Method for forming cutters

Patent metadata

Field	Value
Publication number	US-11794290-B2
Application number	US-202117156592-A
Country	US
Kind code	B2
Filing date	Jan 24, 2021
Priority date	Jan 24, 2021
Publication date	Oct 24, 2023
Grant date	Oct 24, 2023

Abstract

The method for forming cutters includes applying a protective layer on an O-ring so as to form a protected O-ring. The protected O-ring is placed around a cutter body having a substrate section and diamond section with a metallic binder. The method includes inserting the cutter body into the pod cavity and leaching the metallic binder through an end portion of the diamond section for at least one day at 60 degrees Celsius or higher so as to form a polycrystalline diamond compact cutter from the cutter body. The protected O-ring seals the substrate section during the step of leaching. The step of leaching forms an exposed O-ring from the protected O-ring with a hardness reduction and a modulus reduction that identifies a time window for maintaining a sealing force to protect the substrate, while achieving the target profile of the diamond table for a high quality and reliable cutter.

First claim

We claim:

1. A method for forming cutters, the method comprising the steps of:
setting a back cap into a pod so as to form an assembly with a pod cavity;
applying a protective layer on an O-ring so as to form a protected O-ring,
wherein said O-ring is comprised of at least one of a group consisting of: nitrile butadiene rubber (NBR), hydrogenated nitrile butadiene rubber (HNBR), Ethylene-propylene diene monomer (EPDM), Epichlorohydrin (ECO), Polyacrylic rubber (ACM), Fluorosilicone rubber (FVMQ), Fluoroelastomers (FKM), Copolymer of tetrafluoroethylene and propylene (FEPM), perfluoroelastomer (FFKM), and Silicone rubber;
placing said protected O-ring around a cutter body, said cutter body being comprised of: a substrate section, and diamond section being comprised of a metallic binder;
inserting said cutter body into said pod cavity so as to seal said substrate section within said pod,
wherein said diamond section is comprised of an end portion extending outward from said pod, said end portion being sealed to said substrate section by said protected O-ring; and
leaching said metallic binder through said end portion of said diamond section for at least 1 day at 60 degrees Celsius or higher so as to form a polycrystalline diamond compact cutter from said cutter body and an exposed O-ring from said protected O-ring, said exposed O-ring having a hardness reduction relative to said protected O-ring, said exposed O-ring having a modulus reduction relative to said protected O-ring.

2. The method, according to claim 1 , wherein said hardness reduction relative to said protected O-ring is less than a hardness reduction of an exposed unprotected O-ring relative to an unprotected O-ring.

3. The method, according to claim 1 , wherein said modulus reduction relative to said protected O-ring is less than a modulus reduction of an exposed unprotected O-ring relative to an unprotected O-ring.

4. The method, according to claim 1 , wherein said step of applying said protective layer is comprised of the steps of:
coating a poly (para-xylene) on said O-ring so as to form a coated layer as said protective layer, said coated layer having a thickness of at least 1 micrometer.

5. The method, according to claim 4 , wherein said coated layer has a thickness between 1-5 micrometers.

6. The method, according to claim 4 , wherein said poly (para-xylene) is comprised of at least one of a group consisting of:

7. The method, according to claim 4 , wherein said step of leaching said metallic binder is for 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said hardness reduction relative to said protected O-ring less than 20%.

8. The method, according to claim 7 , wherein said step of leaching said metallic binder is for 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said modulus reduction relative to said protected O-ring less than 90%.

9. The method, according to claim 4 , wherein said step of leaching said metallic binder is for 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said modulus reduction relative to said protected O-ring less than 90%.

10. The method, according to claim 4 , wherein said step of leaching said metallic binder is for 1 day at 60 degrees Celsius or higher, said exposed O-ring having said modulus reduction relative to said protected O-ring less than 60%.

11. The method, according to claim 1 , wherein said step of applying said protective layer is comprised of the steps of:
coating a fluoropolymer on said O-ring so as to form a fluoro-coated layer as said protective layer, said fluoro-coated layer having a thickness with a range of 1-5 micrometers,
wherein said fluoropolymer is comprised of at least one of a group consisting of: polytetrafluoroethylene (PTFE), perfluoroalkoxy (PFA), ethylenetetrafluoroethylene (ETFE), polychlorotrifluoroethylene (PCTFE), polyvinylidenefluoride (PVDF), fluorinated ethylene propylene copolymer (FEP), and ethylene chlorotrifluoroethylene (ECTFE).

12. The method, according to claim 11 , where the step of coating said fluropolymer is comprised of the steps of:
applying said fluoropolymer by liquid suspension on a surface of said O-ring;
drying said fluoro-coated layer so as to remove water; and
heating said fluro-coated layer and said O-ring.

13. The method, according to claim 11 , where the step of coating said fluropolymer is comprised of the steps of:
melt-coating said fluoropolymer on said O-ring.

14. The method, according to claim 1 , wherein said step of applying said protective layer is comprised of the steps of:
fluorinating a surface of said O-ring so as to form a fluorination layer as said protective layer, said fluorination layer having a thickness with a range of 2-4 micrometers.

15. The method, according to claim 14 , wherein said step of leaching said metallic binder is for 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said hardness reduction relative to said protected O-ring less than 20%.

16. The method, according to claim 1 , wherein said step of applying said protective layer is comprised of the steps of:
encapsulating said O-ring with an encapsulated fluoropolymer so as to form an encapsulated layer as said protective layer, said encapsulated layer having a thickness with a range of 1-20 micrometers,
wherein said encapsulated fluoropolymer is comprised of at least one of a group consisting of: polytetrafluoroethylene (PTFE), perfluoroalkoxy (PFA), ethylenetetrafluoroethylene (ETFE), polychlorotrifluoroethylene (PCTFE), polyvinylidenefluoride (PVDF), fluorinated ethylene propylene copolymer (FEP), and ethylene chlorotrifluoroethylene (ECTFE).

17. The method, according to claim 16 , wherein said step of leaching said metallic binder is for 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said hardness reduction less than 5%.

18. The method, according to claim 17 , wherein said step of leaching said metallic binder is 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said modulus reduction less than 20%.

19. The method, according to claim 16 , wherein said step of leaching said metallic binder is 1-3 days at 60 degrees Celsius or higher, said exposed O-ring having said modulus reduction less than 20%.

20. The method, according to claim 1 , wherein said pod is comprised of at least one of a group consisting of: polytetrafluoroethylene (PTFE), perfluoroalkoxy (PFA), ethylenetetrafluoroethylene (ETFE), polychlorotrifluoroethylene (PCTFE), polyvinylidenefluoride (PVDF), fluorinated ethylene propylene copolymer (FEP), and ethylene chlorotrifluoroethylene (ECTFE).

Assignees

• Cnpc Usa Corp
• Beijing Huamei Inc

Inventors

• Ren Jiaxiang
• Cheng Chris

Classifications

• B23P15/28 Primary

  cutting tools (sawing tools B23D63/00, B23D65/00; files or rasps B23D73/00) · CPC title

• E21B10/567

  with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts · CPC title

• F16J15/3284

  characterised by their structure; Selection of materials · CPC title

• B22F3/24 Primary

  After-treatment of workpieces or articles {(B22F3/1146 takes precedence)} · CPC title

• F16J15/102 Primary

  characterised by material · CPC title