In-line coated decorative wood-based boards

Patent metadata

Field	Value
Publication number	US-11633874-B2
Application number	US-201816500642-A
Country	US
Kind code	B2
Filing date	Apr 4, 2018
Priority date	Apr 7, 2017
Publication date	Apr 25, 2023
Grant date	Apr 25, 2023

Abstract

The present invention relates to a process for manufacturing a decorative wood-based board, to a decorative wood-based board, to the use of at least one dry or liquid coating composition comprising at least one inorganic particulate filler material and at least one binder for in-line coating of decorative wood-based boards, and to the use of at least one dry or liquid coating composition comprising at least one inorganic particulate filler material and at least one binder for improving the mechanical properties of a decorative wood-based board. Furthermore, it relates to the use of a decorative wood-based board in flooring applications, furniture, walls, roof panels, display cabinets, storage units, loudspeakers and shop-fittings.

First claim

The invention claimed is:

1. Process for manufacturing a decorative wood-based board, the process comprising the steps of:
a) providing wood particles and/or fibres, in dry form or in form of an aqueous suspension,
b) providing at least one dry or liquid coating composition comprising at least one inorganic particulate filler material and at least one binder, wherein the at least one inorganic particulate filler material comprises at least one inorganic particulate calcium carbonate-containing material having a median particle size d 50 of 0.1 μm to 150.0 μm and/or a specific surface area of 0.5 to 200.0 m 2 /g, as measured by the BET nitrogen method;
c) forming a wood-based mat having a first side and a reverse side from the wood particles and/or fibres provided in step a),
d) pre-pressing the wood-based mat of step c) into a pre-pressed wood-based mat,
e) applying at least one layer of the at least one dry or liquid coating composition of step b) on the first and/or reverse side of the pre-pressed wood-based mat obtained in step d),
f) hot pressing the pre-pressed wood-based mat obtained in step e) into a solid wood-based board, and
g) applying at least one decorative finishing on the first and/or reverse side of the wood-based board obtained in step f) by a step consisting of at least one of inkjet-printing, rotogravure-printing, and/or applying a decorative paper, a decorative foil or a liquid coating;
wherein the at least one dry or liquid coating composition of step b) comprises the at least one inorganic particulate filler material in an amount from 80 to 98 wt.-%, and the at least one binder in an amount from 2 to 20 wt.-% based on the total dry weight of the at least one coating composition.

2. The process according to claim 1 , wherein the wood particles and/or fibres of step a) are combined simultaneously or separately in any order with at least one base binder and/or at least one additive, preferably the at least one base binder is selected from the group comprising phenol-formaldehyde resin (PF), urea-formaldehyde resin (UF), melamine-formaldehyde resin (MF), melamine-urea-formaldehyde resin (MUF), urea-melamine-formaldehyde resin (UMF), urea-melamine-phenol-formaldehyde resin (UMPF), epoxy resin, methylene diphenyl diisocyanate resin (MDI), polyurethane resin (PU), resorcinol resin, starch or carboxymethylcellulose and mixtures thereof, and/or the at least one additive is selected from the group comprising waxes, colourants, filler, dispersants, biocides, hardener, flame retardants and mixtures thereof.

3. The process according to claim 1 , wherein the wood particles of step a) are wood chips.

4. The process according to claim 1 , wherein the at least one inorganic particulate calcium carbonate-containing material of step b) is selected from the group consisting of dolomite, ground calcium carbonate (GCC), preferably ground calcium carbonate (GCC) selected from the group comprising marble, chalk, limestone and mixtures thereof, precipitated calcium carbonate (PCC), preferably precipitated calcium carbonate (PCC) selected from the group comprising one or more of the aragonitic, vateritic and calcitic mineralogical crystal forms, modified calcium carbonate (MCC), gypsum, calcine clay, non-calcined (hydrous) clay, bentonite, inorganic pigments and mixtures thereof.

5. The process according to claim 1 , wherein the at least one inorganic particulate calcium carbonate-containing material of step b) has a median particle size d 50 from 0.3 μm to 50.0 μm and/or a specific surface area of from 0.5 to 75.0 m 2 /g as measured by the BET nitrogen method.

