Metal porous body and method for producing metal porous body

Patent metadata

Field	Value
Publication number	US-11757101-B2
Application number	US-201816500981-A
Country	US
Kind code	B2
Filing date	Mar 13, 2018
Priority date	May 22, 2017
Publication date	Sep 12, 2023
Grant date	Sep 12, 2023

Abstract

The metal porous body having a framework of a three-dimensional network structure is disclosed. The framework is formed of a metal film, the framework has an interior that is hollow, and the metal film contains titanium metal or titanium alloy as a main component.

First claim

The invention claimed is:

1. A metal porous body having a framework of a three-dimensional network structure,
the framework formed of a metal film and the framework having an interior that is hollow, wherein the metal film has an average thickness of 1 μm or more and 300 μm or less,
the metal film containing titanium metal or titanium alloy, a content of the titanium metal or the titanium alloy of the metal film being 90 mass % or more,
the metal porous body has a sheet shape, the sheet shape having a predetermined length in a length direction, a predetermined width in a width direction, and a predetermined thickness in a thickness direction,
the sheet shape is divided into at least two regions in the thickness direction of the sheet shape,
the at least two regions composed of the titanium metal or the titanium alloy of the metal film, the content of the at least two regions composed of the titanium metal or the titanium alloy of the metal film being 90 mass % or more,
a boundary separates each of the at least two regions in the thickness direction of the sheet shape, and
one or both of an average pore diameter of the metal porous body and a weight of the metal porous body is different between the at least two regions, the weight being a mass per unit area.

2. The metal porous body according to claim 1 , wherein
the metal porous body has a porosity of 60% or more and 98% or less.

3. The metal porous body according to claim 1 , wherein
the metal porous body has an average pore diameter of 50 μm or more and 5000 μm or less.

4. The metal porous body according to claim 1 , wherein
the average pore diameter of the metal porous body is different between a first region of the at least two regions on a first side and a second region of the at least two regions on a second side in the thickness direction of the sheet shape.

5. The metal porous body according to claim 1 wherein
the weight of the metal porous body is different between a first region of the at least two regions on a first side and a second region of the at least two regions on a second side in the thickness direction of the sheet shape.

6. The metal porous body according to claim 1 , wherein
the average pore diameter of the metal porous body is different between a central region of the at least two regions and outer regions of the at least two regions located outside the central region in the thickness direction of the sheet shape.

7. The metal porous body according to claim 1 , wherein
the weight of the metal porous body is different between a central region of the at least two regions and outer regions of the at least two regions located outside the central region in the thickness direction of the sheet shape.

8. A method for producing a metal porous body according to claim 1 , comprising:
a molten salt bath preparation step of preparing a molten salt bath that contains an alkali metal halide and a titanium compound;
a dissolution step of dissolving titanium metal in the molten salt bath;
an electrolysis step of performing a molten salt electrolysis by using a cathode and an anode provided in the molten salt bath in which the titanium metal is dissolved so as to electrodeposit the titanium metal on the surface of the cathode; and
a treatment step of treating the cathode on which the titanium metal is electrodeposited with an acid or an alkali,
in the dissolution step, the titanium metal being supplied in at least a minimum amount required to convert Ti 4+ in the molten salt bath into Ti 3+ by a comproportionation reaction represented by the following formula (1):
3Ti 4+ +Ti metal→4Ti 3+   (1),

in the electrolysis step, a porous base material which has a three-dimensional network structure being used as the cathode.

9. The method for producing a metal porous body according to claim 8 , wherein
the porous base material includes at least one material selected from the group consisting of a metal, an alloy, a carbon material and a conductive ceramic.

10. The method for producing a metal porous body according to claim 8 , wherein
the treatment step is performed at a temperature of 20° C. or more.

11. The method for producing a metal porous body according to claim 8 , wherein
the porous base material used as the cathode has an outer profile of a sheet shape, and the average pore diameter is different between a region on one side and a region on the other side in the thickness direction of the sheet, or
the porous base material used as the cathode has an outer profile of a sheet shape, and the average pore diameter is different between a central region and an outer region located outside the central region in the thickness direction of the sheet.

12. The method for producing a metal porous body according to claim 8 , wherein
the titanium metal to be dissolved in the dissolution step is a titanium sponge.

13. The method for producing a metal porous body according to claim 8 , wherein
the titanium metal is used as the anode.

14. An insoluble positive electrode made of the metal porous body according to claim 1 .

15. The insoluble positive electrode according to claim 14 , wherein
the insoluble positive electrode is used in the production of hydrogen.

16. A fuel-cell electrode made of the metal porous body according to claim 1 .

17. The fuel-cell electrode according to claim 16 , wherein
the fuel-cell electrode is used in a polymer electrolyte fuel cell.

18. A method for producing hydrogen in which hydrogen is generated by electrolyzing water using the metal porous body according to claim 1 as an electrode.

19. The method for producing hydrogen according to claim 18 , wherein
the water is an alkaline aqueous solution.

20. The method for producing hydrogen according to claim 18 , wherein
the metal porous bodies are disposed at both sides of a solid polymer electrolyte membrane and brought into contact with the solid polymer electrolyte membrane so that the metal porous bodies act as a positive electrode and a negative electrode, respectively, to electrolyze water supplied to the positive electrode side so as to generate hydrogen at the negative electrode side.

21. A hydrogen producing apparatus configured to generate hydrogen by electrolyzing water, comprising the metal porous body according to claim 1 as an electrode.

22. The hydrogen producing apparatus according to claim 21 , wherein
the water is a strong alkaline aqueous solution.

23. The hydrogen producing apparatus according to claim 21 , wherein
the hydrogen producing apparatus includes a positive electrode and a negative electrode disposed at both sides of a solid polymer electrolyte membrane and configured to be in contact with the solid polymer electrolyte membrane,
the hydrogen producing apparatus is configured to electrolyze water supplied to the positive electrode side so as to generate hydrogen at the negative electrode side, and
at least one of the positive electrode and the negative electrode is made of the metal porous body.

24. A biomaterial made of the metal porous body according to claim 1 .

25. A medical device comprising the biomaterial according to claim 24 .

26. The medical device according to claim 25 , wherein the medical device is selected from the group consisting of a spinal fixation device, a fracture fixation member, an artificial joint, an artificial valve, an intravascular stent, a dental plate, a

Assignees

• Sumitomo Electric Industries

Inventors

• Numata Koma
• Majima Masatoshi
• Awazu Tomoyuki
• Ogawa Mitsuyasu
• Higashino Takahiro
• Tawarayama Hiromasa

Classifications

• C25B9/00

  Cells or assemblies of cells; Constructional parts of cells; Assemblies of constructional parts, e.g. electrode-diaphragm assemblies; Process-related cell features · CPC title

• C25B1/04

  by electrolysis of water · CPC title

• C25B11/031

  Porous electrodes · CPC title

• A61C7/20 Primary

  Arch wires (A61C7/28 takes precedence) · CPC title

• C25D1/08 Primary

  Perforated or foraminous objects, e.g. sieves (C25D1/10 takes precedence) · CPC title