Method of preparing abs graft copolymer and method of preparing thermoplastic resin composition

Patent metadata

Field	Value
Publication number	US-11820849-B2
Application number	US-201916630830-A
Country	US
Kind code	B2
Filing date	Feb 14, 2019
Priority date	Feb 26, 2018
Publication date	Nov 21, 2023
Grant date	Nov 21, 2023

Abstract

The present invention relates to a method of preparing an ABS graft copolymer and a method of preparing a thermoplastic resin composition including the ABS graft copolymer. More specifically, the present invention relates to a method of preparing an ABS graft copolymer, in which a predetermined amount of a vinyl aromatic compound and a predetermined amount of a vinyl cyanide compound are grafted to a small-diameter rubber latex before enlarging particle size of the small-diameter rubber latex is performed, and then enlarging particle size of the small-diameter rubber latex is performed by adding a certain amount of a polymer coagulant, and to a method of preparing a thermoplastic resin composition including the ABS graft copolymer. According to the present invention, latex stability may be improved, and an ABS graft copolymer having excellent impact resistance may be prepared.

First claim

The invention claimed is:

1. A method of preparing an ABS graft copolymer, comprising:
a first graft polymerization step of grafting 4 to 15% by weight of vinyl monomers to 20 to 70% by weight of a conjugated diene rubber latex;
a latex coagulation step of enlarging particle size of the rubber latex by adding a polymer coagulant after the first graft polymerization step;
a latex stabilization step of stabilizing the rubber latex having the enlarged particle size by adding a pH adjusting agent after the latex coagulation step; and
a second graft polymerization step of grafting 25 to 75% by weight of the vinyl monomers to the rubber latex having the enlarged particle size, after the latex stabilization step,
wherein the polymer coagulant is added in an amount of 1 to 4 parts by weight based on 100 parts by weight in total of the conjugated diene rubber latex and the vinyl monomers;
the vinyl monomers comprise a vinyl aromatic compound and a vinyl cyanide compound; and
the rubber latex which the particle size is enlarged has an average particle diameter of 2,800 to 5,000 Å.

2. The method according to claim 1 , wherein the polymer coagulant is a copolymer prepared by polymerizing an unsaturated acid compound.

3. The method according to claim 1 , wherein the polymer coagulant is a copolymer having a core-shell structure.

4. The method according to claim 3 , wherein the copolymer having a core-shell structure comprises 30 to 55% by weight of a core and 45 to 70% by weight of a shell.

5. The method according to claim 3 , wherein the shell comprises an unsaturated acid compound.

6. The method according to claim 5 , wherein the shell comprises 10 to 20% by weight of an unsaturated acid compound and 80 to 90% by weight of a (meth)acrylic acid alkyl ester.

7. The method according to claim 3 , wherein the core comprises a (meth)acrylic acid alkyl ester.

8. The method according to claim 7 , wherein the core further comprises an unsaturated acid compound.

9. The method according to claim 3 , wherein the polymer coagulant comprises 30 to 55% by weight of a core prepared by polymerizing 90 to 100% by weight of a (meth)acrylic acid alkyl ester and 0 to 10% by weight of an unsaturated acid compound; and 45 to 70% by weight of a shell surrounding the core and prepared by polymerizing 80 to 90% by weight of a (meth)acrylic acid alkyl ester and 10 to 20% by weight of an unsaturated acid compound.

10. The method according to claim 1 , wherein the polymer coagulant has an average particle diameter of 800 to 1,500 Å.

11. The method according to claim 1 , wherein the conjugated diene rubber latex has an average particle diameter of 800 to 1,500 Å.

12. A method of preparing a thermoplastic resin composition, comprising performing the method according to claim 1 to prepare the ABS graft copolymer; and
kneading and extruding 20 to 80% by weight of the ABS graft copolymer and 20 to 80% by weight of a non-graft resin.

Assignees

• Lg Chemical Ltd

Inventors

• Jeon Heejung
• Kim Geon Soo
• Kim Changhoe
• Kim Hyung Joon
• Chae Minsu

Classifications

• C08F279/04 Primary

  Vinyl aromatic monomers and nitriles as the only monomers · CPC title

• C08F2/22

  Emulsion polymerisation · CPC title

• C08F6/18

  Increasing the size of the dispersed particles · CPC title

• C08F6/22 Primary

  Coagulation · CPC title

• C08F285/00

  Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers · CPC title