Steel material exhibiting high toughness, method for manufacturing the same, and structural steel plate fabricated using steel material

Patent metadata

Field	Value
Publication number	US-11767582-B2
Application number	US-201816760950-A
Country	US
Kind code	B2
Filing date	Nov 8, 2018
Priority date	Nov 10, 2017
Publication date	Sep 26, 2023
Grant date	Sep 26, 2023

Abstract

The present invention provides a steel material which has a plate shape and achieves both high strength and high rigidity by imparting large nonuniform deformation to the steel material utilizing rolling using a large-diameter work roll. The steel plate according to an embodiment of the present invention is produced by performing rolling using a rolling mill having a work roll diameter of 650 mm or more in a warm temperature region so that a nonuniform metallographic structure is formed in a plate thickness direction and thus the steel plate of the present invention is a high-strength and high-rigidity steel plate in which a yield strength is 580 MPa or more and a Young's modulus at a plate thickness center portion or a surface layer portion is 210 GPa or more and a difference in Young's moduli at the plate thickness center portion and the surface layer portion is 5 GPa or more in a case in which a tensile direction in a tensile test is at least any one of a rolling direction, a plate width direction, or a direction forming an angle difference of 45 degrees from the rolling direction and the plate width direction.

First claim

The invention claimed is:

1. A steel plate consisting of
0.05% to 0.4% by mass of C,
1.65% by mass or less of Mn,
0.55% by mass or less of Si,
0.040% by mass or less of P, and
0.30% by mass or less of S,
with the balance being Fe and inevitable impurities, wherein
an average grain size of a metallographic structure at a plate thickness center portion is in a range of 0.8 μm to 2.0 μm, an average grain size of metallographic structure at a surface layer portion is in a range of 0.3 μm to 2.0 μm, and
an estimated value of Young's modulus obtained according to the following formula at a plate thickness center portion or a surface layer portion is 210 GPa or more:
(estimated value of Young's modulus)= f 001 ×132 [GPa]+ f 111 ×283 [GPa]+(1 −f 001 −f 111 )×208 [GPa]

where f 001 represents an accumulation rate of a <001> orientation with respect to a load axis, f 111 represents an accumulation rate of a <111> orientation, and (1−f 001 −f 111 ) represents an accumulation rate of crystal orientations except the <001> orientation and the <111> orientation.

2. The steel plate according to claim 1 , wherein the Young's modulus at the plate thickness center portion or surface layer portion is 210 GPa or more in a case in which a tensile direction in a tensile test is at least any one of a rolling direction, a plate width direction, or a direction forming an angle difference of 45 degrees from the rolling direction and the plate width direction.

3. The steel plate according to claim 1 , wherein a yield strength at the plate thickness center portion or surface layer portion is 580 MPa or more.

4. The steel plate according to claim 1 , wherein
an orientation accumulation rate of a texture at the plate thickness center portion is
in a range of 0% to 5% in a rolling direction, in a range of 0% to 5% in a plate width direction, and in a range of 14% to 24% in a 45-degree oblique direction in a <001> orientation and
in a range of 0% to 5% in a rolling direction, in a range of 34% to 44% in a plate width direction, and in a range of 0% to 5% in a 45-degree oblique direction in a <111> orientation, and
an orientation accumulation rate of a texture at the surface layer portion is
in a range of 20% to 30% in a rolling direction, in a range of 0% to 5% in a plate width direction, and in a range of 10% to 20% in a 45-degree oblique direction in a <001> orientation and
in a range of 16% to 26% in a rolling direction, in a range of 12% to 22% in a plate width direction, and in a range of 15% to 25% in a 45-degree oblique direction in a <111> orientation.

5. The steel plate according to claim 1 , wherein
an orientation accumulation rate of a texture at the plate thickness center portion is
in a range of 0% to 5% in a rolling direction, in a range of 0% to 5% in a plate width direction, and in a range of 36% to 46% in a 45-degree oblique direction in a <001> orientation and
in a range of 0% to 5% in a rolling direction, in a range of 2% to 12% in a plate width direction, and in a range of 0% to 5% in a 45-degree oblique direction in a <111> orientation, and
an orientation accumulation rate of a texture at the surface layer portion is
in a range of 10% to 20% in a rolling direction, in a range of 10% to 20% in a plate width direction, and in a range of 14% to 24% in a 45-degree oblique direction in a <001> orientation and
in a range of 8% to 18% in a rolling direction, in a range of 28% to 38% in a plate width direction, and in a range of 5% to 15% in a 45-degree oblique direction in a <111> orientation.

6. The steel plate according to claim 1 , wherein
an orientation accumulation rate of a texture at the plate thickness center portion is
in a range of 0% to 5% in a rolling direction, in a range of 0% to 5% in a plate width direction, and in a range of 12% to 22% in a 45-degree oblique direction in a <001> orientation and
in a range of 0% to 5% in a rolling direction, in a range of 20% to 30% in a plate width direction, and in a range of 0% to 5% in a 45-degree oblique direction in a <111> orientation, and
an orientation accumulation rate of a texture at the surface layer portion is
in a range of 0% to 5% in a rolling direction, in a range of 0% to 5% in a plate width direction, and in a range of 8% to 18% in a 45-degree oblique direction in a <001> orientation and
in a range of 2% to 12% in a rolling direction, in a range of 10% to 20% in a plate width direction, and in a range of 2% to 12% in a 45-degree oblique direction in a <111> orientation.

7. The steel plate according to claim 1 , wherein a difference in Young's moduli at the plate thickness center portion and the surface layer portion is 5 GPa or more.

8. A method for manufacturing the steel plate according to claim 1 , the method comprising performing rolling of a steel plate or steel material at a temperature in a range of 400° C. or more and 600° C. or less using a rolling mill having a work roll diameter of 650 mm or more, the steel plate or steel material consisting of
0.05% to 0.4% by mass of C,
1.65% by mass or less of Mn,
0.55% by mass or less of Si,
0.040% by mass or less of P, and
0.30% by mass or less of S,
with the balance being Fe and inevitable impurities.

9. The method according to claim 8 , wherein the rolling is any of reverse rolling, cross rolling, or one-way rolling of the steel plate or steel material.

10. A structural steel plate comprising the steel plate according to claim 1 , wherein a residual compressive stress in a surface layer is 100 MPa or more.

11. The method according to claim 8 , the method further comprising imparting tensile plastic deformation to the steel plate after the rolling to obtain a structural steel plate.

12. The method according to claim 8 , the method further comprising performing plastic working after the rolling to obtain a structural steel plate.

Assignees

• Nat Inst Materials Science

Inventors

• Inoue Tadanobu
• Qiu Hai
• Ueji Rintaro

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C22C38/04 Primary

  containing manganese · CPC title

• C21D8/0205

  Chemistry & Metallurgy · mapped topic

• C21D8/0221

  characterised by the working steps · CPC title

• C21D9/46

  for sheet metals · CPC title