Two-component system for elastic coatings

Patent metadata

Field	Value
Publication number	US-11760828-B2
Application number	US-201816645870-A
Country	US
Kind code	B2
Filing date	Aug 21, 2018
Priority date	Sep 26, 2017
Publication date	Sep 19, 2023
Grant date	Sep 19, 2023

Abstract

The present invention relates to a two-component system comprising a component A) comprising at least one polymeric polyol which has an OH content of ≤4.5 wt %, based on the total solids content of the polymeric polyol, and a component B) comprising at least one polyisocyanate which has a number average isocyanate group functionality of ≥4.0 to ≤10.0, based on the total solids content of the polyisocyanate, a fraction of ≤25 wt %, based on the total solids content of the polyisocyanate, of oligomers containing isocyanate groups and having a number-average molecular weight of ≤780 g/mol, and an isocyanurate group fraction of ≥5 mol % to ≤70 mol %, based on the total amount of isocyanurate groups and allophanate groups in the polyisocyanate. The invention further relates to a method for producing a coating on a substrate, to the coating obtainable by this method, and to the coated substrate.

First claim

The invention claimed is:

1. A two-component system comprising
component A) comprising at least one polymeric polyol which has an OH content of ≤4.5 wt %, based on the total solids content of the polymeric polyol, and
component B) comprising at least one polyisocyanate which
has a number average isocyanate group functionality of >5.0 to <10.0, based on the total solids content of the polyisocyanate,
a fraction of ≤25 wt %, based on the total solids content of the polyisocyanate, of oligomers containing isocyanate groups and having a number-average molecular weight of ≤780 g/mol,
an isocyanurate group fraction of ≥5 mol % to ≤70 mol %, based on the sum of amounts of isocyanurate groups and allophanate groups in the polyisocyanate, and wherein the polyisocyanate is obtained by oligomerization of at least one aliphatic, cycloaliphatic or araliphatic monomeric diisocyanate having a molecular weight of ≥140 to ≤400 g/mol and at least one hydroxy-functional compound having an OH functionality of >2 and ≤6 and a molecular weight of ≥130 to ≤500 g/mol in the presence of a catalyst.

2. The two-component system according to claim 1 , wherein the polyisocyanate comprises at least one oligomer which contains one or more isocyanurate groups and one or more allophanate groups, which in each case are joined chemically to one another via an aliphatic, cycloaliphatic or araliphatic group having a molecular weight of ≥56 to ≤316 g/mol.

3. The two-component system according to claim 1 , wherein the number average isocyanate group functionality is >5.0 to ≤8.0, based on the total solids content of the polyisocyanate.

4. The two-component system according claim 1 , wherein the fraction of the oligomers containing isocyanate groups and having a number-average molecular weight of ≤780 g/mol is ≤22 wt %, based on the total solids content of the polyisocyanate.

5. The two-component system according to claim 1 , wherein the fraction of isocyanurate groups is ≥10 mol % to ≤60 mol %, based on the total amount of isocyanurate groups and allophanate groups in the polyisocyanate.

6. The two-component system according claim 1 , wherein the polyisocyanate has a fraction of allophanate groups of ≥30 mol % to ≤95 mol %, based on the total amount of isocyanurate groups and allophanate groups in the polyisocyanate.

7. The two-component system according to claim 2 , wherein the one or more isocyanurate groups and one or more allophanate groups of the oligomer are each joined chemically to one another via a linear or branched aliphatic group in the molecular weight range from ≥56 to ≤316 g/mol, via a 1,5-pentyl or 1,6-hexyl group.

8. The two-component system according to claim 1 , wherein the hydroxy-functional compound has an OH functionality of ≥3 and ≤5 and a molecular weight of ≥130 to ≤500 g/mol.

9. The two-component system according to claim 1 , wherein the polymeric polyol present at least in component A) is a polycarbonate polyol.

10. The two-component system according to claim 1 , wherein component A) consists of ≥30 wt %, of the polymeric polyol, based on the total weight of component A), and the balance to 100 wt % is composed of one or more polymeric polyester, polyether and/or polycarbonate polyols which are different from the polymeric polyol, and also, optionally, of one or more additives.

11. The two-component system according to claim 1 , wherein a further constituent of component A) of the two-component system is water.

12. A method for producing a coating on a substrate, comprising the following steps:
1) Providing a substrate;
2) Applying at least one two-component system according to claim 1 ;
3) Curing the two-component system applied in step 2), optionally with supply of heat,
wherein the two-component system optionally comprises one or more additives.

13. The coating produced or producible by the method according to claim 12 .

14. A substrate at least partially coated with the coating according to claim 13 .

15. The two-component system according to claim 1 , wherein component A) consists of ≥30 and ≤50 wt %, of the polymeric polyol, based on the total weight of component A), and the balance to 100 wt % is composed of one or more polymeric polyester, polyether and/or polycarbonate polyols which are different from the polymeric polyol, and also, optionally, of one or more additives.

Assignees

• Covestro Deutschland Ag

Inventors

• Irle Christoph
• Mager Dieter
• Liu Qinglan
• Cheng Limin

Classifications

• C09D175/06 Primary

  from polyesters · CPC title

• C08G18/44 Primary

  Polycarbonates · CPC title

• C08G18/706

  the liquid medium being water · CPC title

• C08G18/73

  acyclic · CPC title

• C08G18/7837

  containing allophanate groups · CPC title