Polycarbonate-polyorganosiloxane copolymer, polycarbonate resin composition including same, and molded product thereof

Patent metadata

Field	Value
Publication number	US-11697708-B2
Application number	US-201816490057-A
Country	US
Kind code	B2
Filing date	Mar 1, 2018
Priority date	Mar 1, 2017
Publication date	Jul 11, 2023
Grant date	Jul 11, 2023

Abstract

Provided is a polycarbonate-polyorganosiloxane copolymer including polycarbonate blocks (A-1) each formed of a specific repeating unit and polyorganosiloxane blocks (A-2) each containing a specific repeating unit, wherein the polycarbonate-polyorganosiloxane copolymer satisfies the following expression (F1a):15≤wM1  (F1a)wherein wM1 represents the average content of the polyorganosiloxane blocks (A-2) in polycarbonate-polyorganosiloxane copolymers each having a molecular weight determined by using a polycarbonate as a conversion reference of from 56,000 or more to 200,000 or less among polycarbonate-polyorganosiloxane copolymers obtained through the separation of the polycarbonate-polyorganosiloxane copolymer by gel permeation chromatography.

First claim

The invention claimed is:

1. A polycarbonate-based resin composition, comprising:
polycarbonate-polyorganosiloxane copolymers (A), each comprising polycarbonate blocks (A-1) each formed of a repeating unit represented by the following general formula (I); and
polyorganosiloxane blocks (A-2) each containing a repeating unit represented by the following general formula (II), wherein the polycarbonate-polyorganosiloxane copolymers satisfy the following expression (F1a):
40≤wM1 (F1a);
wherein wM1 represents an average content (mass %) of the polyorganosiloxane blocks (A-2) in a first fraction of the polycarbonate-polyorganosiloxane copolymers, each copolymer of the first fraction having a molecular weight calculated by gel permeation chromatography of from 56,000 or more to 200,000 or less, the first fraction is obtained through separation of the polycarbonate-polyorganosiloxane copolymers by gel permeation chromatography
an aromatic polycarbonate-based resin (B) except the polycarbonate-polyorganosiloxane copolymers (A); and
a styrene-based resin (C),
wherein the styrene-based resin (C) is blended with respect to 100 parts by mass of a total of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B), and
wherein a ratio of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B) in 100 mass % of a total amount of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B), and the styrene-based resin (C) is from 50 mass % or more to 99 mass % or less:

wherein R 1 and R 2 each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, a fluorenediyl group, an arylalkylene group having 7 to 15 carbon atoms, an arylalkylidene group having 7 to 15 carbon atoms, —S—, —SO—, —SO 2 —, —O—, or —CO—, R 3 and R 4 each independently represent a hydrogen atom, a halogen atom, an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or an aryl group having 6 to 12 carbon atoms, and “a” and “b” each independently represent an integer of from 0 to 4;
wherein the viscosity-average molecular weight (Mv) of a polycarbonate-based resin formed of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B) is 9,000 or more and 23,000 or less and the content of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers (A) is 30 mass % or more and 70 mass % or less,
wherein the polyorganosiloxane blocks (A-2) have an average chain length of from 55 or more to 120 or less; and
wherein the composition does not comprise a rubber-modified styrene-based resin.

2. The polycarbonate-based resin composition according to claim 1 , wherein the aromatic polycarbonate-based resin (B) contains a polycarbonate block including, in a main chain thereof, a repeating unit represented by the following general formula (III):

wherein R 30 and R 31 each independently represent a halogen atom, an alkyl group having 1 to 6 carbon atoms, or an alkoxy group having 1 to 6 carbon atoms, X′ represents a single bond, an alkylene group having 1 to 8 carbon atoms, an alkylidene group having 2 to 8 carbon atoms, a cycloalkylene group having 5 to 15 carbon atoms, a cycloalkylidene group having 5 to 15 carbon atoms, —S—, —SO—, —SO 2 —, —O—, or —CO—, and “d” and “e” each independently represent an integer of from 0 to 4.

