical heating panel according to claim 1 , characterized in that the composite material is produced by the direct blend of the carbon particles with the first polymer, and in that the first polypropylene resin has a melt index MI2 ranging from 80 to 260 g/10 min.

10. The electrical heating panel according to claim 1 , characterized in that the carbon particles are provided in a form of a masterbatch comprising the blend of carbon particles and a second polymer; wherein the second polymer is or comprises a second polypropylene resin.

11. Electrical heating panel, wherein the electrical heating panel comprises at least one device selected from a plate, a sheet or a film, wherein said device has one or more layers wherein at least one layer is a heating layer, characterized in that the one or more heating layers are made of a composite material comprising:
from 5 to 95 wt. % based on the total weight of the composite material of a first polymer wherein the first polymer is or comprises a first polyethylene resin;
from 5.0 to 16.0 wt. % of carbon particles based on the total weight of the composite material as determined according to ISO 11358:2014; wherein the carbon particles are selected from carbon nanotubes, carbon fibers, carbon black and any combination thereof; wherein at least 85 wt. % of the carbon particles based on the total weight of the carbon particles have an average aspect ratio L/D that is ranging from 120 to 800;
wherein each of the one or more heating layers has a thickness ranging from 100 μm to 4.0 mm.

12. The electrical heating panel according to claim 11 , characterized in that the first polyethylene resin has a melt index MI2 ranging from 0.1 to 100 g/10 min.

13. The electrical heating panel according to claim 11 , characterized in that the first polyethylene resin has a density ranging from 0.900 g/cm 3 to 0.960 g/cm 3 .

14. The electrical heating panel according to claim 11 , characterized in that the first polyethylene resin is or comprises a post-consumer resin being a blend of recycled polypropylene and recycled polyethylene, wherein the content of the recycled polypropylene ranges from 3 to 25 wt. % relative to the total weight of the post-consumer resin.

15. The electrical heating panel according to claim 11 , characterized in that

Assignees

• Totalenergies Onetech

Inventors

• Lhost Olivier
• Trolez Yves
• Boukalidis Cristo
• Marcq François

Classifications

• H05B3/36 Primary

  heating conductor embedded in insulating material · CPC title

• B32B27/08

  of synthetic resin · CPC title

• B32B27/20

  using fillers, pigments, thixotroping agents · CPC title

• B32B27/32

  comprising polyolefins {(comprising vinyl (co)polymers or acrylic (co)polymers B32B27/30)} · CPC title

• H05B3/145

  Carbon only, e.g. carbon black, graphite · CPC title