Surface-reacted calcium carbonate with functional cations

Patent metadata

Field	Value
Publication number	US-11718759-B2
Application number	US-202117492216-A
Country	US
Kind code	B2
Filing date	Oct 1, 2021
Priority date	Jul 25, 2016
Publication date	Aug 8, 2023
Grant date	Aug 8, 2023

Abstract

A surface-reacted calcium carbonate is described. In embodiments, the surface-reacted calcium carbonate is obtained by a process comprising treating a calcium carbonate-comprising material with at least one H3O+ ion donor, carbon dioxide, and at least one water-soluble metal cation source in an aqueous medium to form an aqueous suspension of surface-reacted calcium carbonate.

First claim

The invention claimed is:

1. A surface-reacted calcium carbonate wherein the surface-reacted calcium carbonate is obtained by a process comprising the steps of:
a) providing a calcium carbonate-comprising material, wherein the calcium carbonate-comprising material is a natural ground calcium carbonate;
b) providing at least one H 3 O + ion donor, wherein the at least one H 3 O+ ion donor is phosphoric acid,
c) providing at least one water-soluble metal cation source, wherein the at least one water-soluble metal cation source is selected from the group consisting of copper nitrate, copper sulphate, copper acetate, copper chloride, copper bromide, copper iodide, zinc nitrate, zinc sulphate, zinc acetate, zinc chloride, zinc bromide, zinc iodide, hydrates thereof, and mixtures thereof, and
d) treating the calcium carbonate-comprising material of step a) with the at least one H 3 O + ion donor of step b) and carbon dioxide in an aqueous medium to form an aqueous suspension of surface-reacted calcium carbonate, wherein in step d) the calcium carbonate-comprising material is treated with a solution comprising the at least one H 3 O+ ion donor of step b) and the at least one water-soluble metal cation source of step c),
wherein the carbon dioxide is formed in-situ by the H 3 O + ion donor treatment of the calcium carbonate-comprising material and/or is supplied from an external source and the at least one water-soluble metal cation source of step c) is added during step d);
wherein the surface-reacted calcium carbonate comprises the calcium carbonate-comprising material, at least one water-insoluble calcium salt other than calcium carbonate, and at least one water-insoluble metal cation salt incorporated into the internal structure of the surface-reacted calcium carbonate, and wherein the ratio of the at least one water-insoluble metal cation salt to calcium carbonate-comprising material is in the range of 0.00001:1 to 0.1:1 by weight.

2. The surface-reacted calcium carbonate of claim 1 , wherein the calcium carbonate-comprising material is in the form of particles having a weight median particle size d 50 (wt) from 0.05 μm to 10 μm, and/or a weight top cut particle size d 98 (wt) from 0.15 μm to 55 μm.

3. The surface-reacted calcium carbonate of claim 2 , wherein the weight median particle size d 50 (wt) is from 0.2 μm to 5.0 μm and/or the weight top cut particle size d 98 (wt) is from 1 μm to 40 μm.

4. The surface-reacted calcium carbonate of claim 1 , wherein the molar ratio of the at least one H 3 O + ion donor to the calcium carbonate-comprising material is from 0.01 to 4.

5. The surface-reacted calcium carbonate of claim 4 , wherein the molar ratio is from 0.02 to 2.

6. The surface-reacted calcium carbonate of claim 1 , wherein the at least one water-soluble metal cation source is provided in an amount from 0.01% wt. -% to 60 wt. -%, based on the total weight of the calcium carbonate-comprising material.

7. The surface-reacted calcium carbonate of claim 6 , wherein the amount of the at least one water-soluble metal cation source is from 0.05 wt.-% to 50 wt.-%.

8. The surface-reacted calcium carbonate of claim 1 , wherein in step d) the calcium carbonate-comprising material is treated with a first solution comprising a first part of the at least one H 3 O + ion donor of step b), and subsequently, with a second solution comprising the remaining part of the at least one H 3 O + ion donor of step b) and the at least one water-soluble metal cation source of step c).

9. The surface-reacted calcium carbonate of claim 1 , wherein step d) is carried out at a temperature from 20° C. to 90° C.

