Solution composition for steel sheet surface treatment, zinc-based plated steel sheet surface-treated with same, and manufacturing method therefor

Patent metadata

Field	Value
Publication number	US-11634819-B2
Application number	US-202217731862-A
Country	US
Kind code	B2
Filing date	Apr 28, 2022
Priority date	Jun 14, 2016
Publication date	Apr 25, 2023
Grant date	Apr 25, 2023

Abstract

Provided is a solution composition for steel sheet surface treatment, comprising 30 wt % to 60 wt % of a trivalent chromium compound containing chromium phosphate (A) and chromium nitrate (B); 0.2 wt % to 0.4 wt % of a rust-inhibiting and corrosion-resisting agent; 0.1 wt % to 0.3 wt % of a molybdenum-based compound; 5 wt % to 10 wt % of a water-soluble cationic urethane resin; 0.5 wt % to 2.0 wt % of a silane coupling agent; and 27.3 wt % to 64.2 wt % of water, a zinc-based plated steel sheet surface-treated with the same, and a manufacturing method therefor, the zinc-based plated steel sheet surface-treated with the solution composition for steel sheet surface treatment containing trivalent chromium may have an excellent effect on corrosion resistance, blackening resistance, fingerprint resistance, oil resistance, and alkali resistance.

First claim

The invention claimed is:

1. A surface-treated zinc-based plated steel sheet comprising:
a steel sheet;
a zinc-based plated layer formed on at least one surface of the steel sheet; and
a trivalent chromate film layer formed on the zinc-based plated layer,
wherein the trivalent chromate film layer comprises:
78.45 wt % to 82.3 wt % of a trivalent chromium compound containing chromium phosphate (A) and chromium nitrate (B);
1.69 wt % to 1.77 wt % of a rust-inhibiting and corrosion-resisting agent;
0.885 wt % to 1.265 wt % of a molybdenum-based compound;
10.125 wt % to 10.62 wt % of a urethane resin; and
4.425 wt % to 8.44 wt % of a silane coupling agent.

2. The surface-treated zinc-based plated steel sheet according claim 1 , wherein the chromium phosphate (A) and chromium nitrate (B) satisfy a content ratio A/(A+B) of 0.89 to 0.95.

3. The surface-treated zinc-based plated steel sheet according claim 1 , wherein the zinc-based plated layer is a zinc-magnesium-aluminum alloy layer.

4. The surface-treated zinc-based plated steel sheet according claim 3 , wherein the zinc-magnesium-aluminum alloy layer comprises 1.5 wt % to 4 wt % of magnesium (Mg), 1 wt % to 3 wt % of aluminum (Al), a remainder of zinc (Zn), and unavoidable impurities.

5. The surface-treated zinc-based plated steel sheet according claim 4 , wherein the content of aluminum (Al) and magnesium (Mg) satisfy 2.5 wt % to 7.0 wt % of Al+Mg, and 0.38 to 0.48 of Al/(Al+Mg).

6. The surface-treated zinc-based plated steel sheet according claim 1 , wherein the trivalent chromate film layer has a thickness of 0.3 μm to 0.5 μm.

Assignees

• Posco
• Noroo Coil Coatings Co Ltd

Inventors

• Cho Soo-Hyoun
• Bae Dae-Chul
• Kim Dong-Yun
• Park Chang-Hyun

Classifications

• C09D5/08

  Anti-corrosive paints · CPC title

• C22C18/00

  Alloys based on zinc · CPC title

• C22C18/04

  with aluminium as the next major constituent · CPC title

• C23C22/40 Primary

  containing molybdates, tungstates or vanadates · CPC title

• C23C2/40

  Plates; Strips · CPC title