Glass element comprising enamel coating and use thereof, coating agent for making same, and method for producing the coating agent

Patent metadata

Field	Value
Publication number	US-11780770-B2
Application number	US-202117468900-A
Country	US
Kind code	B2
Filing date	Sep 8, 2021
Priority date	Sep 8, 2020
Publication date	Oct 10, 2023
Grant date	Oct 10, 2023

Abstract

Glass elements are provided that include a coating and a sheet-like glass substrate. The sheet-like glass substrate has a first surface and a second surface opposite the first surface. The coating is disposed in at least some areas of at least one of the first and second surfaces. The coating is an inorganic glass-based coating that includes at least one glassy component; at least one pigment comprising pigment particles; and a filler. The filler is inorganic and includes filler particles with a d50 value, based on an equivalent diameter, of at least 0.1 μm and less than 10 μm.

First claim

What is claimed is:

1. A glass element, comprising:
a sheet-like glass substrate having a first surface and a second surface opposite the first surface; and
a coating disposed in at least some areas of at least one of the first and second surfaces,
wherein the coating is an inorganic glass-based coating that comprises:
glassy component;
a second glassy component
at least one pigment comprising pigment particles; and
a filler, the filler being inorganic and comprising filler particles with a d 50 value, based on an equivalent diameter, of at least 0.1 μm and less than 10 μm,

wherein the coating has a coefficient of thermal expansion that is less than or equal to a coefficient of thermal expansion of the glass substrate,
wherein the coating has a glass matrix that has two glassy phases with different compositions and is inhomogeneous, and
wherein the glass substrate comprises a soda-lime glass or is made from soda-lime glass.

2. The glass element of claim 1 , wherein the inorganic glass-based coating is an enamel coating.

3. The glass element of claim 1 , wherein the filler particles and/or the second glassy component have a coefficient of thermal expansion of at least 0.5*10 −6 /K and at most 15*10 −6 /K so that a resulting coefficient of thermal expansion of the coating is at least 6*10 −6 /K and at most 9*10 −6 /K.

4. The glass element of claim 3 , further comprising a difference in the coefficients of thermal expansion of the glass substrate and the coating that is between at least 0.5*10 −6 /K and at most 3.1*10 −6 /K.

5. The glass element of claim 4 , further comprising a color location, in an area where the coating is disposed, with an L* value of more than 60 and an optical density of more than 1 or with an L* value of less than 60 and an optical density of more than 2.

6. The glass element of claim 1 , wherein the glassy component comprises, in wt %, on an oxide basis:
SiO 2 30-75;
Al 2 O 3 0-25;
B 2 O 3 0-30;
Li 2 O 0-12;
Na 2 O 0-25;
CaO 0-12;
MgO 0-9;
BaO 0-27;
SrO 0-4;
ZnO 0-35;
Bi 2 O 3 0-5;
TiO 2 0-10;
ZrO 2 0-7;
As 2 O 3 0-1;
Sb 2 O 3 0-1.5;
F 0-3;
Cl 0-1; and
H 2 O 0-3.

7. The glass element of claim 1 , wherein the glassy component comprises, in wt %, on an oxide basis:
SiO 2 6-65;
Al 2 O 3 0-20;
B 2 O 3 0-40;
Li 2 O 0-12;
Na 2 O 0-18;
K 2 O 0-17;
CaO 0-17;
MgO 0-12;
BaO 0-38;
SrO 0-16;
ZnO 0-70;
TiO 2 0-10;
ZrO 2 0-5;
Bi 2 O 3 0-75;
CoO 0-5;
Fe 2 O 3 0-5;
MnO 0-10;
CeO 2 0-3;
F 0-3;
Cl 0-1; and
H 2 O 0-3.

8. The glass element of claim 1 , further comprising a breaking strength as determined in a ball drop test conducted according to DIN 52306 of at least 70 cm measured on the glass element with a thickness of 4 mm.

9. The glass element of claim 1 , wherein the filler particles comprise SiO 2 and/or Al 2 O 3 .

10. The glass element of claim 1 , wherein the coating has a pattern such that one area of the first or second surface on which the coating is disposed has no coating and another area has the coating.

11. The glass element of claim 1 , wherein the pattern is selected from a group consisting of a raster pattern, a dot raster pattern, and a frame pattern.

12. The glass element of claim 1 , wherein the coating covers at least one of the first and second surfaces with a degree of coverage between 60% and 90%.

13. The glass element of claim 1 , further comprising a thickness between 3 mm and 10 mm.

14. The glass element of claim 1 , wherein the coating has a thickness of up to 20 μm and at least 1 μm.

15. The glass element of claim 1 , wherein the glass element is sized and configured for a use selected from a group consisting of a control panel, a viewing window, a viewing window in a baking oven door, a viewing window in a washing machine door, a viewing window in a washing machine lid, a viewing window in laundry dryer door, a viewing window in laundry dryer lid, a cooking surface cover panel, a shelf, a refrigerator shelf, a viewing window in a fireplace, a viewing window in an oven, an opaque cover plate, and an opaque front panel of an appliance.

16. A coating agent for producing a glass-based inorganic coating on a glass substrate, comprising:
solid components; and
at least one liquid component, wherein the solid components comprise at least a first and a second glassy component, at least one pigment comprising pigment particles, and at least one filler comprising filler particles, wherein the filler is inorganic and comprises filler particles having a d 50 value, based on an equivalent diameter, between at least 0.1 μm and less than 10 μm; and
wherein the coating results in a glass matrix that has two inhomogeneous glassy phases with different compositions and a coefficient of thermal expansion that is less than or equal to a coefficient of thermal expansion of the glass substrate.

17. The coating agent of claim 16 , further comprising a feature selected from a group consisting of: a ratio of a total of the solid components to a total of at least one liquid component between 2 and 3.5 based on weight; a ratio of a total of the solid components to a total of at least one liquid component between 2.2 and 3.1 based on weight; a fraction of the glassy component among a total content of the solid components between 58 vol % and 78 vol %; a fraction of the at least one pigment among a total content of the solid components between 5 vol % and 35 vol %; a fraction of the at least one pigment among a total content of the solid components between 5 vol % and 21 vol %; a fraction of the filler among a total content of solid components between 0.01 vol % and 60 vol %; a fraction of the filler among a total content of solid components between 0.01 vol % and 35 vol %; a fraction of the filler among a total content of solid components between 0.01 vol % and 19 vol %; and a fraction of the filler among a total content of solid components between 0.01 vol % and 15 vol %.

18. A method for producing a coating agent, comprising;
providing a coating agent comprising a first glassy component, a second glassy component, a filler comprising filler particles, and at least one pigment comprising pigment particles;
defining a resulting coefficient of thermal expansion of the coating obtained from the coating agent on a substrate by firing to provide a glass matrix that has two glassy phases;
calculating a volume fraction of the filler and of the second glassy component in the coating agent;
adding the filler and the second glassy component to the coating agent according to the calculated volume fraction; and
dispersing the filler and the second glassy component in the coating agent.

19. The method of claim 18 , wherein the first and second glassy components have different compositions.

Assignees

• Schott Ag

Inventors

• Krechel Ricarda
• Steigenberger Vera
• Schwall Michael
• Caldwell Daniel
• Neitzel Ioannis
• Nattermann Kurt

Classifications

• C03C17/04 Primary

  by fritting glass powder · CPC title

• C03C3/078

  containing an oxide of a divalent metal, e.g. an oxide of zinc · CPC title

• C03C8/04

  containing zinc · CPC title

• C03C8/06

  containing halogen · CPC title

• C03C8/08

  containing phosphorus · CPC title