Ultrahigh-strength maraging stainless steel with multiphase strengthening and preparation method thereof

Patent metadata

Field	Value
Publication number	US-11767574-B2
Application number	US-202217865670-A
Country	US
Kind code	B2
Filing date	Jul 15, 2022
Priority date	Aug 25, 2021
Publication date	Sep 26, 2023
Grant date	Sep 26, 2023

Abstract

Disclosed is an ultrahigh-strength maraging stainless steel with multiphase strengthening and a preparation method thereof. The stainless steel has a composition in mass percentage as follows: 1.0-5.0% of Co, 6.0-10.0% of Ni, 11.0-17.0% of Cr, 0.3-2.0% of Ti, 3.0-7.0% of Mo, 0.08-1.0% of Mn, 0.08-0.5% of Si, 0.02% or less of C, 0.003% or less of P, 0.003% or less of S, and Fe as a balance.

First claim

What is claimed is:

1. A method for preparing maraging stainless steel with multiphase strengthening, comprising:
1) proportioning alloying elements;
2) vacuum smelting for an electrode in a vacuum induction melting furnace;
3) vacuum arc remelting;
4) homogenizing annealing;
5) forging or hot rolling for cogging;
6) cold rolling deformation; and
7) heat treating,
wherein the maraging stainless steel with multiphase strengthening has a composition as follows in mass percentage: 1.0-5.0% of Co, 6.0-10.0% of Ni, 11.0-17.0% of Cr, 0.3-2.0% of Ti, 3.0-7.0% of Mo, 0.08-1.0% of Mn, 0.08-0.5% of Si, 0.02% or less of C, 0.003% or less of P, 0.003% or less of S, and Fe as a balance.

2. The method according to claim 1 , wherein in step 1), the proportioning of alloying elements comprises: taking metal chromium, metal nickel, metal manganese, metal molybdenum, metal cobalt, metal titanium, iron-silicon, and pure iron and inevitable impurities as a balance, according to a mass percentage of each element in the maraging stainless steel.

3. The method according to claim 1 , wherein in step 2), the vacuum smelting for an electrode in a vacuum induction melting furnace is conducted by high vacuum smelting throughout at a vacuum degree of 0.1 Pa or less; pure iron, metal nickel, metal molybdenum and metal cobalt are added with the vacuum induction melting furnace, metal chromium and metal titanium are added from an overhead bunker, and industrial silicon and metal manganese are added from an alloy bunker; after materials added with the vacuum induction melting furnace are molten down, metals from the overhead bunker are added, molten totally and subjected to deoxidation alloying, and the industrial silicon and the metal manganese from the alloy bunker are finally added; during smelting, refining is conducted at a temperature within a range of 1,550-1,650° C. for not less than 60 min under stirring for not less than 10 min; smelting composition is sampled on site and analyzed, and then is adjusted to achieve a target composition; pouring is conducted at a temperature within a range of 1,530-1,550° C., and heat preservation is conducted on a riser.

4. The method according to claim 1 , wherein in step 3), the vacuum arc remelting is conducted at a melting rate within a range of 100-260 Kg/h, and during the vacuum arc remelting, a vacuum degree is maintained at 10 −2 Pa or less.

5. The method according to claim 1 , wherein in step 4), the homogenizing annealing comprises: heating with a furnace in air, vacuum or a protective atmosphere at a rate of 100-180° C./h to a temperature within a range of 600-900° C. and maintaining for 4-8 h, then heating to a temperature within a range of 1,100-1,300° C. and maintaining for 20-50 h, and then conducting furnace cooling, air cooling or oil cooling to room temperature.

6. The method according to claim 1 , wherein in step 5), the forging or hot rolling produces a square ingot or round ingot; the forging or hot rolling for cogging is conducted under conditions as follows: a billet is heated to a temperature within a range of 1,100-1,300° C. and maintained for 10-24 h for discharging and rolling; the forging or hot rolling begins at a temperature of 1,100° C. or higher and ends at a temperature of 950° C. or higher; a hot rolled sheet stock has a total rolling reduction of not less than 50%, and a forged billet has a forging ratio of not less than 6; after the forging or hot rolling, a resultant is cooled in an ice-water mixture to room temperature.

7. The method according to claim 1 , wherein in step 6), the cold rolling deformation is conducted as follows: a cold rolled sheet stock has a total rolling reduction of not less than 65%; a tube stock, a bar stock, a wire stock or a section material is cold deformed by reciprocating tube rolling, groove rolling, universal rolling or drawing to obtain a size and specification of a product as required.

8. The method according to claim 1 , wherein in step 7), the heat treating comprises: quenching treatment, cryogenic treatment and aging treatment.

9. The method according to claim 8 , wherein the quenching treatment is conducted by maintaining at a temperature within a range of 1,050-1,200° C. for 5-30 min, and then quenching in an ice-water mixture at 0° C. for cooling.

10. The method according to claim 8 , wherein the cryogenic treatment is conducted with liquid nitrogen for 4-10 h, followed by returning to room temperature.

11. The method according to claim 8 , wherein the aging treatment is conducted at a temperature within a range of 450-600° C. for 0.5-500 h, followed by air cooling or quenching to room temperature.

Assignees

• Univ Harbin Eng

Inventors

• Zhang Zhongwu
• Li Junpeng

Classifications

• C21D8/02

  during manufacturing of plates or strips (C21D8/12 takes precedence) · CPC title

• C21D8/00

  Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment (hardening articles or materials formed by forging or rolling with no further heating beyond that required for the formation C21D1/02) · CPC title

• C21D8/06

  during manufacturing of rods or wires · CPC title

• C21D8/10

  during manufacturing of tubular bodies · CPC title

• C21D9/46 Primary

  for sheet metals · CPC title