Abstract

The present invention relates to a process for the production of metal alloy nanoparticles which catalyse the oxygen reduction reaction (ORR) for use in proton exchange membrane fuel cells (PEMFC) or electrolyser cells. In particular, the present invention relates to a process for producing alloy nanoparticles from platinum group metals and other metals under reductive conditions. In particular the present invention relates to a process for producing alloy nanoparticles comprising the steps of mixing a salt of at least one metal, a material comprising a platinum group metal, a nitrogen-rich compound, and optionally a support material, to provide a precursor mixture, and heating said precursor mixture to a temperature of at least 400° C., in the presence of a gas comprising hydrogen (H 2 ), to provide said alloy nanoparticles.

First claim

The invention claimed is:

1. A process for producing alloy nanoparticles comprising:
a) mixing:
a salt of at least one first metal selected from the group consisting of alkaline earth metals, transition metals, and lanthanides, or mixtures thereof,
a material comprising gold (Au),
a nitrogen-rich organic compound, and
a support material,

to provide a precursor mixture,
b) heating said precursor mixture to a temperature of at least 400° C., in the presence of a gas comprising hydrogen (H 2 ), to provide said alloy nanoparticles,
wherein the nitrogen-rich organic compound has a chemical formula with a stoichiometric ratio between carbon to nitrogen of 6:1-1:4 and,
wherein the material comprising gold (Au) is selected from the group consisting of a salt of gold, and nanoparticles of gold on the support material.

2. The process according to claim 1 , wherein the process further comprises:
c) contacting said alloy nanoparticles with a solution comprising an acid to further purify said alloy nanoparticles.

3. The process according to claim 2 , wherein the acid of step c) is an inorganic acid.

4. The process according to claim 3 , wherein the inorganic acid is selected from the group consisting of sulphuric acid (H 2 SO 4 ), hydrochloric acid (HCl), hydrofluoric acid (HF), nitric acid (HNO 3 ) and phosphoric acid (H 3 PO 4 ).

5. The process according to claim 1 , wherein the at least one first metal is selected from the group consisting of a rare earth metal, nickel (Ni), zirconium (Zr), copper (Cu) and cobalt (Co), or a mixture thereof.

6. The process according to claim 5 , wherein the rare earth metal is selected from the group consisting of cerium (Ce), dysprosium (Dy), erbium (Er), europium (Eu), gadolinium (Gd), holmium (Ho), lanthanum (La), lutetium (Lu), neodymium (Nd), praseodymium (Pr), promethium (Pm), samarium (Sm), scandium (Sc), terbium (Tb), thulium (Tm), ytterbium (Yb), and yttrium (Y).

7. The process according to claim 1 , wherein the salt of at least one first metal is selected from the group consisting of GdCl 3 , GdBr 3 , GdI 3 , TbCl 3 , YCl 3 , and NiCl 2 , or a mixtures thereof.

8. The process according to claim 1 , wherein the support material is based on materials selected from the group consisting of carbon, alumina, silica, and titanium oxide, or combinations thereof.

9. The process according to claim 1 , wherein the nitrogen-rich organic compound has a chemical formula with a stoichiometric ratio between carbon to nitrogen of 2:1-1:2.

10. The process according to claim 1 , wherein the nitrogen-rich organic compound is a compound selected from the group consisting of cyanamide (NH 2 CN), dicyandiamide ((H 2 N) 2 C═NCN), melamine (C 3 H 6 N 6 ), carbon nitrides, ethylenediamine (C 2 H 8 N 2 ), 1,10-phenanthroline (C 12 H 8 N 2 ), histidine (C 6 H 9 N 3 O 2 ), 2,2′-bipyridine (C 10 H 8 N 2 ), 2,5-dimethylpyrrole (C 6 H 9 N), maleimide (C 4 H 3 NO 2 ), imidazole (C 3 H 4 N 2 ), polyacrylonitrile (C 3 H 3 N), and thiourea (CH 4 N 2 S).

11. The process according to claim 1 , wherein the heating of the precursor of step b) is performed at a temperature of 400-1000° C.

