Wash primer composition

Patent metadata

Field	Value
Publication number	US-11845878-B2
Application number	US-201917264419-A
Country	US
Kind code	B2
Filing date	Jul 31, 2019
Priority date	Jul 31, 2018
Publication date	Dec 19, 2023
Grant date	Dec 19, 2023

Abstract

A coating composition includes a (A) binder component and a (B) pigment component. The (A) binder component includes (A1) polyvinyl butyrate, (A2) a particular film forming resin, (A3) an acid, (A4) an optional functionalized tri-alkoxy silane, and (A5) an optional polymeric phosphate ester. The (B) pigment component includes (B1) a calcium ion-exchanged silica, (B2) a corrosion inhibiting pigment, and (B3), a polyalkylene oxide phosphate. The coating composition is formed by combining the aforementioned components. In a method, the coating composition is applied to a substrate.

First claim

What is claimed is:

1. A coating composition comprising:
A. a binder component comprising;
(A1) polyvinyl butyral present in an amount of from about 30 to about 70 parts by weight based on 100 parts by weight of said binder component;
(A2) a film forming resin that is Poly(Bisphenol A-Co-Epichlorohydrin) Glycidyl End-Capped and that is present in an amount of from about 10 to about 40 parts by weight based on 100 parts by weight of said binder component;
(A3) an acid present in an amount of from about 13 to about 30 parts by weight based on 100 parts by weight of said binder component; and
(A4) a functionalized tri-alkoxy silane present in an amount of from about 3 to about 10 parts by weight based on 100 parts by weight of said binder component;

B. a pigment component comprising;
(B1) a calcium ion-exchanged silica present in an amount of from about 30 to about 40 parts by weight based on 100 parts by weight of said binder component;
(B2) a corrosion inhibiting pigment present in an amount of from about 40 to about 50 parts by weight based on 100 parts by weight of said binder component; and
(B3) a polyalkylene oxide phosphate present in an amount of from about 1 to about 7 parts by weight based on 100 parts by weight of said binder component.

2. The coating composition of claim 1 wherein the polyvinyl butyral is present in an amount of from about 60 to about 65 parts by weight based on 100 parts by weight of said binder component.

3. The coating composition of claim 1 wherein the film forming resin is present in an amount of from about 13 to about 17 parts by weight based on 100 parts by weight of said binder component.

4. The coating composition of claim 1 wherein the acid is present in an amount of from about 13 to about 15 parts by weight based on 100 parts by weight of said binder component.

5. The coating composition of claim 4 wherein the acid is phosphoric acid.

6. The coating composition of claim 1 wherein the functionalized tri-alkoxy silane is present in an amount of from about 4 to about 6 parts by weight based on 100 parts by weight of said binder component.

7. The coating composition of claim 6 wherein the functionalized tri-alkoxy silane is gamma-glycidoxypropyltrimethoxysiliane.

8. The coating composition of claim 1 wherein the calcium ion-exchanged silica is present in an amount of from about 30 to about 35 parts by weight based on 100 parts by weight of said binder component.

9. The coating composition of claim 1 wherein the corrosion inhibiting pigment is present in an amount of from about 45 to about 50 parts by weight based on 100 parts by weight of said binder component.

10. The coating composition of claim 9 wherein the corrosion inhibiting pigment is Ca Sr Zn Phosphosilicate.

11. The coating composition of claim 1 wherein the polyalkylene oxide phosphate is present in an amount of from about 2 to about 5 parts by weight based on 100 parts by weight of said binder component.

12. The coating composition of claim 11 wherein the polyalkylene oxide phosphate is polyethylene oxide terminated with a phosphate group.

13. The coating composition of claim 1 consisting essentially of (A1)-(A4) and (B1)-(B3) wherein (A1) is present in an amount of about 60 to about 70 parts by weight based on 100 parts by weight of said binder component, (A2) is present in an amount of about 10 to about 20 parts by weight based on 100 parts by weight of said binder component, and/or (A3) is present in an amount of about 13 to about 20 parts by weight based on 100 parts by weight of said binder component.

