Abstract

A process for forming mineral fibers by internal centrifugation using a device including a basket and a fiberizing spinner suitable for rotating jointly about an axis of rotation, the basket including an annular wall pierced by orifices and the fiberizing spinner including an annular wall pierced by orifices, the process including feeding the basket with material to be fiberized at a temperature Ta; centrifuging the material to be fiberized by joint rotation of the basket and of the fiberizing spinner. The factor F is greater than 2000, the factor F being defined by F=μadN/Q; wherein μa is the viscosity of the material to be fiberized at the temperature Ta; d is the distance between the annular walls of the basket and of the fiberizing spinner; N is the number of orifices of the basket; and Q is the feed flow rate of the material to be fiberized.

First claim

The invention claimed is:

1. A process for forming mineral wool by internal centrifugation using a device comprising a basket and a fiberizing spinner which are suitable for rotating jointly about an axis of rotation, the basket comprising an annular wall pierced by a plurality of orifices and the fiberizing spinner comprising an annular wall pierced by a plurality of orifices, said process comprising:
feeding the basket with material to be fiberized at a temperature T a ;
centrifuging the material to be fiberized by joint rotation of the basket and of the fiberizing spinner,

wherein a factor F is greater than 2000, the factor F being defined by

F
=

μ
a

⁢
d
⁢
N

Q

,

wherein:
μ a is the viscosity, expressed in Pa·s, of the material to be fiberized at the temperature T a ;
d is the distance, expressed in m, between the annular wall of the basket and the annular wall of the fiberizing spinner;
N is the number of orifices of the basket; and
Q is the feed flow rate, expressed in kg/s, of the material to be fiberized, and
wherein the annular wall of the basket comprises from 220 to 1,000 orifices.

2. The process as claimed in claim 1 , wherein the viscosity of the material to be fiberized at the temperature T a is from 50 to 150 Pa·s.

3. The process as claimed in claim 1 , wherein the distance between the annular wall of the basket and the annular wall of the fiberizing spinner is from 0.05 to 0.2 m.

4. The process as claimed in claim 1 , wherein the feed flow rate of the material to be fiberized is from 0.01 to 0.5 kg/s.

5. The process as claimed in claim 1 , wherein the material to be fiberized comprises the constituents below, in the weight proportions defined by the following limits:

SiO 2
35 to 80%, 

Al 2 O 3
0 to 30%,

CaO + MgO
2 to 35%,

Na 2 O + K 2 O
0 to 20%.

6. The process as claimed in claim 5 , wherein the material to be fiberized is fed into the basket at a temperature of from 1000 to 1550° C.

7. The process as claimed in claim 1 , wherein the factor F is greater than 5000.

8. The process as claimed in claim 7 , wherein the factor F is greater than 10000.

9. A process for forming mineral wool by internal centrifugation using a device comprising a basket and a fiberizing spinner which are suitable for rotating jointly about an axis of rotation, the basket comprising an annular wall pierced by a plurality of orifices and the fiberizing spinner comprising an annular wall pierced by a plurality of orifices, said process comprising:
feeding the basket with material to be fiberized at a temperature T a ;
centrifuging the material to be fiberized by joint rotation of the basket and of the fiberizing spinner,

wherein a factor F is greater than 2000, the factor F being defined by F=μ a dN/Q, wherein:
μ a is the viscosity, expressed in Pa·s, of the material to be fiberized at the temperature T a ;
d is the distance, expressed in m, between the annular wall of the basket and the annular wall of the fiberizing spinner;
N is the number of orifices of the basket; and
Q is the feed flow rate, expressed in kg/s, of the material to be fiberized,
wherein the orifices of the annular wall of the basket have a diameter of from 1.5 to 3 mm, and
wherein the annular wall of the basket comprises from 220 to 1,000 orifices.

Assignees

• Saint Gobain Isover

Inventors

• Brogniez Sébastien
• Guery Guillaume

Classifications

• C03B37/045 Primary

  Construction of the spinner cups · CPC title

• D01D5/18

  by means of rotating spinnerets · CPC title

• D01D7/02

  in centrifugal spinning pots · CPC title

• D10B2101/06

  Glass · CPC title

• D10B2401/20

  optical · CPC title