Abstract

A method for manufacturing an optical article including the following steps: a. providing a first substrate with a main surface, b. depositing a second substrate on the main surface with an adhesive layer so that the space between the first substrate and second substrate is filled by the adhesive layer, c. curing the adhesive layer to induce a polymerization of the adhesive layer, wherein a tension step takes place after steps a. and b., and before step c., the tension step including applying symmetrically a tension, preferentially with a central symmetry, preferentially a radial isotropic tension or an ortho-distributed symmetrical tension, on the edges of the second substrate sensibly in a tension plan parallel to a plan representative of the main surface.

First claim

The invention claimed is:

1. A method for manufacturing an optical article comprising:
providing a first substrate with a main surface;
depositing a second substrate on said main surface with an adhesive layer so that a space between the first substrate and second substrate is filled by said adhesive layer; and
curing the adhesive layer to induce a polymerization of the adhesive layer, wherein
a tension step takes place after the providing and the depositing, and before the curing, said tension step comprising applying symmetrically a tension to a polymeric film, on edges of the second substrate in a tension plane parallel to a plane of the main surface, to homogeneously place the second substrate on the first substrate, and to obtain the second substrate which is rigorously parallel to the first substrate without introducing surface heterogeneities on a resulting assembly comprising said first and second substrates,
the second substrate has a first main face, which is predetermined to be in contact with the adhesive layer and a second main surface,
the second main surface of the second substrate is fixed to the polymeric film which is larger than said second main surface, and
the tension step is applied by said polymeric film to edges situated on the second main surface of the second substrate, the film being extendable during the tension step, said film being a cling film.

2. The method according to claim 1 , wherein the tension is one of a tension with a central symmetry, a radial isotropic tension, and an orthogonally distributed symmetrical tension.

3. The method according to claim 1 , wherein
the first substrate is mineral glass, and
the second substrate is organic glass.

4. The method according to claim 1 , wherein the main surface of the first substrate is planar.

5. The method according to claim 1 , wherein the symmetric tension is applied both before the curing step and during at least part of the curing step.

6. The method according to claim 1 , wherein the symmetric tension is such that a local horizontal tension is at least 3 times greater than other components of local tension.

7. The method according to claim 1 , wherein the depositing further comprises:
applying a photocurable adhesive to the main surface of the first substrate;
joining with the second substrate horizontally such that the second substrate is above the first substrate; and
allowing the adhesive to spread along an interface between said first and second substrates under a weight of the second substrate until the adhesive fills the space between the first substrate and the second substrate.

8. The method according to claim 1 , wherein the tension step further comprises applying a pressure which is different from an atmospheric pressure, between a face of the polymeric film fixed to the second substrate and an opposite face of the polymeric film which is not fixed to said second substrate, one of these faces cooperating with an external wall to form a tight-sealed chamber.

9. The method according to claim 8 , wherein during the tension step, the first substrate and the second substrate are in the tight-sealed chamber, and a negative pressure is applied in said chamber.

10. The method according to claim 9 , wherein said negative pressure is comprised between 0.05 bar and 1 bar.

11. The method according to claim 1 , wherein
during the depositing the first substrate is deposited in a support which comprises a recess delimited by a wall for receiving said first substrate, and arranged so that a surface of said wall protrudes at a first height,
the first height is greater than a height of the first substrate once placed in the recess, and is comparable to a cumulative height of the first substrate, the adhesive layer, and the second substrate, and
the film covers the second substrate.

12. The method according to claim 11 , wherein the first height is comparable to said cumulative height to within 1 mm.

Assignees

• Essilor Int

Inventors

• Meynen Mathieu
• Jouard Ludovic
• Reignault Marc
• Uhalte Nogues Sira

Classifications

• B32B38/1875

  Tensioning · CPC title

• B32B37/12

  characterised by using adhesives · CPC title

• B32B37/1018

  using only vacuum · CPC title

• B29D11/00403 Primary

  Producing compound lenses · CPC title

• B32B2037/1253

  curable adhesive · CPC title