Nanocomposite supercapacitors and method of preparation thereof

Patent metadata

Field	Value
Publication number	US-11688564-B1
Application number	US-202217586166-A
Country	US
Kind code	B1
Filing date	Jan 27, 2022
Priority date	Jan 27, 2022
Publication date	Jun 27, 2023
Grant date	Jun 27, 2023

Abstract

An asymmetric nanocomposite supercapacitor and a method of making the asymmetric nanocomposite supercapacitor. The asymmetric nanocomposite supercapacitor includes a negative electrode with monoclinic tungsten oxide (m-WO 3 ) nanoplates, and a binding compound coated on one face of a substrate, and a positive electrode with a carbonaceous material and a binding compound coated on one face of a substrate. Where the face of the positive electrode and the face of the negative electrode coated with the carbonaceous material and m-WO 3 nanoplates, respectively, are separated by and in direct contact with a porous separator.

First claim

The invention claimed is:

1. An asymmetric nanocomposite supercapacitor, comprising:
a first electrode;
a second electrode;
a porous separator between the first and second electrodes;
wherein the porous separator is coated with an electrolyte;

wherein the first electrode comprises:
a first substrate at least partially coated on one face with a first mixture of a first binding compound and a carbonaceous material;

wherein the second electrode comprises:
a second substrate at least partially coated on one face with a second mixture of a second binding compound and monoclinic tungsten-oxide (m-WO 3 ) nanoplates;
wherein the face of the first substrate and the face of the second substrate coated with the carbonaceous material and m-WO 3 nanoplates, respectively, are separated by and in direct contact with the porous separator.

2. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the porous separator is at least one selected from a group consisting of polypropylene membrane, glass fiber, and cellulose fiber;
the electrolyte is at least one selected from a group consisting of a hydrogen halide, sulfuric acid, nitric acid, perchloric acid, chloric acid, an alkali metal salt, an alkaline earth salt;
the binding compound is at least one selected from a group consisting polyvinylidene fluoride and n-methylpyrrolidone;
the carbonaceous material is at least one selected from the group consisting of graphite, graphene, activated carbon, reduced graphene oxide, highly reduced graphene oxide (HRG), carbon nanotubes, carbon nanofibers, and carbon black; and
the substrate is a formed from at least one material selected from the group consisting of copper, aluminum, nickel, iron, and steel.

3. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the first mixture comprises 10-20 wt % of the first binding compound and 80-90 wt % of the carbonaceous material based on the total weight of the first binding compound, and the carbonaceous material; and
the second mixture comprises 10-20 wt % of the second binding compound and 80-90 wt % of the m-WO 3 nanoplates based on the total weight of the binding compound, and the m-WO 3 nanoplates.

4. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the carbonaceous material is HRG;
the HRG is substantially crystalline and in layered sheet form having 2-20 layers;
the sheets have an average d-spacing of 0.25-0.45 nm;
the HRG comprises at most 5% oxygen based on the total atomic weights of carbon, hydrogen, and oxygen in the HRG.

5. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the m-WO 3 nanoplates are substantially monoclinic crystalline phase;
the platelets have an average d-spacing of 0.3-0.5 nm;
the platelets have an average length of 50-200 nm, an average width of 10-150 nm, and
an average thickness of 5-20 nm; and
wherein the O and W elements are homogeneously distributed throughout the nanoplates.

6. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the carbonaceous material is HRG;
the HRG has a surface area of 500-800 m 2 /g; and
the m-WO 3 nanoplates have a surface area of 150-250 m 2 /g.

7. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the thickness of the coating of the carbonaceous material on the first substrate and the m-WO 3 nanoplates on the second substrate is less than 500 nm each.

8. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the first electrode has a specific capacitance of at least 440 F/g at a current density of 0.5 A/g.

9. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the second electrode has a specific capacitance of at least 310 F/g at a current density of 0.5 A/g.

10. The asymmetric nanocomposite supercapacitor of claim 1 , having:
a specific capacitance of at least 380 F/g at a current density of 0.5 A/g;
wherein the carbonaceous material is HRG.

11. The asymmetric nanocomposite supercapacitor of claim 10 , wherein:
at least 90% of the initial specific capacitance is maintained after 5000 charge-discharge cycles.

12. The asymmetric nanocomposite supercapacitor of claim 10 , having:
an energy density of at least 90 Wh/kg at a power density of 500 W/kg.

13. The asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the supercapacitor is operated up to 1.8 V.

14. A wearable device comprising the asymmetric nanocomposite supercapacitor of claim 1 , wherein:
the supercapacitor is electrically connected to a sensor; and
the supercapacitor functions as a battery.

15. The asymmetric nanocomposite supercapacitor of claim 1 , comprising:
2-10 of the asymmetric nanocomposite supercapacitors connected in parallel and/or series.

16. A method of making the asymmetric nanocomposite supercapacitor of claim 1 , comprising:
mixing 80-90 wt % of the carbonaceous material with 10-20 wt % of the first binding compound based on the total weight of the carbonaceous material and the first binding compound in a polar aprotic solvent and stirring for at least 3 hours to form a carbonaceous slurry;
mixing 80-90 wt % of the m-WO 3 nanoplates with 10-20 wt % of the second binding compound based on the total weight of the m-WO 3 nanoplates and the second binding compound in a polar aprotic solvent and stirring for at least 3 hours to form a m-WO 3 nanoplates slurry;
coating a layer of the carbonaceous slurry onto the first substrate to form a carbonaceous electrode;
coating a layer of the m-WO 3 nanoplates slurry onto the second substrate to form a m-WO 3 nanoplates electrode;
drying the carbonaceous electrode and the m-WO 3 nanoplates electrode in an oven at a temperature of at least 60° C. for at least 4 hours to form a dried carbonaceous electrode and a dried m-WO 3 nanoplates electrode, respectively;
soaking the porous separator in an aqueous solution of the electrolyte for at least 1 hour to form an electrolyte porous separator;
combining the dried carbonaceous electrode, the dried m-WO 3 nanoplates electrode, and the electrolyte porous separator;
wherein the first and second substrates are outer layers and the carbonaceous and m-WO 3 nanoplates are inner layers separated by the electrolyte porous separator to make an asymmetric nanocomposite supercapacitor.

17. The method of claim 16 , wherein:
the m-WO 3 nanoplates are made by a method comprising:
dissolving a tungsten oxide salt in acid and stirring for at least 30 minutes to form a tungsten oxide solution;
mixing ammonium nitrate into the tungsten oxide solution and heating to at least 160° C. for at least 12 hours in an autoclave to form a reaction mixture;
cooling to below 30° C., and filtering the reaction mixture to leave a precipitate; and

washing with at least one polar solvent and drying the precipitate at a temperature of at least 60° C. for at least 3 hours to leave m-WO 3 nanoplates.

Assignees

• Univ King Fahd Pet & Minerals

Inventors

• Ashraf Muhammad
• Tahir Muhammad Nawaz
• Ullah Nisar
• Shah Syed Shaheen
• Khan Ibrahim

Classifications

• H01G11/36

  Nanostructures, e.g. nanofibres, nanotubes or fullerenes · CPC title

• H01G11/46 Primary

  Metal oxides · CPC title

• H01G11/26

  characterised by their structure, e.g. multi-layered, porosity or surface features · CPC title

• H01G11/52

  Separators · CPC title

• H01G11/24

  characterised by structural features of the materials making up or comprised in the electrodes, e.g. form, surface area or porosity; characterised by the structural features of powders or particles used therefor · CPC title