3. The polycarbonate-based resin composition according to claim 1 , wherein a mass ratio “(A)/(B)” of the polycarbonate-polyorganosiloxane copolymers (A) to the aromatic polycarbonate-based resin (B) is from 0.1/99.9 to 99.9/0.1.

4. The polycarbonate-based resin composition according to claim 1 , wherein a content of the polyorganosiloxane blocks (A-2) with respect to a total of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B) is from 0.1 mass % or more to 10 mass % or less.

5. The polycarbonate-polyorganosiloxane copolymer according to claim 1 , wherein a content of the polyorganosiloxane blocks (A-2) in the polycarbonate-polyorganosiloxane copolymers (A) is 30 mass % or more and 40 mass % or less.

6. The polycarbonate-based resin composition according to claim 1 , wherein a content of the polyorganosiloxane blocks (A-2) with respect to a total of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B) is from 1.8 mass % or more to 5 mass % or less.

7. The polycarbonate-polyorganosiloxane copolymer according to claim 1 , wherein the polyorganosiloxane blocks (A-2) have an average chain length of from 61 or more to 85 or less.

8. The polycarbonate-based resin composition according to claim 1 , wherein the blending amount of the styrene-based resin (C) in the polycarbonate-based resin composition is from 3 mass % or more to 35 mass % or less in 100 mass % of the total amount of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B), and the styrene-based resin (C).

9. The polycarbonate-based resin composition according to claim 1 , wherein an Izod impact strength of the composition at −30° C. —is 45 kJ/m 2 or more, and
a content of the polyorganosiloxane blocks (A-2) with respect to a total of the polycarbonate-polyorganosiloxane copolymers (A) and the aromatic polycarbonate-based resin (B) is from 3.0 mass % or more to 10 mass % or less.

10. The polycarbonate-based resin composition according to claim 1 , wherein the styrene-based resin (C) has constituent units derived from acrylonitrile and styrene.

11. The polycarbonate-based resin composition according to claim 1 , wherein the styrene-based resin (C) comprises an acrylonitrile-styrene copolymer.

12. The polycarbonate-based resin composition according to claim 1 , wherein an acrylonitrile-styrene copolymer is the only styrene-based resin in the composition.

13. The polycarbonate-based resin composition according to claim 1 , wherein an blending amount of the styrene-based resin (C) in the composition is 15 mass % or less with respect to the total amount of the polycarbonate-polyorganosiloxane copolymers (A), the aromatic polycarbonate-based resin (B) and the styrene-based resin (C).

14. The polycarbonate-based resin composition according to claim 13 , wherein an Izod impact strength at −40° C. of the composition is 37 kJ/m 2 or more.

15. The polycarbonate-based resin composition according to claim 13 , wherein the composition has a deflection temperature under load measured by a method 1 of 120° C. or more, and
wherein the method 1 includes a load of 1.8 MPa being applied to a test piece of the composition in conformity with ASTM Standard D-648 at a rate of temperature increase of 120° C./h and a fulcrum-to-fulcrum distance of 100 mm, and the deflection temperature under load being a temperature when the deflection of the test piece measured in an edgewise manner reached 0.26 mm.

16. The polycarbonate-based resin composition according to claim 13 , wherein
the content of the polyorganosilox

Assignees

• Idemitsu Kosan Co

Inventors

• Ishikawa Yasuhiro
• Abe Tomoko
• Akimoto Takafumi

Classifications

• C08L55/02

  ABS [Acrylonitrile-Butadiene-Styrene] polymers · CPC title

• C08L2203/20

  use in electrical or conductive gadgets · CPC title

• C08L25/12

  with unsaturated nitriles · CPC title

• C08G64/186 Primary

  containing polysiloxane sequences · CPC title

• C08L69/00

  Compositions of polycarbonates; Compositions of derivatives of polycarbonates · CPC title