Abstract

Disclosed is a method comprising: a) dispersing a first monomer mixture comprising least one least monomer, the first monomer mixture having a total glass transition temperature (Tg) in the range of from −10° C. to −65° C. with a surfactant and an initiator in an aqueous medium; b) when the first monomer mixture is completely dispersed, adding a second monomer mixture comprising at least one monomer, the second monomer mixture having a Tg at least 20° C. greater than the Tg of the first monomer mixture, to the aqueous medium; c) when the second monomer mixture is completely dispersed, adding a third monomer mixture comprising at least one monomer, the third monomer mixture having a Tg in the range of from −25° C. to 50° C.; and d) forming a polymer with the first, second, and third monomer mixtures. Also disclosed is a pressure sensitive adhesive comprising the polymer formed by this method.

First claim

The invention claimed is:

1. A method consisting of:
a) dispersing and allowing to at least partially polymerize a first monomer mixture, a surfactant, and an initiator in an aqueous medium, the first monomer mixture comprising a monomer selected from the group consisting of butyl acrylate, ethylhexyl acrylate, ethyl acrylate, isooctyl acrylate, and combinations thereof and the partially polymerized first monomer mixture having a total glass transition temperature (“Tg”) in the range of from −10 to −65° C.;
b) after the first monomer mixture is completely dispersed in the aqueous medium, adding and allowing to at least partially polymerize a second monomer mixture to the aqueous medium, the second monomer mixture comprising isobornyl (meth)acrylate and the partially polymerized second monomer mixture having a total Tg of at least 20° C. greater than the Tg of the first monomer mixture;
c) after the second monomer mixture is completely dispersed in the aqueous medium, adding and allowing to at least partially polymerize, a third monomer mixture to the aqueous medium, the third monomer mixture comprising a monomer selected from butyl methacrylate, butyl acrylate, styrene, and combinations thereof and the partially polymerized third monomer mixture having a total Tg of from −25 to 50° C.; and
d) forming a polymer with the first, second, and third monomer mixtures,
wherein the first monomer mixture accounts for from 73 to 79.5 weight percent of the total weight of the first monomer mixture, the second monomer mixture, and the third monomer mixture,
wherein the second monomer mixture accounts for from 0.5 to 7 weight percent of the total weight of the first monomer mixture, the second monomer mixture, and the third monomer mixture.

Assignees

• Rohm & Haas

Inventors

• Einsla Melinda L
• Patrick Steven R
• Griffith Jr William B
• Nedwick Paul

Classifications

• C08F265/06 Primary

  Polymerisation of acrylate or methacrylate esters on to polymers thereof · CPC title

• C08F220/1804 Primary

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• C08F265/04 Primary

  on to polymers of esters · CPC title

• C08F285/00

  Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers · CPC title

• C09J151/00

  Adhesives based on graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds (based on ABS polymers C09J155/02); Adhesives based on derivatives of such polymers · CPC title