6. The process according to claim 1 , wherein the at least one binder of step b) is selected from the group consisting of alkyd resin, epoxy resin, epoxy ester resin, poly(vinyl alcohol), poly(vinyl pyrrolidone), poly(vinyl acetate), poly(oxazolines), poly(vinylacetamides), partially hydrolyzed poly(vinyl acetate/vinyl alcohol), poly((meth)acrylic acid), poly((meth)acrylamide), poly(alkylene oxide), polyether, saturated polyester, sulfonated or phosphated polyesters and polystyrenes, poly(styrene-co-(meth)acrylate), poly(styrene-co-butadiene), polyurethane latex, poly(n-butyl (meth)acrylate), poly(2-ethylhexyl (meth)acrylate), copolymers of (meth)acrylates, such as n-butyl(meth)acrylate and ethyl(meth)acrylate, copolymers of vinylacetate and n-butyl(meth)acrylate casein, copolymers of polyvinylchloride, gelatin, cellulose ethers, zein, albumin, chitin, chitosan, dextran, pectin, collagen derivatives, collodian, agar-agar, arrowroot, guar, carrageenan, starch, tragacanth, xanthan, or rhamsan and mixtures thereof.

7. The process according to claim 1 , wherein a single or multi-layer wood-based mat is formed in step c).

8. The process according to claim 1 , wherein pre-pressing step d) is carried out at ambient temperature, e.g. from 10 to 60° C., more preferably from 15 to 30° C., and/or a pressure ranging from 5 to 40 bar, preferably from 8 to 35 bar.

9. The process according to claim 1 , wherein coating step e) is carried out by metering size press, curtain coating, spray coating or roller coating.

10. The process according to claim 1 , wherein coating step e) is carried out on the first and reverse side of the pre-pressed wood-based mat to manufacture a decorative wood-based board being coated on the first and the reverse side, and/or coating step e) is carried out a second time using a different or the same liquid coating composition of step b).

11. The process according to claim 1 , wherein hot pressing step f) is carried out at a temperature ranging from 130 to 260° C., more preferably from 160 to 240° C.

12. The process according to claim 1 , wherein the decorative wood-based board is a fibre board product, preferably a high-density fibre (HDF) board, medium-density fibre (MDF) board, low-density fibre (LDF) board, a particle board, an oriented strandboard (OSB), a hardboard, or an insulation board.

13. The process according to claim 1 , wherein in step g) the at least one decorative finishing is applied as a liquid coating being a lacquer layer.

14. The process according to claim 1 , wherein the process comprises the further steps of
h) applying at least one protective layer on the at least one decorative finishing obtained in step g), and/or
i) in case that the at least one decorative finishing is only present on one side, applying at least one backing layer on the side of the decorative wood-based board opposite to the at least one decorative finishing, preferably in form of a paper.

15. A decorative wood-based board, obtained according to the process of claim 1 , comprising
a) the solid wood-based board,
b) the at least one coating layer on the first and/or reverse side of the solid wood-based board, wherein the coating comprises
i) the at least one inorganic particulate filler material, having a ratio of particle size d 80 to particle size d 20 from 0.5 to 1.0, and
ii) the at least one binder, and

c) the at least one decorative finishing on the first and/or reverse side of the wood-based board.

16. The decorative wood-based board according to claim 15 , wherein the at least one decorative finishing is present on the at least one coating layer on the first and/or reverse side of the wood-based board.

17. The decorative wood-based board according to claim 15 , wherein the at least one decorative finishing is present on one side of the wood-based board and the at least one coating layer is present on the opposite side of the wood-based board and represents a backing layer or is part of a backing layer.

Assignees

• Omya Int Ag

Inventors

• Schrul Christopher
• Ozyhar Tomasz

Classifications

• B27N3/04 Primary

  from fibres · CPC title

• B27N3/10

  Moulding of mats · CPC title

• B27N3/02

  from particles · CPC title

• B27N7/005 Primary

  Coating boards, e.g. with a finishing or decorating layer · CPC title

• B27N3/06

  Making particle boards or fibreboards, with preformed covering layers, the particles or fibres being compressed with the layers to a board in one single pressing operation · CPC title