10. The surface-reacted calcium carbonate of claim 1 , wherein the process further comprises a step e) of separating the surface-reacted calcium carbonate from the aqueous suspension obtained in step d).

11. The surface-reacted calcium carbonate of claim 1 , wherein the process further comprises a step f) of drying the surface-reacted calcium carbonate after step d) at a temperature in the range from 60° C. to 600° C.

12. The surface-reacted calcium carbonate of claim 11 , wherein the drying is conducted until the moisture content of the surface-reacted calcium carbonate is from 0.01 wt.-% to 5 wt.-% based on the total weight of the dried surface-reacted calcium carbonate.

13. The surface-reacted calcium carbonate of claim 1 , wherein the surface-reacted calcium carbonate has a specific surface area of from 15 m 2 /g to 200 m 2 /g measured using nitrogen and the BET method.

14. The surface-reacted calcium carbonate of claim 13 , wherein the specific surface area is from 20 m 2 /g to 180 m 2 /g.

15. The surface-reacted calcium carbonate of claim 1 , wherein the surface-reacted calcium carbonate has a volume determined median particle size d 50 (vol) from 1 μm to 75 μm and/or a volume determined top cut particle size d 98 (vol) from 2 μm to 150 μm.

16. The surface-reacted calcium carbonate of claim 15 , wherein the volume determined median particle size d 50 (vol) is from 2 μm to 50 μm and/or the volume determined top cut particle size d 98 (vol) is from 4 μm to 100 μm.

17. The surface-reacted calcium carbonate of claim 1 , wherein the surface-reacted calcium carbonate has an intra-particle intruded specific pore volume in the range from 0.1 cm 3 /g to 2.3 cm 3 /g calculated from mercury porosimetry measurement.

18. The surface-reacted calcium carbonate of claim 17 , wherein the intra-particle intruded specific pore volume is from 0.2 cm 2 /g to 2.0 cm 3 /g.

19. The surface-reacted calcium carbonate of claim 1 , wherein the surface-reacted calcium carbonate has an intra-particle pore size in a range of from 0.004 μm to 1.6 μm determined from mercury porosimetry measurement.

20. The surface-reacted calcium carbonate of claim 19 , wherein the intra-particle pore size is from 0.005 μm to 1.3 μm.

21. The surface-reacted calcium carbonate of claim 1 , wherein the ratio of the at least one water-insoluble metal cation salt to calcium carbonate-comprising material is in the range of 0.001 to 0.01 by weight.

22. A composition comprising a surface-reacted calcium carbonate according to claim 1 , the composition further comprising an additional surface-reacted calcium carbonate, wherein the additional surface-reacted calcium carbonate is a reaction product of natural ground calcium carbonate or precipitated calcium carbonate with carbon dioxide and at least one H 3 O + ion donor, wherein the carbon dioxide is formed in-situ by the H 3 O + ion donor treatment and/or is supplied from an external source.

23. An article comprising a surface-reacted calcium carbonate according to claim 1 , wherein the article is selected from the group consisting of paper products, engineered wood products, plasterboard products, polymer products, hygiene products, medical products, healthcare products, filter products, woven materials, nonwoven materials, geotextile products, agriculture products, horticulture products, clothing, footwear products, baggage products, household products, industrial products, packaging products, building products, and construction products.

24. The surface-reacted calcium carbonate of claim 1 , wherein the natural ground calcium carbonate is selected from the group consisting of marble, chalk, dolomite, limestone, and mixtures thereof.

Assignees

• Omya Int Ag

Inventors

• Gerard Daniel E
• Rentsch Samuel
• Welker Matthias
• Urwyler Simon
• Glaubitz Joachim
• Knupfer Martina Elisabeth
• Gane Patrick A C

Classifications

• A23B2/788

  Inorganic compounds · CPC title

• C09C1/022 Primary

  Treatment with inorganic compounds · CPC title

• D21H17/675

  Oxides, hydroxides or carbonates · CPC title

• D21H19/385

  Oxides, hydroxides or carbonates · CPC title

• D21H21/52

  Additives of definite length or shape · CPC title