12. The process according to claim 1 , wherein the salt of at least one first metal is a halogen salt.

13. The process according to claim 1 , wherein the process is performed in the absence of an organic solvent.

14. A process for producing alloy nanoparticles comprising:
a) mixing:
a salt of at least one first metal selected from the group consisting of alkaline earth metals, transition metals, and lanthanides, or mixtures thereof,
a material comprising a platinum group metal selected from the group consisting of ruthenium (Ru), rhodium (Rh), palladium (Pd), Osmium (Os), iridium (Ir) and platinum (Pt), or a material comprising gold (Au),
a nitrogen-rich organic compound, and
a support material,

to provide a precursor mixture,
b) heating said precursor mixture to a temperature of at least 400° C., in the presence of a gas comprising hydrogen (H 2 ), to provide said alloy nanoparticles, wherein the nitrogen-rich organic compound has a chemical formula with a stoichiometric ratio between carbon to nitrogen of 6:1-1:4 and, wherein the nitrogen-rich organic compound is a compound selected from the group consisting of cyanamide (NH 2 CN), dicyandiamide ((H 2 N) 2 C═NCN), melamine (C 3 H 6 N 6 ), carbon nitrides, ethylenediamine (C 2 H 8 N 2 ), 1,10-phenanthroline (C 12 H 8 N 2 ), histidine (C 6 H 9 N 3 O 2 ), 2,2′-bipyridine (C 10 H 8 N 2 ), 2,5-dimethylpyrrole (C 6 H 9 N), maleimide (C 4 H 3 NO 2 ), imidazole (C 3 H 4 N 2 ), polyacrylonitrile (C 3 H 3 N), and thiourea (CH 4 N 2 S).

15. The process according to claim 14 , wherein the process further comprises:
c) contacting said alloy nanoparticles with a solution comprising an acid to further purify said alloy nanoparticles.

16. The process according to claim 15 , wherein the acid of step c) is an inorganic acid.

17. The process according to claim 16 , wherein the inorganic acid is selected from the group consisting of sulphuric acid (H 2 SO 4 ), hydrochloric acid (HCl), hydrofluoric acid (HF), nitric acid (HNO 3 ) and phosphoric acid (H 3 PO 4 ).

18. The process according to claim 14 , wherein the at least one first metal is selected from the group consisting of a rare earth metal, nickel (Ni), zirconium (Zr), copper (Cu) and cobalt (Co), or a mixture thereof.

19. The process according to claim 18 , wherein the rare earth metal is selected from the group consisting of cerium (Ce), dysprosium (Dy), erbium (Er), europium (Eu), gadolinium (Gd), holmium (Ho), lanthanum (La), lutetium (Lu), neodymium (Nd), praseodymium (Pr), promethium (Pm), samarium (Sm), scandium (Sc), terbium (Tb), thulium (Tm), ytterbium (Yb), and yttrium (Y).

20. The process according to claim 14 , wherein the salt of at least one first metal is selected from the group consisting of GdCl 3 , GdBr 3 , GdI 3 , TbCl 3 , YCl 3 , and NiCl 2 , or a mixtures thereof.

21. The process according to claim 14 , comprising mixing a material comprising a platinum group metal, wherein the material comprising a platinum group metal is selected from the group consisting of a platinum group metal, a salt of a platinum group metal, and nanoparticles of a platinum group metal on a support material.

22. The process according to claim 14 , comprising mixing a material comprising gold, wherein the material comprising gold (Au) is selected from the group consisting of a salt of gold, and nanoparticles of gold on a support material.

23. The process according to claim 14 , wherein the support material is based on materials selected from the group consisting of carbon, alumina, silica, and titanium oxide, or combinations thereof.

24. The process according to claim 14 , wherein the nitrogen-rich organic compound has a chemical formula with a stoichiometric ratio between carbon to nitrogen of 2:1-1:2.

25. The process according to claim 14 , wherein the heating of the precursor of step b) is performed at a temperature of 400-1000° C.

26. The process according to claim 14 , wherein the salt of at least one first metal is a halogen salt.

27. The process according to claim 14 , wherein the process is performed in the absence of an organic solvent.

28. A process for producing alloy nanoparticles comprising:
a) mixing:
a salt of at least one first metal selected from the group cons

Assignees

• Univ Danmarks Tekniske

Inventors

• Li Qingfeng
• Brandes Benedikt Axel
• Jensen Jens Oluf
• Cleeman Lars Nilausen
• Hu Yang

Classifications

• C22C5/02

  Alloys based on gold · CPC title

• B01J23/10

  of rare earths · CPC title

• B01J23/02

  of the alkali- or alkaline earth metals or beryllium · CPC title

• B01J23/52

  Gold · CPC title

• B01J23/40

  of the platinum group metals · CPC title