Composite particles having coated aggregates with low structure carbon black cores, coatings and inks with high resistivity and optical density, devices made therewith, and methods for making same

Patent metadata

Field	Value
Publication number	US-11773269-B2
Application number	US-202017004772-A
Country	US
Kind code	B2
Filing date	Sep 10, 2020
Priority date	Jul 1, 2016
Publication date	Oct 3, 2023
Grant date	Oct 3, 2023

Abstract

Composite particles that super-aggregates of coated aggregates having low structure carbon black cores and metal/metalloid oxide mantles are described. Coatings containing filler-polymer compositions which have the composite particles as filler, such as curable coatings and cured coatings or films formed therefrom containing the filler-polymer compositions, with combinations of high resistivity, good optical density properties, good thermal stability, high dielectric constant, and good processability, along with their use in black matrices, black column spacers, light shielding elements in LCDs and other display devices, also are described. Inks containing the composite particle are described. Devices having these compositions, components and/or elements, and methods of preparing and making these various materials and products are described.

First claim

What is claimed is:

1. A method of making carbon black-metal/metalloid oxide composite particles, comprising:
forming a stream of combustion gases by reacting a preheated air stream with a fuel;
introducing first feedstock into the stream of combustion gases at a predetermined number of points arranged in a first ring pattern that is defined around the stream of combustion gases to form a reaction stream and start pyrolysis of the first feedstock in the reaction stream, wherein the first feedstock comprises carbon black-yielding feedstock;
introducing an auxiliary hydrocarbon into the stream of combustion gases at a predetermined number of points arranged in a second ring pattern that is defined around the stream of combustion gases, wherein the first and second ring patterns may be located at a same location or different locations;
additionally introducing into at least one of the stream of combustion gases or the reaction stream or any combinations thereof at least one substance containing at least one Group IA element or Group IIA element or any combinations thereof;
allowing carbon black aggregates to form in the reaction stream, thereby forming carbon black aggregates suspended in the reaction stream, wherein the carbon black aggregates having external surfaces;
introducing a second feedstock comprising at least one of metal containing compound or metalloid-containing compound or any combinations thereof into the reaction stream in which the carbon black aggregates are suspended, the reaction stream having sufficient temperature to decompose the at least one metal-containing compound or metalloid-containing compound or any combinations thereof, wherein the decomposed at least one metal-containing compound or metalloid-containing compound or any combinations thereof form a shell comprising metal oxide or metalloid oxide or any combinations thereof about at least a portion of the external surfaces of the carbon black aggregates to form at least partially coated carbon black aggregates; and
allowing the at least partially coated carbon black aggregates to fuse together to form composite particles before quenching the pyrolysis, wherein the at least one metal oxide or metalloid oxide or any combinations thereof is at least 30% by surface area of the exposed outer surface area of the composite particles, and wherein the composite particles have a ratio of BET (m 2 /g)/iodine number (mg/g) of from 2 to 5.

2. The method of claim 1 , further comprising introducing the second feedstock into the reaction stream at a second injection location in a reactor that is a sufficient distance downstream from a first injection location where the introducing of the first feedstock into the stream of combustion gases is completed, wherein the reaction stream having a first average reaction temperature at the first injection location which is greater than a second average reaction temperature at the second injection location with the second average reaction temperature sufficient for decomposition of the at least one metal-containing compound or metalloid-containing compound or any combinations thereof.

3. The method of claim 1 , further comprising introducing the second feedstock into the reaction stream at a second injection location in a reactor that is 150 cm or more downstream from a first injection location where the introducing of the first feedstock into the stream of combustion gases is completed.

4. The method of claim 1 , further comprising introducing the second feedstock into the reaction stream at a second injection location in a reactor which occurs at least 30 milliseconds after the introducing of the first feedstock into the stream of combustion gases is completed at a first injection location, wherein this residence time is defined by the total gas volume of the flow after the first injection location and the volume of the reactor between the first and second injection locations.

5. The method of claim 1 , wherein the second feedstock consists essentially of at least one silicon-containing compound.

6. The method of claim 1 , wherein the second feedstock consists of a silicon-containing compound or silicon-containing compounds.

7. The method of claim 1 , wherein the carbon black aggregates suspended in the reaction stream have an OAN of from 30 to 50 cc/100 g, measured after hydrofluoric acid treatment of the coated carbon black aggregates to leave residual metal or metalloid oxide coating of less than 1 wt %.

8. The method of claim 1 , wherein the at least partially coated carbon black aggregates comprise a carbon core and a metal/metalloid oxide-containing shell.

Assignees

• Cabot Corp

Inventors

• Korchev Andriy
• Moeser Geoffrey D
• Pierre Danny
• Ni Qian
• Villalpando-Paez Federico

Classifications

• C09C1/50 Primary

  Furnace black {; Preparation thereof (separation or recovery C09C1/487)} · CPC title

• C09C1/56

  Treatment of carbon black {; Purification} · CPC title

• G02F1/133512

  Light shielding layers, e.g. black matrix (G02F1/136209 takes precedence) · CPC title

• C01P2004/80

  Particles consisting of a mixture of two or more inorganic phases · CPC title

• C01P2006/10

  Solid density · CPC title