Two-component polyurethane or polyisocyanurate low pressure spray foam composition containing a gaseous blowing agent comprising pressurized carbon dioxide

Patent metadata

Field	Value
Publication number	US-11655349-B2
Application number	US-202016815275-A
Country	US
Kind code	B2
Filing date	Mar 11, 2020
Priority date	Mar 11, 2019
Publication date	May 23, 2023
Grant date	May 23, 2023

Abstract

Storage-stable two-component polyurethane or polyisocyanurate spray foam compositions are disclosed, said compositions comprising: (a) an A-side component comprising one or more polyisocyanate and one or more blowing agent; and (b) a B-side component comprising one or more polyol and one or more blowing agent comprising pressurized gaseous carbon dioxide and one or more liquid blowing agent; wherein both the A-side component and the B-side component, separately, generate less than 300 ppm of fluoride ion after one week of aging at 50° C.

First claim

What is claimed:

1. A storage-stable two-component polyurethane or polyisocyanurate spray foam composition comprising:
a) an A-side component comprising one or more polyisocyanate and one or more blowing agent; and
b) a B-side component comprising one or more polyol and one or more blowing agent comprising pressurized gaseous carbon dioxide and one or more liquid blowing agent;

wherein both the A-side component and the B-side component, separately, generate less than 300 ppm of fluoride ion after one week of aging at 50° C.

2. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the pressurized gaseous carbon dioxide in the B-side component is present at a level of from 0.5 wt. % to 10 wt. % carbon dioxide, based on the total weight of the B-side component.

3. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the pressurized gaseous carbon dioxide in the B-side component provides a pressure of from 0.14 MPa to 4.00 MPa (21 psig to 580 psig) on the B-side component as measured at ambient temperature.

4. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the one or more liquid blowing agent in the B-side component is present at a level of from 10 wt. % to 40 wt. %, based on the total weight of the B-side component.

5. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the one or more liquid blowing agent in the B-side component is or comprises a hydrohaloolefin.

6. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 5 , wherein the one or more blowing agent in the A-side component is or comprises a hydrohaloolefin gaseous blowing agent.

7. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the one or more liquid blowing agent in the B-side component is or comprises a hydrofluoroolefin, hydrochloroolefin or a hydrofluorochloroolefin.

8. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein the one or more liquid blowing agent in the B-side component is or comprises (E)-1-chloro-3,3,3-trifluoropropene (HFO-1233zd).

9. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein both the one or more blowing agent in the A-side component and the one or more liquid blowing agent in the B-side component comprise a hydrohaloolefin blowing agent.

10. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein both the A-side component and the B-side component comprise one or more liquid blowing agent.

11. The storage-stable two-component polyurethane or polyisocyanurate spray foam composition of claim 1 , wherein both the A-side component and the B-side component comprise one or more blowing agent comprising pressurized gaseous carbon dioxide and one or more liquid blowing agent.

12. A two-component polyurethane or polyisocyanurate spray foam composition comprising:
a) an A-side component comprising:
i) one or more polyisocyanate,
ii) one or more blowing agent; and
iii) optionally, one or more surfactant; and

b) a B-side component comprising:
i) one or more polyol,
ii) one or more blowing catalyst or gelation catalyst or combination thereof,
iii) one or more blowing agent comprising pressurized gaseous carbon dioxide and one or more liquid blowing agent,
iv) optionally, one or more flame retardant; and
v) optionally, one or more surfactant.

13. The two-component polyurethane or polyisocyanurate spray foam composition of claim 12 , wherein the pressurized gaseous carbon dioxide in the B-side component is present at a level of from 0.5 wt. % to 10 wt. % carbon dioxide, based on the total weight of the B-side component.

14. The two-component polyurethane or polyisocyanurate spray foam composition of claim 12 , wherein the one or more liquid blowing agent in the B-side component is or comprises (E)-1-chloro-3,3,3-trifluoropropene (HFO-1233zd).

15. A method of providing a space filling layer or space filling volume adjacent to or on a surface, the method comprising:
(a) providing a foamable composition comprising:
(i) an A-side component comprising one or more polyisocyanate and one or more blowing agent; and
(ii) a B-side component comprising one or more polyol and one or more blowing agent comprising pressurized gaseous carbon dioxide and one or more liquid blowing agent;

wherein both the A-side component and the B-side component, separately, generate less than 300 ppm of fluoride ion after one week of aging at 50° C.;
(b) applying a foamed sample, or pre-foamed sample that generates a foamed sample, of the foamable composition to said surface; and
(c) allowing the foamed sample of foamable composition to cure to a foam having a density of less than 48 kg/m 3 .

16. The method of claim 15 , wherein the pressurized gaseous carbon dioxide in the B-side component is present at a level of from 0.5 wt. % to 10 wt. % carbon dioxide, based on the total weight of the B-side component.

17. The method of claim 15 , wherein the pressurized gaseous carbon dioxide in the B-side component provides a pressure of from 0.14 MPa to 4.00 MPa (21 psig to 580 psig) on the B-side component as measured at ambient temperature.

18. The method of claim 15 , wherein the one or more liquid blowing agent in the B-side component is or comprises a hydrohaloolefin.

19. The method of claim 15 , wherein the one or more liquid blowing agent in the B-side component is or comprises (E)-1-chloro-3,3,3-trifluoropropene (HFO-1233zd).

20. The method of claim 15 , wherein the step of applying the foamed sample is performed by spraying the foamable composition from a pressurized container.

Assignees

• Ddp Specialty Electronic Materials Us Llc

Inventors

• Thomas Megan Marie
• Koh Kyoung Moo
• Rickard Mark Alan

Classifications

• C08J9/14

  organic · CPC title

• C08G2101/00

  Manufacture of cellular products · CPC title

• C08G18/76

  aromatic · CPC title

• C08G18/66

  Compounds of groups C08G18/42, C08G18/48, or C08G18/52 · CPC title

• C08G18/40

  High-molecular-weight compounds {(C08G18/2805 takes precedence)} · CPC title