14. The coating composition of claim 13 wherein:
the polyvinyl butyral is present in an amount of from about 60 to about 65 parts by weight based on 100 parts by weight of said binder component;
the film forming resin is present in an amount of from about 13 to about 17 parts by weight based on 100 parts by weight of said binder component;
the acid is phosphoric acid and is present in an amount of from about 13 to about 15 parts by weight based on 100 parts by weight of said binder component;
the functionalized tri-alkoxy silane is gamma-glycidoxypropyltrimethoxysiliane and is present in an amount of from about 3 to about 10 parts by weight based on 100 parts by weight of said binder component;
the calcium ion-exchanged silica is present in an amount of from about 30 to about 35 parts by weight based on 100 parts by weight of said binder component;
the corrosion inhibiting pigment is Ca Sr Zn Phosphosilicate and is present in an amount of from about 45 to about 50 parts by weight based on 100 parts by weight of said binder component; and
the polyalkylene oxide phosphate is polyethylene oxide terminated with a phosphate group and is present in an amount of from about 2 to about 5 parts by weight based on 100 parts by weight of said binder component.

15. The coating composition of claim 13 wherein:
the polyvinyl butyral is present in an amount of about 63 parts by weight based on 100 parts by weight of said binder component;
the film forming resin is present in an amount of about 16 parts by weight based on 100 parts by weight of said binder component;
the acid is phosphoric acid and is present in an amount of about 14 parts by weight based on 100 parts by weight of said binder component;
the functionalized tri-alkoxy silane is gamma-glycidoxypropyltrimethoxysiliane and is present in an amount of about 5 parts by weight based on 100 parts by weight of said binder component;
the calcium ion-exchanged silica is present in an amount of about 33 parts by weight based on 100 parts by weight of said binder component;
the corrosion inhibiting pigment is Ca Sr Zn Phosphosilicate and is present in an amount of about 46 parts by weight based on 100 parts by weight of said binder component; and
the polyalkylene oxide phosphate is polyethylene oxide terminated with a phosphate group and is present in an amount of about 2 parts by weight based on 100 parts by weight of said binder component.

16. The coating composition of claim 1 consisting of (A1)-(A4) and (B1)-(B3) wherein (A1) is present in an amount of about 60 to about 70 parts by weight based on 100 parts by weight of said binder component, (A2) is present in an amount of about 10 to about 20 parts by weight based on 100 parts by weight of said binder component, and/or (A3) is present in an amount of about 13 to about 20 parts by weight based on 100 parts by weight of said binder component.

17. The coating composition of claim 16 wherein:
the polyvinyl butyral is present in an amount of from about 60 to about 65 parts by weight based on 100 parts by weight of said binder component;
the film forming resin is present in an amount of from about 13 to about 17 parts by weight based on 100 parts by weight of said binder component;
the acid is phosphoric acid and is present in an amount of from about 12 to about 15 parts by weight based on 100 parts by weight of said binder component;
the functionalized tri-alkoxy silane is gamma-glycidoxypropyltrimethoxysiliane and is present in an amount of from about 3 to about 10 parts by weight based on 100 parts by weight of said binder component;
the calcium ion-exchanged silica is present in an amount of from about 30 to about 35 parts by weight based on 100 parts by weight of said binder component;
the corrosion inhibiting pigment is Ca Sr Zn Phosphosilicate and is present in an amount of from about 45 to about 50 parts by weight based on 100 parts by weight of said binder component; and
the polyalkylene oxide phosphate is polyethylene oxide terminated

Assignees

• Axalta Coating Systems Ip Co

Inventors

• Houze Eric
• Lothert Anja
• Bhargava Gaurang
• Wendt Martin
• Nahas Robert
• Harvey Iain

Classifications

• C09D129/14 Primary

  Homopolymers or copolymers of acetals or ketals obtained by polymerisation of unsaturated acetals or ketals or by after-treatment of polymers of unsaturated alcohols · CPC title

• C09D5/12

  Wash primers · CPC title

• C09D7/61

  inorganic · CPC title

• C08K3/36

  Silica · CPC title

• C08K2003/329

  Phosphorus containing acids · CPC title